A. Schulman POLYAXIS® CP812 Stabilized Compounded Rotational Molding Resin

Category Polymer , Thermoplastic
Manufacturer
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF A. Schulman POLYAXIS® CP812 Stabilized Compounded Rotational Molding Resin.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
DescriptionPolyaxis CP 812 is a stabilized compounded rotational molding resin with a combination of good flow and stiffness. NOTE: Physical properties are based on rotationally molded samples from unpigmented resins. Density and ESCR tests were performed on compression molded samples.Information provided by A. Schulman.
Physical Properties Metric English Comments
Specific Gravity 0.935 g/cc
0.935 g/cc
ASTM D792
ESCR 100% Igepal® >= 1000 hour
>= 1000 hour
ASTM D1693
Melt Index of Compound 6.0 - 7.0 g/10 min
6.0 - 7.0 g/10 min
2.16/190; ASTM D1238
Mechanical Properties Metric English Comments
Tensile Strength, Yield 15.5 MPa
2250 psi
2"/min; ASTM D638
Elongation at Break 500 %
500 %
2"/min; ASTM D638
Flexural Modulus 0.538 GPa
78.0 ksi
at 1% secant modulus; ASTM D790
Impact Test 65.1 J

@Thickness 3.17 mm,
Temperature -40.0 °C
48.0 ft-lb

@Thickness 0.125 in,
Temperature -40.0 °F
ARM impact
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 49.0 °C
120 °F
ASTM D648
Descriptive Properties Value Comments
UV Stabilization UV-8