- Polymer Property : Deflection Temperature at 0.46 MPa (66 psi) = 306 °F
Polymer Property : Deflection Temperature at 0.46 MPa (66 psi) = 306 °F Product List
Thermal PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 152 °C | 306 °F | Unannealed; ASTM D648 |
| Multibase Multi-Pro® 3010 X Black Polypropylene Forms:PelletsProcessing Methods:Injection MoldingInformation provided by Multibase |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 152 °C | 306 °F | ASTM D648 |
| RheTech Products GC15P200-00 15% Glass Fiber Reinforced Polypropylene Copolymer, Chemically Coupled, Black Applications: Electrical housingsUnderhood componentsConsumer goodsInjection molding conditions reported in table.Information provided by RheTech Products. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 152 °C @Thickness 3.18 mm |
306 °F @Thickness 0.125 in |
Unannealed; ASTM D648 |
| PolyOne Maxxam™ PPC-20G Black Polypropylene Copolymer (PP Copolymer) PolyOne's Maxxam™ family of polypropylene- and polyethylene-based products covers a wide range of applications, markets and performance requirements. Standard grades are compounded with calcium car.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 152 °C @Thickness 3.18 mm |
306 °F @Thickness 0.125 in |
Unannealed; ASTM D648 |
| PolyOne Maxxam™ PPC-20G Nat Polypropylene Copolymer (PP Copolymer) PolyOne's Maxxam™ family of polypropylene- and polyethylene-based products covers a wide range of applications, markets and performance requirements. Standard grades are compounded with calcium car.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 152 °C | 306 °F | 120°C/h; ISO 75/1 |
| Polykemi AB POLYfill PPH GF1030 PD2 Polypropylene Homopolymer, Glass Fibre-Reinforced, Chemically Coupled Information provided by Polykemi AB |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 152 °C | 306 °F | Unannealed; ASTM D648 |
| Ravago Manufacturing Americas Hylex® P1310G30 HB Polycarbonate, 30% Fiberglass Reinforced, UV Stabilized Information provided by Ravago. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 152 °C | 306 °F | 120°C/h; ISO 75/1 |
| Polykemi AB POLYfill PPH GF4030 PD2 Polypropylene Homopolymer, Glass Fibre-Reinforced, Chemically Coupled Information provided by Polykemi AB |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 152 °C @Thickness 3.20 mm |
306 °F @Thickness 0.126 in |
ASTM D648 |
| Covestro Apec® DP9-9331 High-Heat Polycarbonate, General Purpose
(discontinued **) Information provided by Bayer Corporation, Plastics DivisionAs of 1 September 2015, Bayer MaterialScience was separated from Bayer AG and has officially adopted its new name – Covestro. This produ.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 152 °C @Thickness 4.00 mm |
306 °F @Thickness 0.157 in |
after annealing 150°C 16 hr; ASTM D648 |
| Solvay Specialty Polymers Solef® 3108/0903 Anti-static PVDF Compound
(discontinued **) Key features of this grade: Anti-static, Formulated. Recommended processing is injection. Available as granules.General information about SOLEF® PVDF: SOLEF® PVDF is a fluorinated semi-crystall.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 152 °C | 306 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| SABIC Innovative Plastics LNP LUBRICOMP IN001 PA6.12 LNP* LUBRICOMP* IN001 is a compound based on Nylon 6/12 resin containing 2% Moly. Added feature of this grade is: Wear Resistant. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 152 °C | 306 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| SABIC Innovative Plastics LNP Stat-kon DEL369E PC LNP* Stat-Kon* DEL369E is a compound based on Polycarbonate containing Carbon Fiber and PTFE. Characteristics of this grade are Flame Retardant and Statically Conductive.This data was supplied by S.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 152 °C @Thickness 3.20 mm |
306 °F @Thickness 0.126 in |
unannealed; ASTM D 648 |
| SABIC Innovative Plastics LNP Stat-kon KS302 Acetal Copoly LNP* Stat-kon* KS302 is a compound based on Acetal Copolymer resin containing Stainless Steel.This data was supplied by SABIC-IP for the Americas region. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 152 °C @Thickness 3.20 mm |
306 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics LNP STAT-KON KS302 Acetal Copoly (Asia Pacific) LNP* Stat-kon* KS302 is a compound based on Acetal Copolymer resin containing Stainless Steel. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 152 °C | 306 °F | ASTM D648 |
| SPS Guang Zhou POLLITEâ„¢ 1002G30 Flame-retarded/GF30%-Polycarbonate Characteristic: High mechanical properties, high rigidity, high heat resistant, good dimensional stability, good flame retardanceApplications: E/E parts, power tool, office suppliesInformation Provi.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 152 °C | 306 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| SABIC Innovative Plastics LNP THERMOCOMP KB006 Acetal LNP* THERMOCOMP* KB006 is a compound based on Acetal containing 30% Glass Bead. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 152 °C | 306 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| SABIC Innovative Plastics LNP THERMOCOMP PB006SXS PA 6 (Europe-Africa-Middle East) LNP* THERMOCOMP* PB006SXS is a compound based on PA 6 resin containing Glass Bead. Added features include: Heat Stabilized. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 152 °C | 306 °F | Unannealed; ASTM D648 |
| Techmer ES HiFill FR® PC GF20 FR 20% Glass Filled Availability: North AmericaForms: PelletsFiller/Reinforcement: Glass Fiber, 20% Filler by WeightFeatures: Flame RetardantInformation provided by TP Composites, Inc. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 152 °C @Thickness 3.20 mm |
306 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics LNP THERMOCOMP TF002 PU LNP* THERMOCOMP* TF002 is a compound based on Polyurethane resin containing 10% Glass Fiber. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 152 °C | 306 °F | HDT-A; ISO 75-2 |
| Borealis Xmod™ GD301HP High Performance 32% Glass Fiber Reinforced Xmod GD301HP is reinforced with 32% chemically coupled glass fibers and based on specific Polymer matrix material which is bringing excellent mechanical properties (impact behavior) and very good st.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 152 °C | 306 °F | |
| Covestro Apec® HT KU 1-9331 High-Heat Polycarbonate Transparent and opaque shades possible.Applications: Lighting, automotive and household goods, light covers, indicator and brake light lenses.Information provided by Bayer.As of 1 September 2015, Ba.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 152 °C | 306 °F | ASTM D648 |
| Aclo Accutech Polypropylene Homopolymer HP0334G10CL Glass Reinforced Coupled |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 152 °C | 306 °F | ASTM D648 |
| Aclo Accutech Polypropylene Homopolymer HP0334G20M10CL Glass/Mineral Reinforced Coupled |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 152 °C | 306 °F | ASTM D648 |
| Aclo Accutech Polypropylene Homopolymer HP0339G15M15CL Glass/Mineral Reinforced Coupled |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 152 °C | 306 °F | ISO 75-1, -2 |
| Celanese Celcon® MC90 POM, Mineral Reinforced Celcon« acetal copolymer grade MC90 is a mineral reinforced grade offering low warp, improved dimensional stability, improved stiffness, improved practical impact and retention of other base resin .. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 152 °C | 306 °F | ISO 75-1, -2 |
| Celanese Celcon® WR90Z POM, UV Resistant Celcon« WR90Z is a standard nominal 9 melt flow rate based acetal copolymer stabilized to provide maximum ultraviolet radiation resistance in outdoor applications while retaining a good balance of .. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 152 °C | 306 °F | ASTM D648 |
| Ashley Polymers Ashlene® P1440 Polycarbonate, 40% Glass Reinforced A 40% glass reinforced polycarbonate for maximum mechanical strength and thermal properties. P1443 with UV stabilizer.Data provided by the manufacturer |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 152 °C | 306 °F | ISO 75 -1 & -2 flat |
| Asahi Kasei Tenac®-C 4563 Copolymer Acetal Resin Weather-Resistant grade containing UV absorber and other additives for superior weathering abilityInformation provided by Asahi Kasei Corporation. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 152 °C @Thickness 6.35 mm |
306 °F @Thickness 0.250 in |
Unannealed; ASTM D648 |
| PolyOne Gravi-Tech™ GRV-NY-060-CU Polyamide 6 (Nylon 6) Information provided by PolyOne |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 152 °C | 306 °F | 75/Method Bf |
| Premix Thermoplastics PRE-ELEC® PA 1408 Conductive Thermoplastic Compound PRE-ELEC® PA 1408 is a conductive thermoplastic compound based on polyamide 6. Conductivity is achieved by using conductive carbon black. In addition to a low electrical resistivity PRE-ELEC® PA 1.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 152 °C | 306 °F | ASTM D648 |
| RheTech Products GC15P200-01 15% Glass Fiber Reinforced Polypropylene Copolymer, Chemically Coupled, Black Applications: Electrical housingsUnderhood componentsInjection molding conditions reported in table.Information provided by RheTech Products. |
|||