- Polymer Property : Deflection Temperature at 1.8 MPa (264 psi) = 120 °F
Polymer Property : Deflection Temperature at 1.8 MPa (264 psi) = 120 °F Product List
Thermal PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 48.9 °C | 120 °F | ASTM D648 |
| RheTech Products FT1002-00 Thermoplastic Polyolefin, Non-UV Stabilized, Natural Applications: Step padsHitch padsScuff platesInjection molding conditions reported in table.Information provided by RheTech Products. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 48.9 °C | 120 °F | ASTM D648 |
| RheTech Products FT1003-00 Thermoplastic Polyolefin, Non-UV Stabilized, Natural Applications: Step and hitch padsInterior component and trimA/B pillarsInjection molding conditions reported in table.Information provided by RheTech Products. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 48.9 °C | 120 °F | ASTM D648 |
| RheTech Products FT1004-01 Thermoplastic Polyolefin, Non-UV Stabilized, Black Applications: Step padsHitch padsScuff platesInjection molding conditions reported in table.Information provided by RheTech Products. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 48.9 °C | 120 °F | ASTM D648 |
| RheTech Products FT2600-00UV Thermoplastic Polyolefin, Non-UV Stabilized, Natural Applications: Interior trimSplash shieldScuff padsInjection molding conditions reported in table.Information provided by RheTech Products. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 48.9 °C | 120 °F | ASTM D648 |
| RheTech Products FT2700-00 Thermoplastic Polyolefin, Non-UV Stabilized, Natural Applications: Air deflectorsFuel filler shieldsUnderhood componentsInjection molding conditions reported in table.Information provided by RheTech Products. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 48.9 °C | 120 °F | ASTM D648 |
| RheTech Products FT3080-757UV Thermoplastic Polyolefin, UV Stabilized, Pueblo Gold Applications: Step padsHitch padsScuff padsInjection molding conditions reported in table.Information provided by RheTech Products. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 49.0 °C | 120 °F | ASTM D648 |
| Protective Coating PC-7® Epoxy Paste PC-7® is a tough job Epoxy formulation developed for maximum bonding power. Components A (grey) and B (black), when mixed, react to form a bond of good strength. PC-7® formulation provides exten.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 49.0 °C | 120 °F | ASTM D648 |
| North Wood Plastics 60 HDPE + UNIFILL (40% Wood Fiber) Data provided by North Wood Plastics, Inc. UNIFILL-60 is a general purpose polyolefin compound compatible in both PP and HDPE. It is a masterbatch with 60% high quality pine wood flour filler. It.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 48.9 - 210 °C | 120 - 410 °F | Average value: 78.9 °C Grade Count:49 |
| Overview of materials for Polybutylene Terephthalate (PBT), Impact Grade This property data is a summary of similar materials in the MatWeb database for the category "Polybutylene Terephthalate (PBT), Impact Grade". Each property range of values reported is minimum and m.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 49.0 °C @Thickness 1.57 mm |
120 °F @Thickness 0.0618 in |
Annealed; ASTM D648 |
| PolyOne Maxxam™ FR PP 301 EXT Polypropylene, Unspecified (PP, Unspecified) Information provided by PolyOne |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 48.9 °C | 120 °F | ASTM D648 |
| RTP Company RTP 200F TFE 20 SI Nylon 12 (PA 12) PTFE 20% - Silicone
(discontinued **) PTFE 20% - SiliconeComments:PTFE LubricatedSilicone LubricatedUnless otherwise specified, all data listed is for natural or black colored materials. Pigments can affect properties.Information provid.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 49.0 - 77.8 °C | 120 - 172 °F | Average value: 60.6 °C Grade Count:7 |
| Overview of materials for Nylon 12, PTFE Filled This property data is a summary of similar materials in the MatWeb database for the category "Nylon 12, PTFE Filled". Each property range of values reported is minimum and maximum values of appropri.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 49.0 °C @Thickness 6.40 mm |
120 °F @Thickness 0.252 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics Valox® 195 PBT PELLET FORM. For compounding only (not for injection molding). Unreinforced PBT. Melt viscosity between 740 and 900 poise. Natural Color (1001) Only. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 48.9 °C | 120 °F | ASTM D648 |
| Spartech PE4125 Reinforced High Density Polyethylene Compound Spartech Polycom's filled high molecular weight, high density polyethylenes are specifically designed for blow molding and sheet extrusion /thermoforming of structural parts. These materials offer a.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 49.0 °C | 120 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| SABIC Innovative Plastics LNP STAT-KON MX12407C PP LNP* STAT-KON* MX12407C is a compound based on Polypropylene resin containing Proprietary Filler(s). Added features of this material include: Electrically Conductive, Clean Compounding System. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 49.0 °C @Thickness 3.20 mm |
120 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics LNP THERMOCOMP TH0300B PU LNP* Thermocomp* Th0300B is a compound based on Polyurethane containing proprietary fillers. Characteristics of this grade are High Specific Gravity. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 49.0 °C | 120 °F | ISO 75-2 |
| Borealis Daplen™ EE040AE TPO Compound Daplen EE040AE is an elastomer modified polypropylene compound intended for injection molding. Daplen EE040AE is a material with excellent impact /stiffness ratio. Thanks to its low thermal expansi.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 49.0 °C | 120 °F | ISO 75-2 |
| Borealis Daplen™ EE115T TPO Compound Daplen EE115T is a 10% mineral and elastomer modified polypropylene compound intended for injection molding. Daplen EE115T is a material with excellent impact /stiffness ratio. Thanks to its low th.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 48.9 °C | 120 °F | ASTM D 648 |
| RTP Company RTP 1500-55D TFE 10 Polyether-Ester Block Copolymer (TEEE/COPE), PTFE Lubricated |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 49.0 - 49.7 °C | 120 - 121 °F | UV Postcure; ASTM D648 |
| DSM Somos® BioClear Parts created with Somos® BioClear are designed for medical applications that are non-implant and have limited contact with the body such as device prototyping. They are shatter-resistant so they w.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 48.9 °C | 120 °F | ISO 75-2/A |
| ExxonMobil PP7043L1 Polypropylene Impact Copolymer Product Description: An impact copolymer resin characterized by medium flow. It is suitable for molding applications like consumer products, containers and rigid packaging applications.Availability.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 48.9 °C | 120 °F | |
| Aclo Accutech Polypropylene Copolymer CP0437M10L Mica Reinforced |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 49.0 °C | 120 °F | ASTM D648 |
| Braskem RP 141 Injection Molding Polypropylene Description: RP 141 is a high melt flow rate random copolymer designed for injection molding. This product offers outstanding transparency, very good stiffness/impact strength balance and excellent .. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 48.9 °C | 120 °F | ASTM D648 |
| Celanese VANDAR 2100UV PBT, Impact Modified Vandar 2100UV is a polyester alloy designed to offer maximum impact strength at room and low temperatures. This unfilled compound is characterized by outstanding chemical resistance, dimensional sta.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 48.9 °C | 120 °F | Unannealed; ASTM D648 |
| LNP Stat-Kon® SS- Polyamide 12, Stainless Steel Fiber
(discontinued **) Features: Electrically ConductiveForms: PelletsProcessing Method: Injection MoldingInformation provided by LNP, a GE Plastics Company.This data sheet is labeled Discontinued; however many LNP grades.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 49.0 °C | 120 °F | ASTM D648 |
| Adell RZ-14 Copolymer Polypropylene, 20% Calcium Carbonate Filled Data provided by Adell Plastics, Inc. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 49.0 °C @Thickness 3.20 mm |
120 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics Valox® V2105U PBT (Asia Pacific) Unreinforced, Wear resistant, UV Stabilized PBT designed for outdoor, agricultural, industrial and automotive applications. This grade has very high impact strength to stiffness ratio. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 48.9 °C | 120 °F | ASTM D 648 |
| RTP Company RTP 142 HI Polypropylene (PP), Impact Modified - Calcium Carbonate |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 49.0 °C | 120 °F | ASTM-D648 |
| Braskem RP 145 RACO Random Polypropylene Copolymer RP 145 is a high melt flow rate random copolymer designed for use in thin-walled injection molding parts. This product offers good transparency, very good stiffness/impact strength balance, excellen.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 48.9 °C | 120 °F | ASTM D648 |
| Celanese VANDAR 2122 PBT, 10% Mineral Reinforced Vandar 2122 is a polyester alloy which contains 10% mineral filler. It offers exceptional toughness and practical impact strength. This resin offers Class A paintable finish with excellent dimension.. |
|||