Polymer Property : Dielectric Strength = 10.0 kV/mm Product List
Electrical PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Dielectric Strength | >= 10.0 kV/mm @Thickness 1.00 mm |
>= 254 kV/in @Thickness 0.0394 in |
in oil; ASTM D149 |
| SABIC Innovative Plastics LNP KONDUIT PX11311 PA 6 (Asia Pacific) Thermally conductive mineral filled PA6 FR compound |
|||
| Dielectric Strength | >= 10.0 kV/mm @Thickness 1.00 mm |
>= 254 kV/in @Thickness 0.0394 in |
in oil; ASTM D149 |
| SABIC Innovative Plastics LNP KONDUIT PX11313 PA 6 (Asia Pacific) Thermally conductive mineral filled PA6 FR compounding |
|||
| Dielectric Strength | 10.0 kV/mm | 254 kV/in | ASTM D149 |
| Parker Chomerics THERM-A-FORM T646 Cure-in-Place Potting and Underfill Material Description: THERM-A-FORM™ thermally conductive silicone elastomer products are dispensable form-in-place compounds designed for heat transfer without excessive compressive force in electronics co.. |
|||
| Dielectric Strength | 10.0 kV/mm @Thickness 3.18 mm, Temperature 23.0 °C |
254 kV/in @Thickness 0.125 in, Temperature 73.4 °F |
ASTM D149 |
| Solvay Specialty Polymers Solef® 460/461 Polyvinylidene Fluoride (PVDF)
(Unverified Data**) Solef® 460/461 PVDF homopolymer has high melt viscosity and is typically processed by extrusion.Information provided by Solvay Specialty Polymers. |
|||
| Dielectric Strength | 10.0 - 150 kV/mm | 254 - 3810 kV/in | Average value: 42.4 kV/mm Grade Count:58 |
| Overview of materials for Polyvinylidinefluoride (PVDF), Molded/Extruded This property data is a summary of similar materials in the MatWeb database for the category "Polyvinylidinefluoride (PVDF), Molded/Extruded". Each property range of values reported is minimum and m.. |
|||
| Dielectric Strength | 10.0 kV/mm | 254 kV/in | Short Time; ASTM D149 |
| Plenco 4246 Phenolic, Granular, Injection Molded
(discontinued **) Two-stage Phenolic. PLENCO 04246 flow 18 is a black two-stage, medium heat resistant phenolic molding compound. It has excellent electrical, moldability and molded finish characteristics. It is use.. |
|||
| Dielectric Strength | 10.0 kV/mm | 254 kV/in | 150°C for 1,000 hrs |
| Fujipoly Industries Sarcon® 30Q Thin-Film QR Sarcon QR is Fujipolys originally developed High Heat Conductive/Low Hardness Silicone Rubber. Fine, high heat conductive ceramic particles are mixed with insulative silicone rubber.Information prov.. |
|||
| Dielectric Strength | 10.0 kV/mm | 254 kV/in | 150°C for 1,000 hrs |
| Fujipoly Industries Sarcon® 30U Thin-Film UR Sarcon UR is Fujipolys originally developed High Heat Conductive/Low Hardness Silicone Rubber. Fine, high heat conductive ceramic particles are mixed with insulative silicone rubber.Information prov.. |
|||
| Dielectric Strength | 10.0 kV/mm | 254 kV/in | 200°C for 1,000 hrs |
| Fujipoly Industries Sarcon® 30U Thin-Film UR Sarcon UR is Fujipolys originally developed High Heat Conductive/Low Hardness Silicone Rubber. Fine, high heat conductive ceramic particles are mixed with insulative silicone rubber.Information prov.. |
|||
| Dielectric Strength | 10.0 kV/mm | 254 kV/in | AC 60 Hz; 200°C for 1,000 hrs |
| Fujipoly Industries Sarcon® 45T Thin-Film TR Sarcon TR is Fujipolys originally developed High Heat Conductive Silicone Rubber. Fine, high heat conductive ceramic particles are mixed with insulative silicone rubber.Sarcon GTR is a composite of .. |
|||
| Dielectric Strength | 10.0 kV/mm | 254 kV/in | JIS-K-6249; ASTM D-149 |
| Fujipoly Industries Sarcon® GR-HFd Gap Filler Pad Sarcon GR-d is a highly conformable, thermally conductive material in areas where space between surfaces is uneven and surface textures vary. GR-HFd has a hardened top surface and mesh embedded over.. |
|||
| Dielectric Strength | >= 10.0 kV/mm | >= 254 kV/in | |
| Misumi Alumina 96 Aluminum Oxide, Al2O3 Information provided by MISUMI Corporation. |
|||
| Dielectric Strength | >= 10.0 kV/mm | >= 254 kV/in | |
| Misumi Steatite MgO-SiO2Information provided by MISUMI Corporation. |
|||
| Dielectric Strength | 10.0 kV/mm | 254 kV/in | 60°C for 500 hrs |
| Fujipoly Industries Sarcon® 85T Thin-Film TR Sarcon TR is Fujipolys originally developed High Heat Conductive Silicone Rubber. Fine, high heat conductive ceramic particles are mixed with insulative silicone rubber.Sarcon GTR is a composite of .. |
|||
| Dielectric Strength | >= 10.0 kV/mm | >= 254 kV/in | ASTM-D150 |
| CeramTec Rubalit® 702 Alumina, 85% Rubalit® 702 is a high-performance material for the manufacturing of metal-film resistors. With an alumina content of 85%, it provides extreme hardness and high thermal conductivity. Practical appl.. |
|||
| Dielectric Strength | >= 10.0 kV/mm | >= 254 kV/in | ASTM-D149 |
| CeramTec Rubalit® 708 Alumina, 96% Based on 96% aluminum oxide, Rubalit® 708 was developed specifically for making heavy-duty resistors and miniature metal layer resistors. Because of its outstanding strength, this same material is .. |
|||
| Dielectric Strength | 10.0 kV/mm | 254 kV/in | ASTM D149-95a |
| Thermoseal KLINGERSIL® C-4439 Metal Reinforced Gasketing Fiberglass, Aramid & Inorganic FibersNitrile BinderHigh Temperature & StressVibrationGalvanized Low Carbon Steel InsertInformation provided by Thermoseal Inc. |
|||
| Dielectric Strength | 10.0 kV/mm | 254 kV/in | Step by Step; ASTM D149 |
| Plenco 3597 Phenolic, Granular, Injection Molded PLENCO 03597 is a mineral filled phenolic molding compound offering excellent flammability ratings even at thin cross sections, along with excellent arc and comparative track resistance values. UL r.. |
|||
| Dielectric Strength | 10.0 kV/mm | 254 kV/in | |
| Covestro Baydur® 60 Polyurethane Rigid integral skin polyurethane foam for engineering components. The integral distribution of density gives a higher flexural modulus. If required, the property level can be improved by increasing .. |
|||
| Dielectric Strength | 10.0 kV/mm @Thickness 3.00 mm |
254 kV/in @Thickness 0.118 in |
96hr/105°C+1hr/oil 90°C; Perpendicular; IEC 60243-1; IEC/EN 61212-2 6.1.2.1 |
| Elektro-Isola Etronit B 66 Phenolic, Paper Reinforcement, Dark Brown, Tubes Description: Specially designed for high-voltage insulation with high requirements for insulating capacity along the tube.Applications: Insulating tubes in high-voltage switchgear and tap changers.... |
|||
| Dielectric Strength | 10.0 kV/mm @Thickness 3.00 mm |
254 kV/in @Thickness 0.118 in |
24hr/23°C/50% RH+1hr/oil 90°C; Perpendicular; IEC 60243-1; IEC/EN 61212-2 6.1.2.1 |
| Elektro-Isola G-Etronax PI Polyimide, Glass Fabric Reinforcement, Dark Brown, Tubes Description: Extremely good mechanical properties, at high temperatures. Low thermal conductivity.Applications: Material for components used in the aerospace industry. Insulation parts in wire weldi.. |
|||
| Dielectric Strength | 10.0 kV/mm | 254 kV/in | cond; IEC 60243-1 |
| DSM Stanyl® TW341-B PA46 Heat Stabilized, Lubricated |
|||
| Dielectric Strength | 10.0 - 11.0 kV/mm | 254 - 279 kV/in | ASTM D149 |
| Adamas Adalon® 452 PTFE, Mica filler Information provided by Adamas, HPM |
|||
| Dielectric Strength | 10.0 kV/mm | 254 kV/in | Short Time; Dry; ASTM D149 |
| Resinoid 2010 Phenolic Molding, Fabric Reinforced Data provided by the manufacturer.The Resinoid 2000 organic fiber reinforced series compounds feature mechanical strength, dimensional stability, and shock resistance |
|||
| Dielectric Strength | >= 10.0 kV/mm | >= 254 kV/in | |
| Beijing Evergrow Resources PTFE Adhesive Tape PTFE adhesive tape is manufactured by PTFE high strength suspension resin. The skived PTFE tape is one side etched, and then coated with adhesive back and chippd to different sizes. It is anticorros.. |
|||
| Dielectric Strength | 10.0 kV/mm | 254 kV/in | 60 Hz, wet, SS; ASTM D149 |
| Sumitomo Bakelite North America FM 4004 Fiberglass and Mineral Reinforced Phenolic Novolac FM 4004 is a fiberglass and mineral reinforced phenolic novolac compound. This compound exhibits excellent dimensional stability and good strength at elevated temperatures, and conforms to the requ.. |
|||
| Dielectric Strength | 10.0 kV/mm | 254 kV/in | ST; ASTM D149 |
| Sumitomo Bakelite North America FM 4005 Fiberglass Reinforced Phenolic Novolac FM 4005 is a fiberglass reinforced phenolic novolac molding compound, with excellent dimensional stability and good strength at elevated temperatures. This material is compliant with the specificat.. |
|||
| Dielectric Strength | >= 10.0 kV/mm @Thickness 1.00 mm |
>= 254 kV/in @Thickness 0.0394 in |
in oil; ASTM D149 |
| SABIC Innovative Plastics LNP KONDUIT PX11313 PA 6 (Europe-Africa-Middle East) Thermally conductive mineral and glass fiber filled PA6, FR, compliant with ECO protocols, non-brominated, non-chlorinated |
|||