SABIC Innovative Plastics Lexan® XHT3141 PC Copolymer (Asia Pacific)

Category Polymer , Thermoplastic , Polycarbonate (PC)
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name Lexan®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics Lexan® XHT3141 PC Copolymer (Asia Pacific).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
XHT3141 is a high flow, high heat polycarbonate copolymer. It is available in a range of opaque and limited transparent colors.
Physical Properties Metric English Comments
Specific Gravity 1.20 g/cc
1.20 g/cc
ASTM D792
Density 1.20 g/cc
0.0434 lb/in³
ISO 1183
Moisture Absorption 0.300 %
0.300 %
23°C / 50% RH; ISO 62
Water Absorption at Saturation 0.30 %
0.30 %
ISO 62
Linear Mold Shrinkage, Flow 0.0060 - 0.0090 cm/cm

@Thickness 3.20 mm
0.0060 - 0.0090 in/in

@Thickness 0.126 in
SABIC Method
Melt Flow 33 g/10 min

@Load 2.16 kg,
Temperature 330 °C
33 g/10 min

@Load 4.76 lb,
Temperature 626 °F
ASTM D1238
Melt Index of Compound 30 g/10 min

@Load 2.16 kg,
Temperature 330 °C
30 g/10 min

@Load 4.76 lb,
Temperature 626 °F
MVR [cm^3/10 min]; ISO 1133
Mechanical Properties Metric English Comments
Tensile Strength at Break 55.0 MPa
7980 psi
Type I, 50 mm/min; ASTM D638
60.0 MPa
8700 psi
50 mm/min; ISO 527
Tensile Strength, Yield 70.0 MPa
10200 psi
Type I, 50 mm/min; ASTM D638
70.0 MPa
10200 psi
50 mm/min; ISO 527
Elongation at Break 70 %
70 %
Type I, 50 mm/min; ASTM D638
70 %
70 %
50 mm/min; ISO 527
Elongation at Yield 6.0 %
6.0 %
Type I, 50 mm/min; ASTM D638
6.0 %
6.0 %
50 mm/min; ISO 527
Tensile Modulus 2.50 GPa
363 ksi
1 mm/min; ISO 527
2.70 GPa
392 ksi
5 mm/min; ASTM D638
Flexural Yield Strength 80.0 MPa
11600 psi
2 mm/min; ISO 178
120 MPa
17400 psi
1.3 mm/min, 50 mm span; ASTM D790
Flexural Modulus 2.50 GPa
363 ksi
2 mm/min; ISO 178
2.60 GPa
377 ksi
1.3 mm/min, 50 mm span; ASTM D790
Izod Impact, Notched 0.970 J/cm
1.82 ft-lb/in
ASTM D256
0.550 J/cm

@Temperature -30.0 °C
1.03 ft-lb/in

@Temperature -22.0 °F
ASTM D256
Izod Impact, Notched (ISO) 9.00 kJ/m²
4.28 ft-lb/in²
80*10*3; ISO 180/1A
9.00 kJ/m²

@Temperature -30.0 °C
4.28 ft-lb/in²

@Temperature -22.0 °F
80*10*3; ISO 180/1A
Izod Impact, Unnotched (ISO) NB
NB
80*10*3; ISO 180/1U
NB

@Temperature -30.0 °C
NB

@Temperature -22.0 °F
80*10*3; ISO 180/1U
Charpy Impact Unnotched NB
NB
Edgew 80*10*3 sp=62mm; ISO 179/1eU
NB

@Temperature -30.0 °C
NB

@Temperature -22.0 °F
Edgew 80*10*3 sp=62mm; ISO 179/1eU
Charpy Impact, Notched 1.10 J/cm²
5.23 ft-lb/in²
Edgew 80*10*3 sp=62mm; ISO 179/1eA
0.900 J/cm²

@Temperature -30.0 °C
4.28 ft-lb/in²

@Temperature -22.0 °F
Edgew 80*10*3 sp=62mm; ISO 179/1eA
Dart Drop, Total Energy 68.0 J

@Temperature 23.0 °C
50.2 ft-lb

@Temperature 73.4 °F
ASTM D3763
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 60.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
33.3 µin/in-°F

@Temperature -40.0 - 104 °F
ASTM E 831
60.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
33.3 µin/in-°F

@Temperature -40.0 - 104 °F
ISO 11359-2
CTE, linear, Transverse to Flow 60.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
33.3 µin/in-°F

@Temperature -40.0 - 104 °F
ASTM E 831
60.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
33.3 µin/in-°F

@Temperature -40.0 - 104 °F
ISO 11359-2
Thermal Conductivity 0.200 W/m-K
1.39 BTU-in/hr-ft²-°F
ASTM C177
Deflection Temperature at 0.46 MPa (66 psi) 164 °C
327 °F
Flatw 80*10*4 sp=64mm; ISO 75/Bf
166 °C

@Thickness 3.20 mm
331 °F

@Thickness 0.126 in
unannealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 152 °C
306 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
156 °C

@Thickness 3.20 mm
313 °F

@Thickness 0.126 in
unannealed; ASTM D648
Vicat Softening Point 168 °C
334 °F
Rate B/50; ISO 306
170 °C
338 °F
Rate B/120; ISO 306
170 °C
338 °F
Rate B/50; ASTM D1525
UL RTI, Electrical 150 °C
302 °F
UL 746B
UL RTI, Mechanical with Impact 130 °C
266 °F
UL 746B
UL RTI, Mechanical without Impact 150 °C
302 °F
UL 746B
Flammability, UL94 HB

@Thickness 1.50 mm
HB

@Thickness 0.0591 in
UL 94
HB

@Thickness 3.00 mm
HB

@Thickness 0.118 in
UL 94
Glow Wire Test 875 °C
1610 °F
IEC 60695-2-13
960 °C

@Thickness 3.00 mm
1760 °F

@Thickness 0.118 in
IEC 60695-2-12
Electrical Properties Metric English Comments
Volume Resistivity >= 1.00e+17 ohm-cm
>= 1.00e+17 ohm-cm
ASTM D257
Surface Resistance >= 1.00e+17 ohm
>= 1.00e+17 ohm
ASTM D257
Dielectric Constant 2.8

@Frequency 1.00e+6 Hz
2.8

@Frequency 1.00e+6 Hz
ASTM D150
2.9

@Frequency 100 Hz
2.9

@Frequency 100 Hz
ASTM D150
Dielectric Strength 23.0 kV/mm

@Thickness 3.20 mm
584 kV/in

@Thickness 0.126 in
in oil; ASTM D149
Dissipation Factor 0.011

@Frequency 1.00e+6 Hz
0.011

@Frequency 1.00e+6 Hz
ASTM D150
0.031

@Frequency 100 Hz
0.031

@Frequency 100 Hz
ASTM D150
Comparative Tracking Index 175 - 250 V
175 - 250 V
UL 746A
Hot Wire Ignition, HWI 15 - 30 sec
15 - 30 sec
UL 746A
High Amp Arc Ignition, HAI >= 120 arcs
>= 120 arcs
UL 746A
Descriptive Properties Value Comments
Ball Pressure Test, 125°C +/- 2°C Passes
IEC 60695-10-2
Metallized Haze Onset 165°C
SABIC Method