- Axiall Suprel® SVA 9420 Rigid PVC, Molding
Axiall Suprel® SVA 9420 Rigid PVC, Molding
| Category | Polymer , Thermoplastic , Vinyl (PVC) |
| Manufacturer | Axiall |
| Trade Name | Suprel® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Axiall Suprel® SVA 9420 Rigid PVC, Molding.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Georgia Gulf Suprel® SVA 9420 Alloy is engineered for injection molding applications that require outstanding impact resistance or toughness, particularly at low temperatures. This alloy complies with specifications frequently referenced in the telecommunications industry, has good UL flammability listings and weatherability listings per UL-746C.Information provided by Georgia GulfGeorgia Gulf became Axiall Corporation in 2013.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.21 g/cc | 1.21 g/cc | ASTM D-792 |
| Linear Mold Shrinkage | 0.0030 - 0.0050 cm/cm | 0.0030 - 0.0050 in/in | ASTM D-955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 27.6 MPa | 4000 psi | ASTM D-638 |
| Tensile Modulus | 1.57 GPa | 227 ksi | ASTM D-638 |
| Flexural Strength | 40.0 MPa | 5800 psi | ASTM D-790 |
| Flexural Modulus | 1.52 GPa | 221 ksi | ASTM D-790 |
| Izod Impact, Notched | 5.87 J/cm @Thickness 3.17 mm, Temperature -40.0 °C |
11.0 ft-lb/in @Thickness 0.125 in, Temperature -40.0 °F |
ASTM D-256 |
| 8.01 J/cm @Thickness 3.17 mm, Temperature 22.8 °C |
15.0 ft-lb/in @Thickness 0.125 in, Temperature 73.0 °F |
ASTM D-256 | |
| Gardner Impact | 0.193 J | 0.142 ft-lb | per mil; ASTM D-4226 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 67.00 °C | 152.6 °F | unannealed; ASTM D-648 |
| 73.00 °C | 163.4 °F | annealed; ASTM D-648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 64.00 °C | 147.2 °F | unannealed; ASTM D-648 |
| 71.00 °C | 159.8 °F | annealed; ASTM D-648 | |
| Vicat Softening Point | 81.1 °C | 178 °F | annealed; ASTM D-1525A |
| UL RTI, Electrical | 50.0 °C | 122 °F | UL-746B |
| Flammability, UL94 | V-0 @Thickness 2.25 mm |
V-0 @Thickness 0.0886 in |
|
| 5VA @Thickness 2.25 mm |
5VA @Thickness 0.0886 in |
| Descriptive Properties | Value | Comments |
|---|---|---|
| UL Weatherability Rating | F(1)/F(2) | UL-746C |