PolyOne Maxxam™ PPC-20G Black Polypropylene Copolymer (PP Copolymer)
| Category | Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene Copolymer |
| Manufacturer | PolyOne Corporation |
| Trade Name | Maxxam™ |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | PolyOne Maxxam™ PPC-20G Black Polypropylene Copolymer (PP Copolymer).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
PolyOne's Maxxam™ family of polypropylene- and polyethylene-based products covers a wide range of applications, markets and performance requirements. Standard grades are compounded with calcium carbonate, glass and talc to provide a desired balance of properties including stiffness, durability, impact resistance and heat resistance. Custom grades are available with features such as UV stabilizers, heat stabilizers, custom color, high impact, etc.Product Code: EM10005762**Information provided by PolyOne
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.03 g/cc | 1.03 g/cc | ASTM D792 |
| Linear Mold Shrinkage, Flow | 0.0020 - 0.0050 cm/cm | 0.0020 - 0.0050 in/in | ASTM D955 |
| Melt Flow | 4.0 g/10 min @Load 2.16 kg, Temperature 230 °C |
4.0 g/10 min @Load 4.76 lb, Temperature 446 °F |
Procedure A; ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 50.0 MPa | 7250 psi | Type I, 51 mm/min; ASTM D638 |
| Elongation at Break | 9.0 % | 9.0 % | Type I, 51 mm/min; ASTM D638 |
| Flexural Strength | 62.1 MPa | 9010 psi | ASTM D790 |
| Flexural Modulus | 3.03 GPa | 439 ksi | ASTM D790 |
| Izod Impact, Notched | 0.640 J/cm @Thickness 3.18 mm, Temperature 23.0 °C |
1.20 ft-lb/in @Thickness 0.125 in, Temperature 73.4 °F |
Injection Molded; ASTM D256A |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 152 °C @Thickness 3.18 mm |
306 °F @Thickness 0.125 in |
Unannealed; ASTM D648 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Mold Temperature | 16.0 - 50.0 °C | 60.8 - 122 °F |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Additive | Impact Modifier | |
| Appearance | Black | |
| Features | Copolymer | |
| General Purpose | ||
| Impact Modified | ||
| Filler / Reinforcement | Glass Fiber Reinforcement | |
| Unspecified FillerReinfor., 20% Filler by Weight | ||
| Forms | Pellets | |
| Generic Material | PP Copolymer | |
| Generic Name | Polypropylene Copolymer (PP Copolymer) | |
| Processing Method | Injection Molding | |
| Regional Availability | Africa & Middle East | |
| Asia Pacific | ||
| Europe | ||
| North America | ||
| South America | ||
| Uses | Automotive Applications | |
| Construction Applications | ||
| Consumer Applications | ||
| General Purpose | ||
| Industrial Applications |