Borealis Daplen™ EE115T TPO Compound

Category Polymer , Thermoplastic , Elastomer, TPE , Thermoplastic Olefinic Elastomer (TPO) , Polypropylene (PP) , TPO
Manufacturer Borealis
Trade Name Daplen™
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Borealis Daplen™ EE115T TPO Compound.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Daplen EE115T is a 10% mineral and elastomer modified polypropylene compound intended for injection molding. Daplen EE115T is a material with excellent impact /stiffness ratio. Thanks to its low thermal expansion this material is suitable to mold parts requiring low change of dimensions over a broad temperature range. This product is optimized to give good surface aesthetics.Daplen EE115T has been developed especially for bumpers, spoilers and exterior trims.Information provided by the Manufacturer.
Physical Properties Metric English Comments
Density 0.990 g/cc
0.0358 lb/in³
ISO 1183
Linear Mold Shrinkage 0.0085 - 0.0095 cm/cm
0.0085 - 0.0095 in/in
Borealis Method
Melt Flow 10 g/10 min

@Load 2.16 kg,
Temperature 230 °C
10 g/10 min

@Load 4.76 lb,
Temperature 446 °F
ISO 1133
Mechanical Properties Metric English Comments
Ball Indentation Hardness 35.0 MPa
5080 psi
At 132 N/10 sec; ISO 2039
Tensile Strength, Yield 17.00 MPa
2465 psi
At 50 mm/min; ISO 527-2
Elongation at Break 450 %
450 %
At 50 mm/min; ISO 527-2
Elongation at Yield 7.0 %
7.0 %
At 50 mm/min; ISO 527-2
Tensile Modulus 1.15 GPa
167 ksi
At 1 mm/min; ISO 527-2
Flexural Modulus 1.10 GPa
160 ksi
At 2 mm/min; ISO 178
Charpy Impact Unnotched NB
NB
ISO 179/1eU
NB

@Temperature -20.0 °C
NB

@Temperature -4.00 °F
ISO 179/1eU
Charpy Impact, Notched 6.50 J/cm²
30.9 ft-lb/in²
ISO 179/1eA
0.500 J/cm²

@Temperature -30.0 °C
2.38 ft-lb/in²

@Temperature -22.0 °F
ISO 179/1eA
0.650 J/cm²

@Temperature -20.0 °C
3.09 ft-lb/in²

@Temperature -4.00 °F
ISO 179/1eA
Thermal Properties Metric English Comments
CTE, linear <= 85.0 µm/m-°C

@Temperature -30.0 - 80.0 °C
<= 47.2 µin/in-°F

@Temperature -22.0 - 176 °F
Borealis Method
Deflection Temperature at 0.46 MPa (66 psi) 87.0 °C
189 °F
ISO 75-2
Deflection Temperature at 1.8 MPa (264 psi) 49.0 °C
120 °F
ISO 75-2
Vicat Softening Point 126 °C
259 °F
A (10N); ISO 306
Processing Properties Metric English Comments
Melt Temperature 220 - 260 °C
428 - 500 °F
Polymer Mass Temp
Mold Temperature 30.0 - 50.0 °C
86.0 - 122 °F