Victrex® PEEK 450GL30 30% Glass Fiber Reinforced

Category Polymer , Thermoplastic , Polyketone , Polyetheretherketone (PEEK) , Polyetheretherketone, PEEK, Glass Fiber Filled
Manufacturer Victrex
Trade Name PEEK
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Victrex® PEEK 450GL30 30% Glass Fiber Reinforced.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Product Description: High performance thermoplastic material, 30% glass fibre reinforced PolyEtherEtherKetone (PEEK), semi crystalline, granules for injection molding and extrusion, standard flow, FDA food contact compliant, color natural/beige.Typical Application Areas: Applications for higher strength in a static system. Low coefficient of thermal expansion. Chemically resistant to aggressive environments, suitable for sterilization for medical and food contact applications.Information provided by Victrex.
Physical Properties Metric English Comments
Density 1.51 g/cc
0.0546 lb/in³
Crystalline; ISO 1183
Water Absorption at Saturation 0.30 %

@Temperature 23.0 °C
0.30 %

@Temperature 73.4 °F
immersion; SO 62-1
0.45 %

@Temperature 100 °C
0.45 %

@Temperature 212 °F
immersion; SO 62-1
Viscosity 550000 cP

@Temperature 400 °C
550000 cP

@Temperature 752 °F
ISO 11443
Linear Mold Shrinkage 0.0030 cm/cm
0.0030 in/in
385°C nozzle, 190°C tool; ISO 294-4
Linear Mold Shrinkage, Transverse 0.0090 cm/cm
0.0090 in/in
385°C nozzle, 190°C tool; ISO 294-4
Spiral Flow 8.50 cm

@Thickness 1.00 mm
3.35 in

@Thickness 0.0394 in
385°C nozzle, 190°C tool
41.0 cm

@Thickness 3.00 mm
16.1 in

@Thickness 0.118 in
385°C nozzle, 190°C tool
Mechanical Properties Metric English Comments
Hardness, Shore D 87.5
87.5
ISO 868
Tensile Strength at Break 35.0 MPa

@Temperature 275 °C
5080 psi

@Temperature 527 °F
ISO 527
60.0 MPa

@Temperature 175 °C
8700 psi

@Temperature 347 °F
ISO 527
115 MPa

@Temperature 125 °C
16700 psi

@Temperature 257 °F
ISO 527
185 MPa

@Temperature 23.0 °C
26800 psi

@Temperature 73.4 °F
ISO 527
Elongation at Break 2.8 %
2.8 %
ISO 527
Tensile Modulus 11.5 GPa
1670 ksi
ISO 527
Flexural Strength 50.0 MPa

@Temperature 275 °C
7250 psi

@Temperature 527 °F
ISO 178
80.0 MPa

@Temperature 175 °C
11600 psi

@Temperature 347 °F
ISO 178
190 MPa

@Temperature 125 °C
27600 psi

@Temperature 257 °F
ISO 178
275 MPa

@Temperature 23.0 °C
39900 psi

@Temperature 73.4 °F
ISO 178
Flexural Modulus 11.0 GPa
1600 ksi
ISO 178
Compressive Strength 55.0 MPa

@Temperature 200 °C
7980 psi

@Temperature 392 °F
ISO 604
160 MPa

@Temperature 120 °C
23200 psi

@Temperature 248 °F
ISO 604
250 MPa

@Temperature 23.0 °C
36300 psi

@Temperature 73.4 °F
ISO 604
Izod Impact, Notched (ISO) 12.0 kJ/m²
5.71 ft-lb/in²
ISO 180/A
Izod Impact, Unnotched (ISO) 65.0 kJ/m²
30.9 ft-lb/in²
ISO 180/U
Charpy Impact Unnotched 5.50 J/cm²
26.2 ft-lb/in²
ISO 179/1U
Charpy Impact, Notched 0.800 J/cm²
3.81 ft-lb/in²
ISO 179/1eA
Thermal Properties Metric English Comments
CTE, linear 45.0 µm/m-°C

@Temperature <=143 °C
25.0 µin/in-°F

@Temperature <=289 °F
Average below Tg; ISO 11359
110 µm/m-°C

@Temperature >=143 °C
61.1 µin/in-°F

@Temperature >=289 °F
Average above Tg; ISO 11359
CTE, linear, Parallel to Flow 18.0 µm/m-°C

@Temperature <=143 °C
10.0 µin/in-°F

@Temperature <=289 °F
Below Tg; ISO 11359
18.0 µm/m-°C

@Temperature >=143 °C
10.0 µin/in-°F

@Temperature >=289 °F
Above Tg; ISO 11359
Thermal Conductivity 0.300 W/m-K
2.08 BTU-in/hr-ft²-°F
Average; ISO 22007-4
0.350 W/m-K
2.43 BTU-in/hr-ft²-°F
Along flow; ISO 22007-4
Melting Point 343 °C
649 °F
ISO 11357
Deflection Temperature at 1.8 MPa (264 psi) 328 °C
622 °F
ISO 75-f
Glass Transition Temp, Tg 143 °C
289 °F
Onset; ISO 11357
150 °C
302 °F
Midpoint; ISO 11357
UL RTI, Electrical 240 °C
464 °F
UL 746B
UL RTI, Mechanical with Impact 220 °C
428 °F
UL 746B
UL RTI, Mechanical without Impact 240 °C
464 °F
UL 746B
Glow Wire Test 960 °C

@Thickness 2.00 mm
1760 °F

@Thickness 0.0787 in
IEC 60695-2-12
Electrical Properties Metric English Comments
Electrical Resistivity 1.00e+16 ohm-cm
1.00e+16 ohm-cm
Dielectric Constant 3.2

@Frequency 1000 Hz
3.2

@Frequency 1000 Hz
3.7

@Frequency 1e+6 Hz
3.7

@Frequency 1e+6 Hz
Dissipation Factor 0.0010

@Frequency 1000 Hz
0.0010

@Frequency 1000 Hz
0.0040

@Frequency 1e+6 Hz
0.0040

@Frequency 1e+6 Hz
Processing Properties Metric English Comments
Processing Temperature <= 100 °C
<= 212 °F
Hopper Temperature
Nozzle Temperature 390 °C
734 °F
Mold Temperature 180 °C
356 °F
Dry Time 3.00 hour

@Temperature 150 °C
3.00 hour

@Temperature 302 °F
5.00 hour

@Temperature 120 °C
5.00 hour

@Temperature 248 °F