Solvay Engineered Polymers SEQUEL® 2300 Engineered Polyolefin  (discontinued **)

Category Polymer , Thermoplastic , Polyolefin
Manufacturer
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Solvay Engineered Polymers SEQUEL® 2300 Engineered Polyolefin  (discontinued **).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Description: SEQUEL® 2300 engineered polyolefin is designed for large mold-in-color automotive interior applications that require high stiffness and dimensional stability over a broad temperature range. This material exhibits excellent low-gloss surface appearance and processability. Applications: Instrument panels and components, A and B-pillar covers, and miscellaneous interior trim components that must exhibit high modulus and superior impact performance. Information provided by Solvay Engineered Polymers.LyondellBasell acquired Solvay Engineered Polymers in 2008. This grade is not part of the current LyondellBasell product line.
Physical Properties Metric English Comments
Specific Gravity 1.06 g/cc
1.06 g/cc
ISO 1183
Filler Content 25 %
25 %
ISO 3451
Linear Mold Shrinkage 0.0094 cm/cm
0.0094 in/in
AMMS; ISO 2577
Melt Flow 11 g/10 min
11 g/10 min
ISO 1133
Mechanical Properties Metric English Comments
Hardness, Shore D 63
63
ISO 686
Tensile Strength, Yield 25.0 MPa
3630 psi
ISO R527
Flexural Modulus 2.20 GPa
319 ksi
ISO 178
Izod Impact, Notched (ISO) 24.0 kJ/m²
11.4 ft-lb/in²
ISO 180
3.50 kJ/m²

@Temperature -40.0 °C
1.67 ft-lb/in²

@Temperature -40.0 °F
ISO 180
Impact Test 22.0 J
16.2 ft-lb
multiaxial, 15 mph; ASTM D3763
25.0 J

@Temperature 0.000 °C
18.4 ft-lb

@Temperature 32.0 °F
multiaxial, 15 mph; ASTM D3763
Thermal Properties Metric English Comments
CTE, linear 60.0 µm/m-°C

@Temperature 20.0 °C
33.3 µin/in-°F

@Temperature 68.0 °F
ASTM E228
Deflection Temperature at 0.46 MPa (66 psi) 112 °C
234 °F
ISO 75
Deflection Temperature at 1.8 MPa (264 psi) 63.0 °C
145 °F
ISO 75
Descriptive Properties Value Comments
Five-Finger Scratch Resistance 3-10 N
FLTM BN 108-13