- Kuraray Genestar™ GR2300 Nylon, 30% Glass Filled
Kuraray Genestar™ GR2300 Nylon, 30% Glass Filled
| Category | Polymer , Thermoplastic , Nylon |
| Manufacturer | Kuraray Company |
| Trade Name | Genestar™ |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Kuraray Genestar™ GR2300 Nylon, 30% Glass Filled.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Standard V-0 Grade. Delivers increased fluidity and weld strength. Well suited for a wide range of electrical and electronic components.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.57 g/cc | 1.57 g/cc | |
| Water Absorption | 1.1 % | 1.1 % | |
| Linear Mold Shrinkage, Flow | 0.0010 cm/cm | 0.0010 in/in | |
| Linear Mold Shrinkage, Transverse | 0.0065 cm/cm | 0.0065 in/in | |
| Melt Flow | 16 g/10 min @Load 2.16 kg, Temperature 320 °C |
16 g/10 min @Load 4.76 lb, Temperature 608 °F |
ASTM D1238 |
| Spiral Flow | 6.50 cm @Load 750 kg, Temperature 320 °C |
2.56 in @Load 1650 lb, Temperature 608 °F |
0.5mm diameter |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength | 55.0 MPa | 7980 psi | Weld; ASTM D638 |
| 180 MPa | 26100 psi | ASTM D638 | |
| Elongation at Yield | 0.70 % | 0.70 % | Weld; ASTM D638 |
| 4.0 % | 4.0 % | ASTM D638 | |
| Flexural Strength | 220 MPa | 31900 psi | ASTM D790 |
| Flexural Modulus | 10.0 GPa | 1450 ksi | ASTM D790 |
| Izod Impact, Notched | 1.00 J/cm | 1.87 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 306 °C | 583 °F | |
| Deflection Temperature at 1.8 MPa (264 psi) | 285 °C | 545 °F | ASTM D648 |
| Glass Transition Temp, Tg | 125 °C | 257 °F | |
| Flammability, UL94 | V-0 | V-0 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+16 ohm-cm | 1.00e+16 ohm-cm | ASTM D257 |
| Dielectric Constant | 3.4 @Frequency 1.00e+10 Hz |
3.4 @Frequency 1.00e+10 Hz |
ASTM D150 |
| Dielectric Strength | 30.0 kV/mm | 762 kV/in | ASTM D149 |
| Dielectric Loss Index | 0.010 @Frequency 1.00e+10 Hz |
0.010 @Frequency 1.00e+10 Hz |
ASTM D150 |
| Comparative Tracking Index | >= 600 V | >= 600 V | ASTM UL746A |
Users viewing this material also viewed the following:
- Plastcom SLOVAMID 6/66 GF 30 FRG 5 TS PA6/66, 30% glass fibre, flame retardant
- Solvay Specialty Polymers Torlon® AI-10 LM Polyamide-imide (PAI) (Unverified Data**)
- LG Chemical LUPOY GP5056F PC/ABS+GF5%, Flame Retardance
- Ineos H12SLME Polypropylene Homopolymer
- A. Schulman POLYBATCH™ Cedar 10310U Concentrate Based In LLDPE
- Hexcel® HexWeb® CR III 1/16-5052-.0015 Corrosion Resistant Specification Grade Aluminum Honeycomb
- DSM Akulon® K224-HG3 Nylon 6-15% Glass Reinforced (European and Asian Grade) (Dry)
- ELM® SoyFluid™ Hydraulic Industrial (ISO 46) Premium Biodegradable – Biobased Hydraulic Oil
- 3M SJ-2A Cold Shrink Jacket Kits
- 3A Composites Core Materials AIREX® PXw.385 Fiber-Reinforced Structural Foam Panel
Copyright © lookpolymers.com All Rights Reserved