Polymer Property : Deflection Temperature at 1.8 MPa (264 psi) = 49.0 °C Product List

Thermal Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.
Thermal Properties Metric English Comments
Deflection Temperature at 1.8 MPa (264 psi) 49.0 °C

@Thickness 1.57 mm
120 °F

@Thickness 0.0618 in
Annealed; ASTM D648
PolyOne Maxxam™ FR PP 301 EXT Polypropylene, Unspecified (PP, Unspecified)
Information provided by PolyOne
Deflection Temperature at 1.8 MPa (264 psi) 49.0 - 49.7 °C
120 - 121 °F
ASTM D648-98c
Proto3000 WaterShed® XC 11122 Stereolithography (SLA) Prototyping Polymer
WaterShed XC is a low viscosity liquid photopolymer that produces strong, tough, water-resistant, ABS-like parts. Most importantly parts created with WaterShed 11122 are nearly colorless, and look ..
Deflection Temperature at 1.8 MPa (264 psi) 49.0 °C

@Thickness 4.00 mm
120 °F

@Thickness 0.157 in
after annealing 150°C 16 hr; ASTM D648
Solvay Specialty Polymers Solef® 61010 PVDF Copolymer  (discontinued **)
Key features of this grade: Permanent Plasticizing, Fuel Line, Piping, Formulated. Recommended processing is extrusion. Available as granules.General information about SOLEF® PVDF: SOLEF® PVDF i..
Deflection Temperature at 1.8 MPa (264 psi) 49.0 °C
120 °F
LyondellBasell Lupolen® 6031 M HDPE, Injection Molding Grade
Easy flow, injection molding grade for fruit crates, tote boxes and bottle crates, cartridges, protective headgear, buckets, dishes, cartridges for adhesive film canisters, aerosol lids, child seats..
Deflection Temperature at 1.8 MPa (264 psi) 49.0 °C
120 °F
unannealed; ISO 75-1A
MBA Polymers PP 2172 Post-consumer recycled polypropylene copolymer
High melt flow rate for injection molding applications. Available in standard black.Information provided by MBA Polymers.
Deflection Temperature at 1.8 MPa (264 psi) 49.0 °C
120 °F
ASTM D648
Techmer ES Electrafil® PP-61/EC Copolymer Polypropylene, Conductive Carbon Filled
Conductive Carbon, Powder Modified
Deflection Temperature at 1.8 MPa (264 psi) 49.0 °C

@Thickness 6.40 mm
120 °F

@Thickness 0.252 in
unannealed; ASTM D648
SABIC Innovative Plastics Valox® 195HP PBT
PELLET FORM. For compounding only (not for injection molding). Unreinforced PBT. FDA 21CFR177.1660 compliant. Melt viscosity between 740 and 900 poise. Natural Color (1001) Only.
Deflection Temperature at 1.8 MPa (264 psi) 49.0 °C
120 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
SABIC Innovative Plastics Valox® HX3061HP PBT
PBT for compounding/fibers only. Not intended for injection molding. Biocompatible. Melt viscosity: 250C at 21.6 kgf is 1450-1850 poise. Available in Natural color (1001) only.
Deflection Temperature at 1.8 MPa (264 psi) 49.0 °C

@Thickness 3.20 mm
120 °F

@Thickness 0.126 in
unannealed; ASTM D648
SABIC Innovative Plastics Valox® HX3061HP PBT
PBT for compounding/fibers only. Not intended for injection molding. Biocompatible. Melt viscosity: 250C at 21.6 kgf is 1450-1850 poise. Available in Natural color (1001) only.
Deflection Temperature at 1.8 MPa (264 psi) 49.0 °C

@Thickness 3.20 mm
120 °F

@Thickness 0.126 in
unannealed; ASTM D648
SABIC Innovative Plastics Valox® HX3091HP PBT
PBT for compounding/fibers only. Not intended for injection molding. Biocompatible. Melt viscosity at 250C and 21.6kgf is 3500-4500 poise. Available in Natural color (1001) only.
Deflection Temperature at 1.8 MPa (264 psi) 49.0 °C

@Thickness 3.20 mm
120 °F

@Thickness 0.126 in
unannealed; ASTM D648
SABIC Innovative Plastics Valox® IQ325HP PBT (Asia Pacific)
FDA compliant PBT resin, using chemically recycled post consumer PET Bottles. Fit to food contact applications.
Deflection Temperature at 1.8 MPa (264 psi) 49.0 °C
120 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
SABIC Innovative Plastics LNP STAT-KON MX12407C PP
LNP* STAT-KON* MX12407C is a compound based on Polypropylene resin containing Proprietary Filler(s). Added features of this material include: Electrically Conductive, Clean Compounding System.
Deflection Temperature at 1.8 MPa (264 psi) 49.0 °C

@Thickness 3.20 mm
120 °F

@Thickness 0.126 in
unannealed; ASTM D648
SABIC Innovative Plastics LNP STAT-KON MX12407C PP
LNP* STAT-KON* MX12407C is a compound based on Polypropylene resin containing Proprietary Filler(s). Added features of this material include: Electrically Conductive, Clean Compounding System.
Deflection Temperature at 1.8 MPa (264 psi) 49.0 °C
120 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
SABIC Innovative Plastics LNP STAT-LOY M3000C PP
LNP* STAT-LOY* M3000C is a compound based on unfilled Polypropylene resin. Added features of this grade include: Clean Compound System, Antistat.
Deflection Temperature at 1.8 MPa (264 psi) 49.0 °C

@Thickness 3.20 mm
120 °F

@Thickness 0.126 in
unannealed; ASTM D648
SABIC Innovative Plastics LNP STAT-LOY M3000C PP
LNP* STAT-LOY* M3000C is a compound based on unfilled Polypropylene resin. Added features of this grade include: Clean Compound System, Antistat.
Deflection Temperature at 1.8 MPa (264 psi) 49.0 °C
120 °F
ISO 75-2
Borealis Daplen™ ED117AE Polypropylene TPO Compound
Daplen™ ED117AE is a 10% mineral filled elastomer modified polypropylene compound intended for injection molding. This material has excellent balanced mechanical properties and gives a good surfac..
Deflection Temperature at 1.8 MPa (264 psi) 49.0 °C
120 °F
ISO 75
Unipetrol PP MONSTEN® MT 935 Polypropylene Random Copolymer
Made for injection molding applications. Antistatic and transparent stabilization. Random copolymer.Information provided by Unipetrol RPA
Deflection Temperature at 1.8 MPa (264 psi) 49.0 °C
120 °F
ISO 75
Unipetrol PP MONSTEN® MT 802 Polypropylene Random Copolymer
Applications include injection molding and extrusion. Antistatic and transparent stabilization. Random copolymer.Information provided by Unipetrol RPA
Deflection Temperature at 1.8 MPa (264 psi) 49.0 - 49.7 °C
120 - 121 °F
UV Postcure; ASTM D648
DSM Somos® BioClear
Parts created with Somos® BioClear are designed for medical applications that are non-implant and have limited contact with the body such as device prototyping. They are shatter-resistant so they w..
Deflection Temperature at 1.8 MPa (264 psi) 49.0 - 57.0 °C
120 - 135 °F
UV Postcure; ASTM D648-07B
DSM Somos® NeXt LV Grey
The second member of the Somos® NeXt family, Somos® NeXt LV Grey delivers the durability and functionality, with a finer resolution of details and faster part processing. This third-generation, hi..
Deflection Temperature at 1.8 MPa (264 psi) 49.0 - 50.0 °C
120 - 122 °F
Thermal Postcure; ASTM D648-98c
DSM Somos® WaterClear® Ultra 10122 Optically Clear, Colorless, Rigid, Stereolithography Resin
DescriptionDSM Somos® WaterClear Ultra 10122 is a next generation optically clear resin with ABS like properties and good temperature resistance. It produces colorless, functional, accurate parts ..
Deflection Temperature at 1.8 MPa (264 psi) 49.0 °C
120 °F
ASTM-D648
Braskem PCD 0810 HECO Polypropylene Heterophasic Copolymer
PCD 0810 is a high melt flow rate heterophasic copolymer developed for injection molding applications. The product combines high impact strength and good processability with a fair stiffness level. ..
Deflection Temperature at 1.8 MPa (264 psi) 49.0 °C
120 °F
ASTM D648
Braskem RP 141 Injection Molding Polypropylene
Description: RP 141 is a high melt flow rate random copolymer designed for injection molding. This product offers outstanding transparency, very good stiffness/impact strength balance and excellent ..
Deflection Temperature at 1.8 MPa (264 psi) 49.0 °C
120 °F
ASTM D648
Ashley Polymers Ashlene® 105 PBT Polyester
A general purpose polyester with low shrinkage and good flow.Data provided by the manufacturer
Deflection Temperature at 1.8 MPa (264 psi) 49.0 - 250 °C
120 - 482 °F
Average value: 144 °C Grade Count:231
Overview of materials for Nylon 6, Heat Stabilized
This property data is a summary of similar materials in the MatWeb database for the category "Nylon 6, Heat Stabilized". Each property range of values reported is minimum and maximum values of appro..
Deflection Temperature at 1.8 MPa (264 psi) 49.0 °C
120 °F
ASTM D648
Adell RZ-14 Copolymer Polypropylene, 20% Calcium Carbonate Filled
Data provided by Adell Plastics, Inc.
Deflection Temperature at 1.8 MPa (264 psi) 49.0 °C
120 °F
ISO 75-2
BASF Ultradur® B 4300 M2 12.5% Mineral Filled PBT
Description: Is a PBT-HI, mineral-reinforced, impact-modified injection-molding grade for rigid parts, for example automotive power door locks.Information provided by BASF
Deflection Temperature at 1.8 MPa (264 psi) 49.0 °C
120 °F
ASTM D648
PlastxWorld Veroplas PA2009L Nylon 6
general purpose, super lubricated injection molding gradeInformation provided by PlastxWorld Inc.
Deflection Temperature at 1.8 MPa (264 psi) 49.0 °C

@Thickness 3.20 mm
120 °F

@Thickness 0.126 in
unannealed; ASTM D648
SABIC Innovative Plastics Valox® V2105U PBT (Asia Pacific)
Unreinforced, Wear resistant, UV Stabilized PBT designed for outdoor, agricultural, industrial and automotive applications. This grade has very high impact strength to stiffness ratio.
Deflection Temperature at 1.8 MPa (264 psi) 49.0 °C
120 °F
ASTM-D648
Braskem RP 145 RACO Random Polypropylene Copolymer
RP 145 is a high melt flow rate random copolymer designed for use in thin-walled injection molding parts. This product offers good transparency, very good stiffness/impact strength balance, excellen..
Copyright © lookpolymers.com All Rights Reserved