- Polimeri Europa EDISTIR PD RK6223N High Impact Polystyrene (HIPS) (discontinued **)
Polimeri Europa EDISTIR PD RK6223N High Impact Polystyrene (HIPS) (discontinued **)
| Category | Polymer , Thermoplastic , Polystyrene (PS) , Polystyrene, Impact Modified |
| Manufacturer | |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Polimeri Europa EDISTIR PD RK6223N High Impact Polystyrene (HIPS)
(discontinued **).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Symbol according to ISO 1043-1: S/B Designation: Thermoplastic ISO 2897-SB,M,083-12-07-23 Halogen and Antimony free, medium impact polystyrene. This grade complies at 2 mm with IEC 65-20-2 and BSI 415/94. It exhibits easy flow and is particularly recommended for injection molding of telectronic equipments. Applications: Developed for TV back covers, monitor and printer housings.Unfilled. Suitable for Injection Molding. Supplied as pellets. Contains release agent. Contains release agent.ISO data. Information provided by EnichemPolimeri Europa now has Enichem's plastics businesses. This grade is no longer in the product line.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.05 g/cc | 0.0379 lb/in³ | |
| Melt Flow | 12 g/10 min @Load 5.00 kg, Temperature 200 °C |
12 g/10 min @Load 11.0 lb, Temperature 392 °F |
cm³/10 min |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 28.0 MPa | 4060 psi | 50 mm/min |
| Elongation at Break | 35 % | 35 % | Nominal |
| Elongation at Yield | 1.5 % | 1.5 % | 50 mm/min |
| Tensile Modulus | 2.20 GPa | 319 ksi | 1 mm/min |
| Charpy Impact Unnotched | 7.50 J/cm² | 35.7 ft-lb/in² | |
| 6.50 J/cm² @Temperature -30.0 °C |
30.9 ft-lb/in² @Temperature -22.0 °F |
||
| Charpy Impact, Notched | 0.800 J/cm² | 3.81 ft-lb/in² | |
| 0.450 J/cm² @Temperature -30.0 °C |
2.14 ft-lb/in² @Temperature -22.0 °F |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Vicat Softening Point | 81.0 °C | 178 °F | 50°C/hr; 50N |
| Flammability, UL94 | HB @Thickness 1.50 mm |
HB @Thickness 0.0591 in |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Electrical Resistivity | >= 1.00e+15 ohm-cm | >= 1.00e+15 ohm-cm | |
| Surface Resistance | >= 1.00e+15 ohm | >= 1.00e+15 ohm | |
| Dielectric Constant | 2.5 @Frequency 100 Hz |
2.5 @Frequency 100 Hz |
|
| Dielectric Strength | 65.0 kV/mm | 1650 kV/in | |
| Dissipation Factor | 0.00040 @Frequency 100 Hz |
0.00040 @Frequency 100 Hz |
|
| Comparative Tracking Index | 500 V | 500 V |