Styrolution PS 416N HIPS
| Category | Polymer , Thermoplastic , Polystyrene (PS) , Polystyrene, Impact Modified |
| Manufacturer | Styrolution |
| Trade Name | PS |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Styrolution PS 416N HIPS.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Styrolution PS 416N is medium impact polystyrene with very good flow properties. It has a high rigidity whilst displaying a very good surface gloss.Very good flow propertiesHigh rigidityVery good surface glossInformation provided by Styrolution
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.04 g/cc | 0.0376 lb/in³ | ISO 1183 |
| Moisture Absorption at Equilibrium | <= 0.10 % @Temperature 23.0 °C |
<= 0.10 % @Temperature 73.4 °F |
50% RH; ISO 62 |
| Water Absorption at Saturation | <= 0.10 % @Temperature 23.0 °C |
<= 0.10 % @Temperature 73.4 °F |
ISO 62 |
| Linear Mold Shrinkage | 0.0050 - 0.0070 cm/cm | 0.0050 - 0.0070 in/in | ISO 294-4 |
| Melt Flow | 21 g/10 min @Load 5.00 kg, Temperature 200 °C |
21 g/10 min @Load 11.0 lb, Temperature 392 °F |
ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 30.0 MPa | 4350 psi | ISO 527 |
| Elongation at Break | 35 % | 35 % | ISO 527 |
| Elongation at Yield | 1.2 % | 1.2 % | ISO 527 |
| Tensile Modulus | 2.60 GPa | 377 ksi | ISO 527 |
| Flexural Strength | 46.0 MPa | 6670 psi | ISO 178 |
| Charpy Impact Unnotched | 0.500 J/cm² | 2.38 ft-lb/in² | ISO 179 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 80.0 µm/m-°C | 44.4 µin/in-°F | ISO 11359 |
| Thermal Conductivity | 0.160 W/m-K | 1.11 BTU-in/hr-ft²-°F | DIN 52612-1 |
| Deflection Temperature at 1.8 MPa (264 psi) | 71.0 °C | 160 °F | ISO 75 |
| Vicat Softening Point | 81.0 °C @Load 5.10 kg |
178 °F @Load 11.2 lb |
120°C/h; ASTM D 1525 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | >= 1.00e+18 ohm-cm | >= 1.00e+18 ohm-cm | IEC 60093 |
| Surface Resistance | >= 1.00e+13 ohm | >= 1.00e+13 ohm | IEC 60093 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 180 - 260 °C | 356 - 500 °F | ISO 294 |
Users viewing this material also viewed the following:
- Polykemi AB SCANAMID 66 A13^ F30 Nylon 66, Glass Fiber Reinforced
- LNP Lubricomp® EFL-4036 UFE Polyetherimide, Glass Fiber Reinforcement, PTFE Lubricant (discontinued **)
- CE Phenolic Laminate
- Lehmann & Voss LUVOCOM® 1-7139-1 Polyamide 66, with aramid reinforcement and PTFE, heat stabilized
- Mueller Alloy 3530 High Leaded Brass 62% (UNS C35300)
- Haynes 625 alloy, 30% cold reduction, 1120°C anneal for 5 minutes
- Solvay Specialty Polymers Ixef® 1022 Polyarylamide (PARA), 50% Glass Fiber (Dry)
- Chase Plastics CP Pryme® NN200STL (DAM) Nylon 66, Super-Toughened, Internally Lubricated
- Dow Corning SILASTIC® LC-50-2004 PART A&B KIT
- Seals Eastern 5717 Fluorocarbon-Elastomer
Copyright © lookpolymers.com All Rights Reserved