Thermal Properties | Metric | English | Comments |
---|---|---|---|
Vicat Softening Point | 81.0 °C | 178 °F | |
PolyOne Geon™ Vinyl Packaging PK8 WHITE 1081 Polyvinyl Chloride, Rigid (PVC, Rigid) The HDT value refers to samples conditioned @ 50 deg.C. for 24 hrs.The bulk density test was performed under ASTM D-1895B.Information provided by PolyOne |
|||
Vicat Softening Point | 81.0 °C | 178 °F | Rate B/50; ISO 306 |
SABIC Innovative Plastics Cycolac® FR15 ABS Flame retardant ABS (non-PBBE additive). Good property/toughness. Excellent moldability. UL94 V-0/5VA rated. |
|||
Vicat Softening Point | 81.0 °C | 178 °F | Rate B; 4 mm thick;10.0 mm wide molded rod; ISO 306/B50 |
Premix Thermoplastics PRE-ELEC® ESD 7120 PRE-ELEC ESD 7120 is a static dissipative thermoplastic compound based on ABS. The dissipative property is permanent and built into the polymer chain. PRE-ELEC ESD 7120 has been developed for inject.. |
|||
Vicat Softening Point | 81.0 °C | 178 °F | DIN 53460 |
Ineos Nova S-3400 Medium Impact Compact Polystyrene
(discontinued **) Impact polystyrene with good flow characteristics and a high elongation. Generally used for applications where a tough material is required. For injection molding generally a lubricated type is us.. |
|||
Vicat Softening Point | 81.1 - 102 °C | 178 - 216 °F | Average value: 89.5 °C Grade Count:10 |
Overview of materials for Acrylic, High Flow, Molded This property data is a summary of similar materials in the MatWeb database for the category "Acrylic, High Flow, Molded". Each property range of values reported is minimum and maximum values of app.. |
|||
Vicat Softening Point | 81.0 - 83.0 °C @Load 5.00 kg |
178 - 181 °F @Load 11.0 lb |
ISO R306 |
Fainplast Compounds RE 240 Rigid PVC, Extrusion Electric channels |
|||
Vicat Softening Point | >= 81.0 °C | >= 178 °F | ASTM D 1525 |
Karina E-844-10/219-Y-ERYM White PVC Compound Tin stabilized PVC compound, recommended for extrusion of profiles for general applications. It is supplied in pellet form and should be processed at the temperature range of 170°C to 190°C.I.. |
|||
Vicat Softening Point | 81.0 - 83.0 °C @Load 5.00 kg |
178 - 181 °F @Load 11.0 lb |
ISO R306 |
Fainplast Compounds RH 210/W Rigid PVC, Antishock Extrusion Various antishock profiles |
|||
Vicat Softening Point | 81.0 °C | 178 °F | |
LyondellBasell Lupolen® UHM 301 MDPE, Ultra-High Molecular Weight For the production of very high abrasion and impact resistant parts with lower slip/stick friction, as well as higher stress crack and chemical resistance. Apart from anticorrosion products, this m.. |
|||
Vicat Softening Point | 81.0 - 83.0 °C @Load 5.00 kg |
178 - 181 °F @Load 11.0 lb |
ISO R306 |
Fainplast Compounds RH 325 Rigid PVC, Antishock Extrusion Antishock furniture profiles |
|||
Vicat Softening Point | 81.0 - 83.0 °C @Load 5.00 kg |
178 - 181 °F @Load 11.0 lb |
ISO R306 |
Fainplast Compounds RKS 300 Rigid PVC, Antishock Extrusion Lead Free Dielectric conduits, antishock |
|||
Vicat Softening Point | 81.0 - 83.0 °C @Load 5.00 kg |
178 - 181 °F @Load 11.0 lb |
ISO R306 |
Fainplast Compounds RKS 325 Rigid PVC, Antishock Extrusion Lead Free Various profiles, antishock |
|||
Vicat Softening Point | 81.0 °C | 178 °F | ASTM D1525 |
LG Chemical LUTENE MB9205 LDPE Injection Molding Grade Description: The physical and structural characteristics of LUTENE MB9205 give it excellent flow properties and good productivity, clarity and surface gloss.Main Application: Lids of all sizes, hous.. |
|||
Vicat Softening Point | 81.0 °C | 178 °F | ASTM D1525 |
LG Chemical LUTENE MB9500 LDPE Injection Molding Grade Description: The physical and structural characteristics of LUTENE MB9500 give it excellent flow properties and good productivity, clarity and surface gloss.Main Application: Powder coating, artific.. |
|||
Vicat Softening Point | 81.0 °C | 178 °F | ASTM D1525 |
SK Chemicals SKYTHANE® 875A T series Polyurethane SKYTHANE is a thermoplastic polyurethane elastomer (TPU). Like materials ranging from rubber to plastics, it has excellent physical properties such as anti-abrasion, oil-resistance and mechanical pr.. |
|||
Vicat Softening Point | 81.0 °C | 178 °F | ISO 306 |
Stir SpA RF 1000A (PVC) Application: Extrusion shock resistant profiles for windowsInformation provided by STIR SpA |
|||
Vicat Softening Point | 81.1 °C | 178 °F | ASTM D1525 |
Teknor Apex Sinvicomp SBC 3710 Polyvinyl Chloride, Rigid Notes: RoHS Compliant Availability: Asia Pacific Features: Food Contact AcceptableUses: Bottles; Containers Forms: Pellets Processing Method: Blow MoldingInformation Provided by Teknor Apex |
|||
Vicat Softening Point | 81.0 °C @Load 5.10 kg |
178 °F @Load 11.2 lb |
50°C per hour; ISO 306B50 |
Total PS CPDS 856 Flame Retardant Polystyrene POLYSTYRENE (PS) COMPOUND (CPDS) 856 is a high impact halogen free polystyrene which offers a good balance of rheological and mechanical properties.Main Characteristics:Bromine and Chlorine free,UL9.. |
|||
Vicat Softening Point | 81.0 °C | 178 °F | ASTM D1525 |
UBE UMERIT 500F Metallocene LLDPE Description: UBE Super Polyethylene Umerit® is an ethylene-olefin copolymer made by UBE using the metallocene catalytic method. The metallocene catalytic method results in superior physical propert.. |
|||
Vicat Softening Point | 81.0 °C | 178 °F | ASTM D1525 |
DuPont Nucrel® 903 Ethylene-Methacrylic Acid Copolymer Resin for Blown and Cast Film 9 wt% Methacrylic Acid.Nucrel® 0903 is an ethylene-methacrylic acid copolymer resin available for use in conventional blown and cast film extrusion and coextrusion equipment designed to process pol.. |
|||
Vicat Softening Point | 81.0 °C @Load 5.10 kg |
178 °F @Load 11.2 lb |
50°C per hour; ISO 306B50 |
Total PS CPDS 853 Flame Retardant Polystyrene POLYSTYRENE (PS) COMPOUND (CPDS) 853 is a high impact, high stiffness halogen free flame retardant polystyrene.Main Characteristics:Bromine and Chlorine free,UL94 V2 @ 1.6 mm with very low combustio.. |
|||
Vicat Softening Point | 81.0 °C | 178 °F | 120°C/hr, 9.8N; ASTM D1525 |
Lubrizol Estane® 2355-95AE Thermoplastic Polyurethane Elastomer Formerly PellethaneFeature: Fuel resistant, extrusion laminate coatingAvailable in Americas, Europe, Middle East, Africa, India and AsiaData provided by Dow Chemical.Lubrizol acquired the Pellethane.. |
|||
Vicat Softening Point | 81.0 °C | 178 °F | ASTM D1525 |
Eastman Cadence™ GS1 Copolyester for film calendering Eastman Cadence™ copolyester, for calendered films, is a specialty plastic developed to meet the demand for an environmentally responsible material for the calendering industry. Available in diffe.. |
|||
Vicat Softening Point | 81.0 °C | 178 °F | ASTM D1525 |
Eastman Cadence™ GS3 Copolyester for film calendering Eastman Cadence™ copolyester, for calendered films, is a specialty plastic developed to meet the demand for an environmentally responsible material for the calendering industry. Available in diffe.. |
|||
Vicat Softening Point | 81.1 °C | 178 °F | ISO 306/B50 |
ExxonMobil Exxtral™ LNT 010 Performance Polyolefin Product Description: A specialty thermoplastic polyolefin resin with high heat ageing resistance, high transparency, low color and low discoloration for contact with hot water, hot air and detergent.. |
|||
Vicat Softening Point | 81.0 °C | 178 °F | 50N (T° increase = 5°C/h); ISO 306B50 |
Total Lacqrene® 852 High Impact Polystyrene
(discontinued **) LACQRENE® 852 is a flame retardant, high impact polystyrene, halogen free, with excellent thermal stability.ApplicationCopier, Fax, Printers, Television, decoders, Hi-FiInformation provided provide.. |
|||
Vicat Softening Point | 81.0 - 83.0 °C @Load 5.00 kg |
178 - 181 °F @Load 11.0 lb |
ISO R306 |
Fainplast Compounds RE 220 Rigid PVC, Extrusion Various profiles |
|||
Vicat Softening Point | 81.0 °C | 178 °F | 120°C/hr, 9.8N; ASTM D1525 |
Lubrizol Estane® 2103-80AEF Thermoplastic Polyurethane Elastomer Formerly PellethaneFeature: Film resin for injection blow moldingAvailable in Americas, Europe, Middle East, Africa, India and AsiaData provided by LubrizolLubrizol acquired the Pellethane product l.. |
|||
Vicat Softening Point | 81.0 °C | 178 °F | ASTM D1525 |
DuPont Nucrel® 0903B Ethylene-Methacrylic Acid Copolymer Resin for Blown and Cast Film
(discontinued **) 9 wt% Methacrylic Acid.Nucrel® 0903B is an ethylene-methacrylic acid copolymer resin available for use in blown and cast film extrusion and coextrusion processes designed to process polyethylene re.. |