Solvay Specialty Polymers Amodel® AT-6130 HS Polyphthalamide (PPA) (Unverified Data**)

Category	Polymer , Thermoplastic , Polyphthalamide (PPA) , Polyphthalamide (PPA), 30% Glass Fiber Reinforced
Manufacturer
Trade Name
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Solvay Specialty Polymers Amodel® AT-6130 HS Polyphthalamide (PPA) (Unverified Data**).pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Amodel AT-6130 HS is a 30% glass-reinforced, toughened polyphthalamide (PPA) resin that has more elongation than other 30% glass-reinforced grades of Amodel resin. This grade was developed for automotive snap-fit electronic connectors. It offers high flow and short molding cycles. The processing window is relatively broad and mold temperatures as low as 150°F (65°C) can be used. - Black: AT-6130 HS BK 324 - Natural: AT-6130 HS NTInjection Notes: Injection pressure between 2-4 in/sec (5-10 cm/sec). Adjust the holding pressure to one-half the injection pressure.Data is presented for dry polymer unless noted as 'conditioned'.Information provided by Solvay Specialty Polymers.

Physical Properties	Metric	English	Comments
Density	1.34 g/cc	0.0484 lb/in³	ISO 1183/A
Filler Content	30 %	30 %	Glass Fiber Reinforcement
Water Absorption	0.15 % @Time 86400 sec	0.15 % @Time 24.0 hour	ASTM D570
Linear Mold Shrinkage, Flow	0.0050 cm/cm	0.0050 in/in	ASTM D955
Linear Mold Shrinkage, Transverse	0.0080 cm/cm	0.0080 in/in	ASTM D955

Mechanical Properties	Metric	English	Comments
Tensile Strength at Break	167 MPa	24200 psi	ASTM D638
	170 MPa	24700 psi	ISO 527-2
Elongation at Break	3.2 %	3.2 %	ASTM D638
	3.3 %	3.3 %	ISO 527-2
Tensile Modulus	9.31 GPa	1350 ksi	ISO 527-2
Flexural Strength	225 MPa	32600 psi	ISO 178
Flexural Yield Strength	236 MPa	34200 psi	ASTM D790
Flexural Modulus	7.58 GPa	1100 ksi	ISO 178
	7.86 GPa	1140 ksi	ASTM D790
Izod Impact, Notched	1.30 J/cm	2.44 ft-lb/in	ASTM D256
	14.0 J/cm	26.2 ft-lb/in	ASTM D256
Charpy Impact, Notched	1.30 J/cm²	6.19 ft-lb/in²	ISO 179/1eA

Thermal Properties	Metric	English	Comments
Melting Point	306 °C	583 °F	Peak; ASTM D3418
	310 °C	590 °F	ISO 11357-3
Deflection Temperature at 0.46 MPa (66 psi)	298 °C	568 °F	Unannealed; ISO 75-2/B
Deflection Temperature at 1.8 MPa (264 psi)	276 °C	529 °F	Unannealed; ISO 75-2/A

Processing Properties	Metric	English
Rear Barrel Temperature	316 - 324 °C	601 - 615 °F
Front Barrel Temperature	327 - 332 °C	621 - 630 °F
Melt Temperature	321 - 335 °C	610 - 635 °F
Mold Temperature	65.6 - 93.3 °C	150 - 200 °F
Drying Temperature	121 °C	250 °F
Dry Time	4.00 hour	4.00 hour
Moisture Content	0.15 %	0.15 %

Descriptive Properties	Value	Comments
Additive	Heat Stabilizer
	Impact Modifier
	Lubricant
	Mold Release
Appearance	Black
	Natural Color
Automotive Specifications	ASTM D4000 PPA0123 G30 KD150 KN080 PM095 PN095 YI255 LD002 Color: BK-324, NT Black & Natural
	ASTM D6779 PA103G30
	DELPHI MS 5218 Color: BK-324, NT Black and Natural
	GM GMP.PPA.017 Color: BK-324, NT Black & Natural
	ISO 1874-PA 6T/66-HI, MH, 11-090, GF30
Availability	Africa & Middle East
	Asia Pacific
	Europe
	North America
	South America
Features	Good Chemical Resistance
	Good Flow
	Good Wear Resistance
	Heat Stabilized
	High Heat Resistance
	High Strength
	Hot Water Moldability
	Impact Modified
	Low Friction
	Lubricated
Forms	Pellets
Generic	PPA
Injection Rate	Fast
Processing Method	Water-Heated Mold Injection Molding
RoHS Compliance	RoHS Compliant
Uses	Automotive Applications
	Automotive Electronics
	Automotive Under the Hood
	Bearings
	Connectors
	Fuel Lines
	General Purpose
	Housings
	Industrial Applications
	Industrial Parts
	Lawn and Garden Equipment
	Machine/Mechanical Parts
	Metal Replacement
	Valves/Valve Parts