Fujipoly Industries SarconÂ® 30Q Thin-Film QR

Category	Polymer , Thermoset , Silicone
Manufacturer	Fujipoly Industries
Trade Name	Sarcon®
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Fujipoly Industries SarconÂ® 30Q Thin-Film QR.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Sarcon QR is Fujipolys originally developed High Heat Conductive/Low Hardness Silicone Rubber. Fine, high heat conductive ceramic particles are mixed with insulative silicone rubber.Information provided by Fujipoly Industries

Mechanical Properties	Metric	English	Comments
Hardness, Shore A	55	55	ASTM D2240
	63	63	60Â°C for 500 hrs with 95% RH; ASTM D2240
	73	73	150Â°C for 1,000 hrs; ASTM D2240
	80	80	200Â°C for 1,000 hrs; ASTM D2240
Tensile Strength, Yield	2.66 MPa	386 psi
	4.33 MPa	628 psi	60Â°C for 500 hrs with 95% RH
	5.33 MPa	773 psi	150Â°C for 1,000 hrs
	6.00 MPa	870 psi	200Â°C for 1,000 hrs
Elongation at Yield	70 %	70 %	200Â°C for 1,000 hrs
	103 %	103 %
	147 %	147 %	60Â°C for 500 hrs with 95% RH
	250 %	250 %
Tear Strength	0.500 kN/m	2.85 pli

Thermal Properties	Metric	English
Maximum Service Temperature, Air	182 Â°C	360 Â°F
Minimum Service Temperature, Air	-60.0 Â°C	-76.0 Â°F
Flammability, UL94	V-0	V-0

Electrical Properties	Metric	English	Comments
Volume Resistivity	2.80e+14 ohm-cm	2.80e+14 ohm-cm	60Â°C for 500 hrs with 95% RH
	1.00e+15 ohm-cm	1.00e+15 ohm-cm
	3.20e+15 ohm-cm	3.20e+15 ohm-cm	150Â°C for 1,000 hrs
	7.50e+15 ohm-cm	7.50e+15 ohm-cm	200Â°C for 1,000 hrs
Dielectric Constant	3.87 @Frequency 1e+6 Hz	3.87 @Frequency 1e+6 Hz	After 1000 hrs at 200Â°C
	3.88 @Frequency 1000 Hz	3.88 @Frequency 1000 Hz	After 1000 hrs at 200Â°C
	3.91 @Frequency 50 Hz	3.91 @Frequency 50 Hz	After 1000 hrs at 200Â°C
	3.99 @Frequency 1000 Hz	3.99 @Frequency 1000 Hz	After 1000 hrs at 150Â°C
	3.99 @Frequency 1e+6 Hz	3.99 @Frequency 1e+6 Hz	After 1000 hrs at 150Â°C
	4.02 @Frequency 50 Hz	4.02 @Frequency 50 Hz	After 1000 hrs at 150Â°C
	4.1 @Frequency 1e+6 Hz	4.1 @Frequency 1e+6 Hz	After 500 hrs at 60Â°C with 95% RH
	4.11 @Frequency 1e+6 Hz	4.11 @Frequency 1e+6 Hz
	4.12 @Frequency 1000 Hz	4.12 @Frequency 1000 Hz
	4.13 @Frequency 1000 Hz	4.13 @Frequency 1000 Hz	After 500 hrs at 60Â°C with 95% RH
	4.15 @Frequency 50 Hz	4.15 @Frequency 50 Hz
	4.2 @Frequency 50 Hz	4.2 @Frequency 50 Hz	After 500 hrs at 60Â°C with 95% RH
Dielectric Strength	7.00 kV/mm	178 kV/in	AC 60 Hz
	10.0 kV/mm	254 kV/in	150Â°C for 1,000 hrs
	11.0 kV/mm	279 kV/in	200Â°C for 1,000 hrs
	11.0 kV/mm	279 kV/in	60Â°C for 500 hrs with 95% RH
Dielectric Breakdown	7000 V	7000 V	Withstand Voltage [V/min]; AC 60 Hz
Dissipation Factor	0.0022 @Frequency 1e+6 Hz	0.0022 @Frequency 1e+6 Hz	After 1000 hrs at 150Â°C
	0.0022 @Frequency 1e+6 Hz	0.0022 @Frequency 1e+6 Hz	After 1000 hrs at 200Â°C
	0.0022 @Frequency 1e+6 Hz	0.0022 @Frequency 1e+6 Hz
	0.0026 @Frequency 1000 Hz	0.0026 @Frequency 1000 Hz	After 1000 hrs at 150Â°C
	0.0027 @Frequency 1e+6 Hz	0.0027 @Frequency 1e+6 Hz	After 500 hrs at 60Â°C with 95% RH
	0.0031 @Frequency 1000 Hz	0.0031 @Frequency 1000 Hz	After 1000 hrs at 200Â°C
	0.0035 @Frequency 50 Hz	0.0035 @Frequency 50 Hz	After 1000 hrs at 200Â°C
	0.0035 @Frequency 1000 Hz	0.0035 @Frequency 1000 Hz
	0.0039 @Frequency 50 Hz	0.0039 @Frequency 50 Hz	After 1000 hrs at 150Â°C
	0.0064 @Frequency 50 Hz	0.0064 @Frequency 50 Hz
	0.0070 @Frequency 1000 Hz	0.0070 @Frequency 1000 Hz	After 500 hrs at 60Â°C with 95% RH
	0.0132 @Frequency 50 Hz	0.0132 @Frequency 50 Hz	After 500 hrs at 60Â°C with 95% RH

Descriptive Properties	Value	Comments
Color	Grey
Thermal Impedance	0.57Â°C/W	FTM P-3010; ASTM D5470