- Kuraray Genestarâ„¢ GA2330 Nylon, 33% Glass Filled
Kuraray Genestarâ„¢ GA2330 Nylon, 33% Glass Filled
| Category | Polymer , Thermoplastic , Nylon |
| Manufacturer | Kuraray Company |
| Trade Name | Genestar™ |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Kuraray Genestarâ„¢ GA2330 Nylon, 33% Glass Filled.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Abrasion Resistance V-0 Grade. Can be used for applications requiring high abrasion and heat resistance, as well as flame retardancy, such as internal gear of copying machine.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.68 g/cc | 1.68 g/cc | |
| Water Absorption | 1.1 % | 1.1 % | |
| Linear Mold Shrinkage, Flow | 0.0010 cm/cm | 0.0010 in/in | |
| Linear Mold Shrinkage, Transverse | 0.0060 cm/cm | 0.0060 in/in | |
| Melt Flow | 13 g/10 min @Load 2.16 kg, Temperature 320 °C |
13 g/10 min @Load 4.76 lb, Temperature 608 °F |
ASTM D1238 |
| Spiral Flow | 4.90 cm @Load 750 kg, Temperature 320 °C |
1.93 in @Load 1650 lb, Temperature 608 °F |
0.5mm diameter |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength | 37.0 MPa | 5370 psi | Weld; ASTM D638 |
| 175 MPa | 25400 psi | ASTM D638 | |
| Elongation at Yield | 0.40 % | 0.40 % | Weld; ASTM D638 |
| 2.5 % | 2.5 % | ASTM D638 | |
| Flexural Strength | 197 MPa | 28600 psi | ASTM D790 |
| Flexural Modulus | 11.0 GPa | 1600 ksi | ASTM D790 |
| Izod Impact, Notched | 1.00 J/cm | 1.87 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 306 °C | 583 °F | |
| Deflection Temperature at 1.8 MPa (264 psi) | 285 °C | 545 °F | ASTM D648 |
| Glass Transition Temp, Tg | 125 °C | 257 °F | |
| Flammability, UL94 | V-0 | V-0 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+16 ohm-cm | 1.00e+16 ohm-cm | ASTM D257 |
| Dielectric Constant | 3.4 @Frequency 1.00e+10 Hz |
3.4 @Frequency 1.00e+10 Hz |
ASTM D150 |
| Dielectric Strength | 30.0 kV/mm | 762 kV/in | ASTM D149 |
| Dielectric Loss Index | 0.010 @Frequency 1.00e+10 Hz |
0.010 @Frequency 1.00e+10 Hz |
ASTM D150 |
Users viewing this material also viewed the following:
- Polymax® Maxelast® P3956 TPE, PP Overmold or Standalone use
- JPJ Technologies 700F HDPE Extrusion
- Solvay Specialty Polymers Algoflon® D 2512 F Polytetrafluoroethylene (PTFE)
- SABIC Innovative Plastics Valox® DR48 PBT
- Tra-Con Tra-Bond F118 Fiber Optic Epoxy Adhesive
- Covestro Texin® 4215 Urethane Thermoplastic Elastomer
- ConocoPhillips Hydroclear® MV100 AW Hydraulic Fluid
- Braskem PN2021 EVA Foam Copolymer
- Bulk Molding Compounds BMC T40-4020-AQ High Strength Arc Quenching Molding Compound
Copyright © lookpolymers.com All Rights Reserved