Borealis Daplen™ MD206U Polypropylene Compound 20% Mineral Filled

Category Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene, Mineral Reinforced
Manufacturer Borealis
Trade Name Daplen™
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Borealis Daplen™ MD206U Polypropylene Compound 20% Mineral Filled.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Daplen MD206U is a 20% mineral filled polypropylene compound intended for injection molding. MD206U has been developed especially for automotive interior parts that require excellent balance between the impact strength and stiffness and good surface quality. In addition it has a good UV and weathering stability.Daplen MD206U has been developed for door panels and pockets, consoles, handles, bumper reinforcement parts, and cowl vent grilles.Information provided by the Manufacturer.
Physical Properties Metric English Comments
Density 1.04 g/cc
0.0376 lb/in³
ISO 1183
Linear Mold Shrinkage 0.011 cm/cm
0.011 in/in
Borealis Method
Melt Flow 7.0 g/10 min

@Load 2.16 kg,
Temperature 230 °C
7.0 g/10 min

@Load 4.76 lb,
Temperature 446 °F
ISO 1133
24 g/10 min

@Load 5.00 kg,
Temperature 230 °C
24 g/10 min

@Load 11.0 lb,
Temperature 446 °F
ISO 1133
Mechanical Properties Metric English Comments
Ball Indentation Hardness 59.0 MPa
8560 psi
H385/30; ISO 2039
Tensile Strength, Yield 24.99 MPa
3625 psi
At 50 mm/min; ISO 527-2
Elongation at Yield 5.0 %
5.0 %
At 50 mm/min; ISO 527-2
Flexural Modulus 2.25 GPa
326 ksi
At 5 mm/min; ISO 178
Charpy Impact Unnotched NB
NB
ISO 179/1eU
3.30 J/cm²

@Temperature -40.0 °C
15.7 ft-lb/in²

@Temperature -40.0 °F
ISO 179/1eU
3.70 J/cm²

@Temperature -20.0 °C
17.6 ft-lb/in²

@Temperature -4.00 °F
ISO 179/1eU
Charpy Impact, Notched 1.20 J/cm²
5.71 ft-lb/in²
ISO 179/1eA
0.250 J/cm²

@Temperature -20.0 °C
1.19 ft-lb/in²

@Temperature -4.00 °F
ISO 179/1eA
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 112 °C
234 °F
ISO 75-2
Deflection Temperature at 1.8 MPa (264 psi) 60.4 °C
141 °F
ISO 75-2
Vicat Softening Point 80.0 °C
176 °F
B (50N); ISO 306
150 °C
302 °F
A (10N); ISO 306
Processing Properties Metric English Comments
Melt Temperature 210 - 260 °C
410 - 500 °F
Mold Temperature 30.0 - 50.0 °C
86.0 - 122 °F
Descriptive Properties Value Comments
Emissions, ug C/g 10
VDA 277
Fogging % 958.2
At 100°C/3 hours
Fogging, mg 0.5
At 100°C/ 16 hours