SABIC Innovative Plastics LNP LUBRICOMP RAL22I PA 66
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP LUBRICOMP |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP LUBRICOMP RAL22I PA 66.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* LUBRICOMP* RAL22I is a compound based on Nylon 66 resin containing 10% PTFE, 10% Aramid Fiber. Added features of this material include: Wear Resistant, High Impact.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.22 g/cc | 1.22 g/cc | ASTM D792 |
| Density | 1.20 g/cc | 0.0434 lb/in³ | ASTM D792 |
| Moisture Absorption | 0.570 % | 0.570 % | 50% RH, 24 hrs; ASTM D570 |
| 0.910 % | 0.910 % | 23°C / 50% RH; ISO 62 | |
| Linear Mold Shrinkage, Flow | >= 0.020 cm/cm @Time 86400 sec |
>= 0.020 in/in @Time 24.0 hour |
ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.020 - 0.040 cm/cm @Time 86400 sec |
0.020 - 0.040 in/in @Time 24.0 hour |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 72.0 MPa | 10400 psi | 5 mm/min; ISO 527 |
| 73.0 MPa | 10600 psi | Type I, 5 mm/min; ASTM D638 | |
| Tensile Strength, Yield | 74.0 MPa | 10700 psi | Type I, 5 mm/min; ASTM D638 |
| Elongation at Break | 8.6 % | 8.6 % | Type I, 5 mm/min; ASTM D638 |
| 8.6 % | 8.6 % | 5 mm/min; ISO 527 | |
| Elongation at Yield | 8.3 % | 8.3 % | Type I, 5 mm/min; ASTM D638 |
| 8.3 % | 8.3 % | 5 mm/min; ISO 527 | |
| Tensile Modulus | 3.43 GPa | 497 ksi | 1 mm/min; ISO 527 |
| 3.51 GPa | 509 ksi | 50 mm/min; ASTM D638 | |
| Flexural Strength | 95.0 MPa | 13800 psi | ISO 178 |
| Flexural Modulus | 3.22 GPa | 467 ksi | 2 mm/min; ISO 178 |
| 3.29 GPa | 477 ksi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| Izod Impact, Notched | 0.510 J/cm | 0.955 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 6.02 J/cm | 11.3 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 5.00 kJ/m² | 2.38 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 41.0 kJ/m² | 19.5 ft-lb/in² | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 7.00 J @Temperature 23.0 °C |
5.16 ft-lb @Temperature 73.4 °F |
ASTM D3763 |
| Impact Test | 1.00 J | 0.738 ft-lb | Multiaxial Impact; ISO 6603 |
| Coefficient of Friction, Dynamic | 0.33 | 0.33 | ASTM D3702 Modified |
| Coefficient of Friction, Static | 0.26 | 0.26 | ASTM D3702 Modified |
| K (wear) Factor | 24.2 x 10-8 mm³/N-M | 12.0 x 10-10 in³-min/ft-lb-hr | Washer; ASTM D3702 Modified |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 57.0 µm/m-°C @Temperature -30.0 - 30.0 °C |
31.7 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| CTE, linear, Transverse to Flow | 83.0 µm/m-°C @Temperature -30.0 - 30.0 °C |
46.1 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 239 °C | 462 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 243 °C @Thickness 3.20 mm |
469 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 114 °C | 237 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 156 °C @Thickness 3.20 mm |
313 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
Users viewing this material also viewed the following:
- Covestro Makrolon® DP1-1243 Polycarbonate, Extrusion (discontinued **)
- Lord Adhesives Flocklok® P13 Adhesive
- Industeel URANUS® 52N+ 25 Cr Super Duplex Stainless Steel with PREN = 40
- SABIC Innovative Plastics Valox® 830 PBT (Asia Pacific)
- SABIC Innovative Plastics Xylex X7509UV PC+POLYESTER (Europe-Africa-Middle East)
- Teknor Apex Monprene® MP-2560B Thermoplastic Elastomer
- Borealis HB600TF Polypropylene
- Hexcel® Redux® 208/5-NA Foaming adhesive film
Copyright © lookpolymers.com All Rights Reserved