Thermal Properties | Metric | English | Comments |
---|---|---|---|
Deflection Temperature at 0.46 MPa (66 psi) | 49.0 - 53.0 °C | 120 - 127 °F | ASTM D648 |
Proto3000 Accura® 50 Plastic Stereolithography (SLA) Prototyping Polymer Simulate the properties and appearance of molded ABS with this durable, accurate and versatile plastic.Features:Durable and stiffOutstanding accuracy w/out shrinkage related distortionChoice of grey.. |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 49.0 °C | 120 °F | ASTM D648 |
RedEye On Demand VeroBlack PolyJet™ FC870 for Rapid Prototyping Vero PolyJet Resin (VeroBlue™ FC840 & VeroBlack™ FC870) is a photopolymer resin designed for precise jetting in super fine layers by PolyJet™ Technology, often used in rapid prototyping. Our Vero.. |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 49.0 °C | 120 °F | ASTM D648 |
RedEye On Demand VeroBlue PolyJet™ FC840 for Rapid Prototyping Vero PolyJet Resin (VeroBlue™ FC840 & VeroBlack™ FC870) is a photopolymer resin designed for precise jetting in super fine layers by PolyJet™ Technology, often used in rapid prototyping. Our Vero.. |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 49.0 °C | 120 °F | ASTM D648 |
RedEye On Demand VeroWhite PolyJet Resin White for Rapid Prototyping Vero PolyJet Resin (VeroBlue™ FC840 & VeroBlack™ FC870) is a photopolymer resin designed for precise jetting in super fine layers by PolyJet™ Technology, often used in rapid prototyping. Our Vero.. |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 49.0 °C | 120 °F | ASTM D648 |
ExxonMobil Escorene® LL-8361 LLDPE, Rotational Molding Powder
(discontinued **) Data Provided by Exxon Chemical Canada.Characteristics: Fully formulated, UV-8 type protection, Good flowUses: Consumer items, Potable water tanks, Laundry tubs |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 49.0 °C | 120 °F | ASTM D648 |
NOVA Chemicals Novapol® TR-0338-UI Hexene MDPE Rotational Molding Resin Excellent low temperature impact properties, Excellent ESCR, Good stiffness, Wide processing windowApplications: General purpose custom molding, Chemical containers, IBCs, Fish boxes, Septic tanks, .. |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 49.0 °C | 120 °F | ASTM D648 |
NOVA Chemicals Novapol® TR-0338-UIG Hexene MDPE Rotational Molding Resin Excellent low temperature impact properties, Excellent ESCR, Good stiffness, Wide processing windowApplications: General purpose custom molding, Chemical containers, IBCs, Fish boxes, Septic tanks, .. |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 49.0 °C | 120 °F | ASTM D648 |
A. Schulman POLYAXIS® CP812 Stabilized Compounded Rotational Molding Resin DescriptionPolyaxis CP 812 is a stabilized compounded rotational molding resin with a combination of good flow and stiffness. NOTE: Physical properties are based on rotationally molded samples from .. |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 49.0 °C | 120 °F | ASTM D648 |
A. Schulman POLYAXIS® CP812 Stabilized Compounded Rotational Molding Resin DescriptionPolyaxis CP 812 is a stabilized compounded rotational molding resin with a combination of good flow and stiffness. NOTE: Physical properties are based on rotationally molded samples from .. |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 49.0 °C | 120 °F | ASTM D648 |
A. Schulman POLYAXIS® CP813-31 General-Purpose Polyethylene DescriptionPolyaxis CP 813-31 is a general-purpose black linear low density polyethylene compound offering quick cycles and part to part consistency. NOTE: Physical properties are based on rotationa.. |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 49.0 °C | 120 °F | ASTM D648 |
A. Schulman POLYAXIS® CP812 Stabilized Compounded Rotational Molding Resin DescriptionPolyaxis CP 812 is a stabilized compounded rotational molding resin with a combination of good flow and stiffness. NOTE: Physical properties are based on rotationally molded samples from .. |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 49.0 °C | 120 °F | ASTM D648 |
A. Schulman POLYAXIS® CP813-31 General-Purpose Polyethylene DescriptionPolyaxis CP 813-31 is a general-purpose black linear low density polyethylene compound offering quick cycles and part to part consistency. NOTE: Physical properties are based on rotationa.. |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 49.0 °C | 120 °F | ASTM D648 |
A. Schulman POLYAXIS® CP813-31 General-Purpose Polyethylene DescriptionPolyaxis CP 813-31 is a general-purpose black linear low density polyethylene compound offering quick cycles and part to part consistency. NOTE: Physical properties are based on rotationa.. |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 49.0 °C | 120 °F | ASTM D648 |
A. Schulman POLYAXIS® CP812 Stabilized Compounded Rotational Molding Resin DescriptionPolyaxis CP 812 is a stabilized compounded rotational molding resin with a combination of good flow and stiffness. NOTE: Physical properties are based on rotationally molded samples from .. |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 49.0 °C | 120 °F | ASTM D648 |
A. Schulman POLYAXIS® CP813-31 General-Purpose Polyethylene DescriptionPolyaxis CP 813-31 is a general-purpose black linear low density polyethylene compound offering quick cycles and part to part consistency. NOTE: Physical properties are based on rotationa.. |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 49.0 °C | 120 °F | ASTM D648 |
A. Schulman POLYAXIS® CP812 Stabilized Compounded Rotational Molding Resin DescriptionPolyaxis CP 812 is a stabilized compounded rotational molding resin with a combination of good flow and stiffness. NOTE: Physical properties are based on rotationally molded samples from .. |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 49.0 °C | 120 °F | ASTM D648 |
A. Schulman POLYAXIS® CP812 Stabilized Compounded Rotational Molding Resin DescriptionPolyaxis CP 812 is a stabilized compounded rotational molding resin with a combination of good flow and stiffness. NOTE: Physical properties are based on rotationally molded samples from .. |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 49.0 °C | 120 °F | ASTM D648 |
A. Schulman POLYAXIS® CP813-31 General-Purpose Polyethylene DescriptionPolyaxis CP 813-31 is a general-purpose black linear low density polyethylene compound offering quick cycles and part to part consistency. NOTE: Physical properties are based on rotationa.. |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 49.0 °C | 120 °F | ASTM D648 |
Covestro Baydur® SFR-243 Polyurethane Composite RRIM Foam, 15% Milled Glass Filled, MDI-based 2-Component Liquid System 0.25 in. thickness.Information provided by Bayer Corporation, Polyurethanes DivisionAs of 1 September 2015, Bayer MaterialScience was separated from Bayer AG and officially adopted its new name – C.. |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 49.0 - 53.0 °C | 120 - 127 °F | ASTM D648 |
3D Systems Accura® 50 Plastic for SLA® Systems Simulate the properties and appearance of molded ABS. For use with the Viper™ SLA® system, SLA 3500, SLA 5000 and SLA 7000 systems.ApplicationsFunctional components for assemblies, mock-ups and te.. |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 49.0 - 65.0 °C | 120 - 149 °F | ASTM D648 |
Arkema Group KYNAR FLEX® 2950-05 Polyvinylidene Fluoride Copolymer - Extrusion & Molding Characteristics: Natural resin - translucent, off-white hemispheres. Very flexible, flame and smoke suppressant. High stability in harsh thermal, chemical and ultraviolet environments. High toug.. |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 49.0 °C | 120 °F | ASTM-D648 |
Braskem IJ33D LLDPE Injection Molding Polyethylene Copolymer IJ33D is a linear low-density polyethylene, narrow molecular weight butene-1 copolymer produced by the solution process for injection molding applications. It offers high fluidity, excellent flexibi.. |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 49.0 °C | 120 °F | ASTM-D648 |
Braskem IN34 LLDPE Injection Molding Polyethylene Copolymer IN34 is a linear low-density polyethylene, narrow molecular weight butene-1 copolymer produced by the solution process for injection molding applications. It offers high fluidity, excellent flexibil.. |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 49.0 - 62.0 °C | 120 - 144 °F | Average value: 56.1 °C Grade Count:36 |
Overview of materials for Linear Low Density Polyethylene (LLDPE), Rotational Molding Grade This property data is a summary of similar materials in the MatWeb database for the category "Linear Low Density Polyethylene (LLDPE), Rotational Molding Grade". Each property range of values report.. |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 49.0 - 60.0 °C | 120 - 140 °F | Average value: 54.4 °C Grade Count:13 |
Overview of materials for Linear Medium Density Polyethylene (LMDPE), Rotational Molded This property data is a summary of similar materials in the MatWeb database for the category "Linear Medium Density Polyethylene (LMDPE), Rotational Molded". Each property range of values reported i.. |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 49.0 °C | 120 °F | ASTM D648 |
A. Schulman POLYAXIS® CP813-31 General-Purpose Polyethylene DescriptionPolyaxis CP 813-31 is a general-purpose black linear low density polyethylene compound offering quick cycles and part to part consistency. NOTE: Physical properties are based on rotationa.. |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 49.0 °C | 120 °F | ASTM D648 |
ExxonMobil Escorene® LL-8302 LMDPE Rotational Molding Grade
(discontinued **) Data provided by the manufacturer, Exxon Chemical.LL-8300 series are linear medium density polyethylene resins that provide outstanding environmental stress crack resistance. LL-8302 is the base re.. |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 49.0 °C | 120 °F | ASTM D648 |
ExxonMobil Escorene® LL-8361 LMDPE Rotational Molding Grade
(discontinued **) Data provided by the manufacturer, Exxon Chemical.LL-8300 series are linear medium density polyethylene resins that provide outstanding environmental stress crack resistance. LL-8361 is fully formu.. |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 49.0 - 65.0 °C | 120 - 149 °F | ASTM D648 |
Arkema Group KYNAR FLEX® 2750-01 Polyvinylidene Fluoride Copolymer - Extrusion & Molding Characteristics: Natural resin - translucent, off-white hemispheres. Very flexible, lubricated. High stability in harsh thermal, chemical and ultraviolet environments. High toughness and mechani.. |