- Polymer Property : Vicat Softening Point = 81.0 °C
Polymer Property : Vicat Softening Point = 81.0 °C Product List
Thermal PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Vicat Softening Point | 81.0 °C | 178 °F | |
| PolyOne Geon™ Vinyl Packaging PK9 WHITE 1082 Polyvinyl Chloride, Rigid (PVC, Rigid) The HDT value refers to samples conditioned @ 50 deg.C. for 24 hrs.The bulk density test was performed under ASTM D-1895B.Information provided by PolyOne |
|||
| Vicat Softening Point | 81.0 °C | 178 °F | Rate B; 4 mm thick;10.0 mm wide molded rod; ISO 306/B50 |
| Premix Thermoplastics PRE-ELEC® ESD 7120 PRE-ELEC ESD 7120 is a static dissipative thermoplastic compound based on ABS. The dissipative property is permanent and built into the polymer chain. PRE-ELEC ESD 7120 has been developed for inject.. |
|||
| Vicat Softening Point | 81.0 °C | 178 °F | DIN 53460 |
| Ineos Nova S-3401 Medium Impact Compact Polystyrene
(discontinued **) Impact polystyrene with good flow characteristics and a high elongation. Generally used for applications where a tough material is required. The material is provided with external lubricate to imp.. |
|||
| Vicat Softening Point | 81.0 °C | 178 °F | ASTM D1525 |
| Celanese Ateva® 1070 Ethylene Vinyl Acetate Copolymer Resin
(discontinued **) Extrusion and injection molding; also recommended for profile and tubing applications and for microcellular crosslinked foam. |
|||
| Vicat Softening Point | 81.0 °C | 178 °F | ASTM D1525 |
| Celanese Ateva® 1070 Film Ethylene Vinyl Acetate Copolymer Film
(discontinued **) Ateva® 1070 resin is a multi-purpose resin. Used in co-extrusion, this resin provides superior sealability, opticals, and strength. This EVA resin may be safely used as articles or components of .. |
|||
| Vicat Softening Point | >= 81.0 °C | >= 178 °F | ASTM D 1525 |
| Karina E-844-10/219-Y-ERYM White PVC Compound Tin stabilized PVC compound, recommended for extrusion of profiles for general applications. It is supplied in pellet form and should be processed at the temperature range of 170°C to 190°C.I.. |
|||
| Vicat Softening Point | 81.0 - 83.0 °C @Load 5.00 kg |
178 - 181 °F @Load 11.0 lb |
ISO R306 |
| Fainplast Compounds RE 620 Rigid PVC, Extrusion Spiral pipes |
|||
| Vicat Softening Point | 81.0 °C | 178 °F | |
| LyondellBasell Lupolen® UHM 201 MDPE, Ultra-High Molecular Weight For the production of very high abrasion and impact resistant parts with lower slip/stick friction, as well as higher stress crack and chemical resistance. Apart from anticorrosion products, this m.. |
|||
| Vicat Softening Point | 81.0 °C | 178 °F | |
| LyondellBasell Lupolen® UHM 301 MDPE, Ultra-High Molecular Weight For the production of very high abrasion and impact resistant parts with lower slip/stick friction, as well as higher stress crack and chemical resistance. Apart from anticorrosion products, this m.. |
|||
| Vicat Softening Point | 81.0 - 83.0 °C @Load 5.00 kg |
178 - 181 °F @Load 11.0 lb |
ISO R306 |
| Fainplast Compounds RH 325 Rigid PVC, Antishock Extrusion Antishock furniture profiles |
|||
| Vicat Softening Point | 81.0 - 83.0 °C @Load 5.00 kg |
178 - 181 °F @Load 11.0 lb |
ISO R306 |
| Fainplast Compounds RK 335/1 Rigid PVC, Extrusion Lead Free Profiles |
|||
| Vicat Softening Point | 81.0 - 83.0 °C @Load 5.00 kg |
178 - 181 °F @Load 11.0 lb |
ISO R306 |
| Fainplast Compounds RKS 320 Rigid PVC, Antishock Extrusion Lead Free Various profiles, antishock |
|||
| Vicat Softening Point | 81.0 - 83.0 °C @Load 5.00 kg |
178 - 181 °F @Load 11.0 lb |
ISO R306 |
| Fainplast Compounds RL 708 Rigid PVC, Extrusion Corrugated electric pipes |
|||
| Vicat Softening Point | 81.0 °C | 178 °F | B120; ISO 306 |
| Inno-Comp INNOPOL® CS 2-9000 MA N Polypropylene Copolymer INNOPOL® CS 2-9000 MA N is a high melt flow copolymer with antistatic additive.INNOPOL® CS 2-9000 MA N is developed for producing injection molded automotive components.All information provide.. |
|||
| Vicat Softening Point | 81.0 °C @Load 5.10 kg |
178 °F @Load 11.2 lb |
120°C/h; ASTM D 1525 |
| Styrolution PS 542N HIPS Styrolution PS 542N is an impact polystyrene with high heat resistance.Information provided by Styrolution |
|||
| Vicat Softening Point | 81.0 °C | 178 °F | ASTM D1525 |
| SK Chemicals SKYTHANE® 875A T series Polyurethane SKYTHANE is a thermoplastic polyurethane elastomer (TPU). Like materials ranging from rubber to plastics, it has excellent physical properties such as anti-abrasion, oil-resistance and mechanical pr.. |
|||
| Vicat Softening Point | 81.0 °C | 178 °F | ASTM D1525 |
| DuPont Elvax® 3135SB Ethylene-Vinyl Acetate Copolymer Resin for Blown Film 12 wt% Vinyl Acetate.Elvax® 3135SB is an extrudable ethylene-vinyl acetate copolymer resin available in pellet form for use in conventional extrusion equipment designed to process polyethylene resi.. |
|||
| Vicat Softening Point | 81.0 °C | 178 °F | ASTM D1525 |
| DuPont Nucrel® 0903HC Ethylene-Methacrylic Acid Copolymer Resin for Blown and Cast Film 9 wt% Methacrylic Acid.Nucrel® 0903HC (High-Clarity) is an ethylene-methacrylic acid copolymer resin available for use in conventional blown and cast film extrusion and coextrusion equipment design.. |
|||
| Vicat Softening Point | 81.0 °C @Load 5.10 kg |
178 °F @Load 11.2 lb |
50°C per hour; ISO 306B50 |
| Total PS CPDS 856 Flame Retardant Polystyrene POLYSTYRENE (PS) COMPOUND (CPDS) 856 is a high impact halogen free polystyrene which offers a good balance of rheological and mechanical properties.Main Characteristics:Bromine and Chlorine free,UL9.. |
|||
| Vicat Softening Point | 81.0 °C | 178 °F | ASTM D1525 |
| DuPont Nucrel® 0902HC Ethylene-Methacrylic Acid Copolymer Resin for Blown and Cast Film 9 wt% Methacrylic Acid.Nucrel® 0902HC (High-Clarity) is an ethylene-methacrylic acid copolymer resin available for use in conventional blown and cast film extrusion and coextrusion equipment design.. |
|||
| Vicat Softening Point | 81.0 °C | 178 °F | ASTM D1525 |
| DuPont Nucrel® 903 Ethylene-Methacrylic Acid Copolymer Resin for Blown and Cast Film 9 wt% Methacrylic Acid.Nucrel® 0903 is an ethylene-methacrylic acid copolymer resin available for use in conventional blown and cast film extrusion and coextrusion equipment designed to process pol.. |
|||
| Vicat Softening Point | 81.0 °C | 178 °F | ASTM D1525 |
| Eastman Cadence™ GS1 Copolyester for film calendering Eastman Cadence™ copolyester, for calendered films, is a specialty plastic developed to meet the demand for an environmentally responsible material for the calendering industry. Available in diffe.. |
|||
| Vicat Softening Point | 81.0 °C | 178 °F | ASTM D1525 |
| Eastman Cadence™ GS2 Copolyester for film calendering Eastman Cadence™ copolyester, for calendered films, is a specialty plastic developed to meet the demand for an environmentally responsible material for the calendering industry. Available in diffe.. |
|||
| Vicat Softening Point | 81.0 °C | 178 °F | |
| Dow Primacor® 1410 Ethylene Acrylic Acid (EAA) Film properties below based on a film thickness of 60 µm. Data provided by Dow Chemical. |
|||
| Vicat Softening Point | 81.0 °C | 178 °F | 50N (T° increase = 5°C/h); ISO 306B50 |
| Total Lacqrene® 852 High Impact Polystyrene
(discontinued **) LACQRENE® 852 is a flame retardant, high impact polystyrene, halogen free, with excellent thermal stability.ApplicationCopier, Fax, Printers, Television, decoders, Hi-FiInformation provided provide.. |
|||
| Vicat Softening Point | 81.0 - 83.0 °C @Load 5.00 kg |
178 - 181 °F @Load 11.0 lb |
ISO R306 |
| Fainplast Compounds RE 220 Rigid PVC, Extrusion Various profiles |
|||
| Vicat Softening Point | 81.0 °C | 178 °F | 120°C/hr, 9.8N; ASTM D1525 |
| Lubrizol Estane® 2103-80AEF Thermoplastic Polyurethane Elastomer Formerly PellethaneFeature: Film resin for injection blow moldingAvailable in Americas, Europe, Middle East, Africa, India and AsiaData provided by LubrizolLubrizol acquired the Pellethane product l.. |
|||
| Vicat Softening Point | 81.0 °C | 178 °F | ASTM D1525 |
| DuPont Nucrel® 0903B Ethylene-Methacrylic Acid Copolymer Resin for Blown and Cast Film
(discontinued **) 9 wt% Methacrylic Acid.Nucrel® 0903B is an ethylene-methacrylic acid copolymer resin available for use in blown and cast film extrusion and coextrusion processes designed to process polyethylene re.. |
|||
Copyright © lookpolymers.com All Rights Reserved