Elektro-Isola G-Etronax PM GPO 3 Polyester, Glass Mat, Red, Sheets

Category Polymer , Thermoplastic , Polyester, TP
Manufacturer Elektro-Isola
Trade Name G-Etronax
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Elektro-Isola G-Etronax PM GPO 3 Polyester, Glass Mat, Red, Sheets.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Description: Good electrical properties such as high breakdown voltage in air and oil and highest arc resistance and tracking resistance. Self-extinguishing. Low smoke emission, halogen-free.Applications: Used as an insulation material in electrotechnical applications such as plate-enclosed distribution systems, partition plates, and busbar carriers.Information provided by Elektro-Isola
Physical Properties Metric English Comments
Density 1.80 g/cc
0.0650 lb/in³
24hr/23°C/50% RH; ISO 1183-A; IEC/EN 60893-2 8.1
Water Absorption 0.40 %
0.40 %
24hr/50°C+24hr in water at 23°C,Test Specimen 50x50x3[mm]; ISO 62-1; IEC/EN 60893-2 8.2
Mechanical Properties Metric English Comments
Tensile Strength 75.0 MPa

@Thickness >=1.50 mm
 10900 psi

@Thickness >=0.0591 in
 24hr/23°C/50% RH; ISO 527; IEC/EN 60893-2 5.6
Modulus of Elasticity 9.00 GPa

@Thickness >=1.50 mm
 1310 ksi

@Thickness >=0.0591 in
 24hr/23°C/50% RH; ISO 178; IEC/EN 60893-2 5.2
Flexural Strength 65.0 MPa

@Thickness >=1.50 mm
 9430 psi

@Thickness >=0.0591 in
 1hr/130°C/measured at 130°C; ISO 178; IEC/EN 60893-2 5.1
170 MPa

@Thickness >=1.50 mm
 24700 psi

@Thickness >=0.0591 in
 24hr/23°C/50% RH; ISO 178; IEC/EN 60893-2 5.1
60.0 MPa

@Treatment Temp. 200 °C,
Time 3600 sec
 8700 psi

@Treatment Temp. 392 °F,
Time 1.00 hour
 ISO 178; IEC/EN 60893-2 5.1
80.0 MPa

@Treatment Temp. 150 °C,
Time 3600 sec
 11600 psi

@Treatment Temp. 302 °F,
Time 1.00 hour
 ISO 178; IEC/EN 60893-2 5.1
130 MPa

@Treatment Temp. 100 °C,
Time 3600 sec
 18900 psi

@Treatment Temp. 212 °F,
Time 1.00 hour
 ISO 178; IEC/EN 60893-2 5.1
160 MPa

@Treatment Temp. 50.0 °C,
Time 3600 sec
 23200 psi

@Treatment Temp. 122 °F,
Time 1.00 hour
 ISO 178; IEC/EN 60893-2 5.1
170 MPa

@Treatment Temp. 20.0 °C,
Time 3600 sec
 24700 psi

@Treatment Temp. 68.0 °F,
Time 1.00 hour
 ISO 178; IEC/EN 60893-2 5.1
Compressive Strength 240 MPa

@Thickness >=5.00 mm
 34800 psi

@Thickness >=0.197 in
 24hr/23°C/50% RH; ISO 604; IEC/EN 60893-2 5.3
Shear Strength 35.0 MPa

@Thickness >=5.00 mm
 5080 psi

@Thickness >=0.197 in
 24hr/23°C/50% RH; IEC/EN 60893-2 5.5
Izod Impact, Notched (ISO) 40.0 kJ/m²

@Thickness >=5.00 mm
 19.0 ft-lb/in²

@Thickness >=0.197 in
 24hr/23°C/50% RH; ISO 180/2A; IEC/EN 60893-2 5.4.3
Thermal Properties Metric English Comments
Maximum Service Temperature, Inert 155 °C

@Thickness 0.000 mm,
Time 7.20e+7 sec
 311 °F

@Thickness 0.000 in,
Time 20000 hour
 IEC 60216; IEC/EN 60893-2 7.1
Flammability, UL94 V-0
V-0
IEC/EN 60893-2 7.2; IEC 60695-11-10
Electrical Properties Metric English Comments
Insulation Resistance 1.00e+9 ohm

@Thickness >=3.00 mm
 1.00e+9 ohm

@Thickness >=0.118 in
 24hr/50°C+24h in water at 23°C; IEC 60167; IEC/EN 60893-2 6.3
Dielectric Constant 4.5

@Thickness <=3.00 mm,
Frequency 50.0 Hz
 4.5

@Thickness <=0.118 in,
Frequency 50.0 Hz
 96hr/105°C+1hr/23°C/20%RH; IEC 60250; IEC/EN 60893-2 6.2
4.5

@Thickness <=3.00 mm,
Frequency 1.00e+6 Hz
 4.5

@Thickness <=0.118 in,
Frequency 1.00e+6 Hz
 96hr/105°C+1hr/23°C/20%RH; IEC 60250; IEC/EN 60893-2 6.2
Dielectric Strength 2.40 kV/mm

@Thickness >=3.00 mm
 61.0 kV/in

@Thickness >=0.118 in
 24hr/23°C/50% RH+1hr/oil 90°C; Parallel; IEC 60245-1; IEC/EN 60893-2 6.1.3.2
10.0 kV/mm

@Thickness 3.00 mm
 254 kV/in

@Thickness 0.118 in
 24hr/23°C/50% RH+1hr/oil 90°C; Perpendicular; IEC 60245-1; IEC/EN 60893-2 6.1.3.1
Dissipation Factor 0.040

@Frequency 50.0 Hz
 0.040

@Frequency 50.0 Hz
 96hr/105°C+1hr/23°C/20%RH; IEC 60250; IEC/EN 60893-2 6.2
0.040

@Frequency 1.00e+6 Hz
 0.040

@Frequency 1.00e+6 Hz
 96hr/105°C+1hr/23°C/20%RH; IEC 60250; IEC/EN 60893-2 6.2
Comparative Tracking Index 600 V

@Thickness 3.00 mm
 600 V

@Thickness 0.118 in
 IEC 60112; IEC/EN 60893-2 6.4