Polymer Property : Melting Point = 306 °C Product List

Thermal Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Thermal Properties	Metric	English	Comments
Melting Point	306 °C	583 °F	DSC
Performance Polymers IPS II PPL-A1050 PEKK (Polyetherketoneketone) Branched Standard Grade Amber pellets; neat resinInformation provided by Infinite Polymer System II.
Melting Point	306 Â°C	583 Â°F
Kuraray Genestarâ„¢ G1300H Nylon, 30% Glass Filled Standard HB grade. Halogen free, following the standards that Br is less than 900ppm, Cl is less than 900ppm, and total of halogen amount (Br and Cl) is less than 1500ppm. It is suitable for use in ..
Melting Point	306 Â°C	583 Â°F
Kuraray Genestarâ„¢ G1302 Nylon, 30% Glass Filled Abrasion Resistance HB grade. Halogen free, following the standards that Br is less than 900ppm, Cl is less than 900ppm, and total of halogen amount (Br and Cl) is less than 1500ppm. It delivers low..
Melting Point	306 Â°C	583 Â°F
Kuraray Genestarâ„¢ G1350H Nylon, 35% Glass Filled Standard HB grade. Halogen free, following the standards that Br is less than 900ppm, Cl is less than 900ppm, and total of halogen amount (Br and Cl) is less than 1500ppm. It is suitable for use in ..
Melting Point	306 Â°C	583 Â°F
Kuraray Genestarâ„¢ GA2330 Nylon, 33% Glass Filled Abrasion Resistance V-0 Grade. Can be used for applications requiring high abrasion and heat resistance, as well as flame retardancy, such as internal gear of copying machine.
Melting Point	306 Â°C	583 Â°F
Kuraray Genestarâ„¢ GN2330 Nylon, 33% Glass Filled Standard V-0 Grade. Features a balance of mechanical strength, mold-ability, and dimensional stability. Well suited for a wide range of electrical and electronic components.
Melting Point	306 Â°C	583 Â°F
Kuraray Genestarâ„¢ GN2332 Nylon, 33% Glass Filled High Flow V-0 Grade. Improves flow-ability in thin-walled parts. Used for components requiring high-flowability, such as 0.3 mm pitch connectors.
Melting Point	306 Â°C	583 Â°F
Kuraray Genestarâ„¢ GP2450NH-2 Nylon, 45% Glass Filled Standard V-0 Grade. Halogen free, following the standards that Br is less than 900ppm, Cl is less than 900ppm, and total of halogen amount (Br and Cl) is less than 1500ppm.This grade meets UL94, V-0..
Melting Point	306 Â°C	583 Â°F
Kuraray Genestarâ„¢ GT2330 Nylon, 33% Glass Filled Toughness V-0 Grade. It is well suited for components requiring a high strength in pin fitting process, due to high ductility properties.
Melting Point	306 Â°C	583 Â°F
Kuraray Genestarâ„¢ GW1458HF Nylon, 45% Glass Filled Low Warpage, High Flow HB grade. Halogen free, following the standards that Br is less than 900ppm, Cl is less than 900ppm, and total of halogen amount (Br and Cl) is less than 1500ppm.
Melting Point	306 Â°C	583 Â°F
Kuraray Genestarâ„¢ GW2458HF Nylon, 45% Glass Filled Low Warpage, High Flow V-0 Grade. It is suited for low warpage and high flow applications, making it well suited for card connectors.
Melting Point	306 Â°C	583 Â°F	ASTM D3418
Solvay Specialty Polymers AmodelÂ® AT-6130 HS Polyphthalamide (PPA), 30% Glass Fiber (Dry) AmodelÂ® AT-6130 HS is a 30% glass-reinforced, toughened polyphthalamide (PPA) resin that has more elongation than other 30% glass-reinforced grades of AmodelÂ® resin. This grade was developed f..
Melting Point	306 °C	583 °F	ASTM D4591
3M Dyneon™ PFA 6910GZ Fluoroplastic Dispersion 3M™ Dyneon™ PFA 6910GZ is a 50% solids fluorothermoplastic aqueous dispersion. It is a copolymer of tetrafluoroethylene and perfluorinated comonomers, with a melt viscosity several orders of magni..
Melting Point	306 - 360 °C	583 - 680 °F	Average value: 342 °C Grade Count:3
Overview of materials for PEKK, Unreinforced This property data is a summary of similar materials in the MatWeb database for the category "PEKK, Unreinforced". Each property range of values reported is minimum and maximum values of appropriate..
Melting Point	306 °C	583 °F	Peak; ASTM D3418
Solvay Specialty Polymers Amodel® AT-6130 HS Polyphthalamide (PPA) (Unverified Data**) Amodel AT-6130 HS is a 30% glass-reinforced, toughened polyphthalamide (PPA) resin that has more elongation than other 30% glass-reinforced grades of Amodel resin. This grade was developed for autom..
Melting Point	306 °C	583 °F
Kuraray Genestar™ GN2450 Nylon, 45% Glass Filled High Strength V-0 Grade. Features a high strength and modulus. It is well suited for FPC sliders and IC sockets, as well as other components that require modulus and dimensional precision.
Melting Point	306 °C	583 °F
Kuraray Genestar™ GR2300 Nylon, 30% Glass Filled Standard V-0 Grade. Delivers increased fluidity and weld strength. Well suited for a wide range of electrical and electronic components.