Victrex® PEEK 600G Polyetheretherketone  (discontinued **)

Category Polymer , Thermoplastic , Polyketone , Polyetheretherketone (PEEK) , Polyetheretherketone, PEEK, Unreinforced
Manufacturer
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Victrex® PEEK 600G Polyetheretherketone  (discontinued **).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Product Description: High performance thermoplastic material, unreinforced PolyEtherEtherKetone (PEEK), semi crystalline, granules for injection moulding and extrusion, low viscosity, FDA food contact compliantTypical Application Areas: Applications for higher strength and stiffness as well as high ductility. Chemically resistant to aggressive environments, suitable for sterilization for medical and food contact applications.Information provided by Victrex
Physical Properties Metric English Comments
Density 1.26 g/cc
0.0455 lb/in³
Amorphous; ISO 1183
1.30 g/cc
0.0470 lb/in³
Crystalline; ISO 1183
Water Absorption 0.40 %
0.40 %
by immersion; ISO 62-1
0.070 %

@Time 86400 sec
0.070 %

@Time 24.0 hour
3.2 mm thick Tensile bar; ISO 62-1
Viscosity 500000 cP

@Temperature 400 °C
500000 cP

@Temperature 752 °F
Melt; ISO 11443
Linear Mold Shrinkage, Flow 0.010 cm/cm
0.010 in/in
390°C nozzle, 200°C tool; ISO 294-4
Linear Mold Shrinkage, Transverse 0.013 cm/cm
0.013 in/in
390°C nozzle, 200°C tool; ISO 294-4
Spiral Flow 850 cm

@Thickness 1.00 mm
335 in

@Thickness 0.0394 in
390°C nozzle, 200°C tool; Victrex
Mechanical Properties Metric English Comments
Tensile Strength, Yield 95.0 MPa
13800 psi
ISO 527
Elongation at Break 45 %
45 %
ISO 527
Tensile Modulus 3.70 GPa
537 ksi
ISO 527
Flexural Strength 12.0 MPa

@Temperature 275 °C
1740 psi

@Temperature 527 °F
Result based on 450G; ISO 178
17.0 MPa

@Temperature 175 °C
2470 psi

@Temperature 347 °F
Result based on 450G; ISO 178
80.0 MPa

@Temperature 125 °C
11600 psi

@Temperature 257 °F
Result based on 450G; ISO 178
155 MPa

@Temperature 23.0 °C
22500 psi

@Temperature 73.4 °F
ISO 178
Flexural Modulus 4.10 GPa
595 ksi
ISO 178
Compressive Strength 70.0 MPa

@Temperature 120 °C
10200 psi

@Temperature 248 °F
Result based on 450G; ISO 604
120 MPa

@Temperature 23.0 °C
17400 psi

@Temperature 73.4 °F
Result based on 450G; ISO 604
Izod Impact, Notched (ISO) 9.50 kJ/m²
4.52 ft-lb/in²
ISO 180/A
Izod Impact, Unnotched (ISO) NB
NB
ISO 180/U
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 35.0 µm/m-°C
19.4 µin/in-°F
Below Tg, Result based on 450G; ISO 11359
150 µm/m-°C
83.3 µin/in-°F
Above Tg, Result based on 450G; ISO 11359
CTE, linear, Transverse to Flow 55.0 µm/m-°C
30.6 µin/in-°F
Average below Tg, Result based on 450G; ISO 11359
140 µm/m-°C
77.8 µin/in-°F
Average above Tg, Result based on 450G; ISO 11359
Specific Heat Capacity 2.20 J/g-°C
0.526 BTU/lb-°F
DSC
Thermal Conductivity 0.290 W/m-K
2.01 BTU-in/hr-ft²-°F
ISO/CD 22007-4
Melting Point 343 °C
649 °F
ISO 11357
Deflection Temperature at 1.8 MPa (264 psi) 152 °C
306 °F
Result based on 450G; ISO 75-f
Glass Transition Temp, Tg 143 °C
289 °F
Onset; ISO 11357
Electrical Properties Metric English Comments
Volume Resistivity 1.00e+9 ohm-cm

@Temperature 275 °C
1.00e+9 ohm-cm

@Temperature 527 °F
Result based on 450G
1.00e+15 ohm-cm

@Temperature 125 °C
1.00e+15 ohm-cm

@Temperature 257 °F
Result based on 450G
1.00e+16 ohm-cm

@Temperature 23.0 °C
1.00e+16 ohm-cm

@Temperature 73.4 °F
Result based on 450G
Dielectric Constant 3.2

@Frequency 50000 Hz,
Temperature 23.0 °C
3.2

@Frequency 50000 Hz,
Temperature 73.4 °F
Result based on 450G
4.5

@Frequency 50000 Hz,
Temperature 200 °C
4.5

@Frequency 50000 Hz,
Temperature 392 °F
Result based on 450G
Dielectric Strength 16.0 kV/mm

@Thickness 2.50 mm
406 kV/in

@Thickness 0.0984 in
Result based on 450G; IEC 60243-1
Dissipation Factor 0.0030

@Frequency 1.00e+6 Hz
0.0030

@Frequency 1.00e+6 Hz
Result based on 450G; IEC 60250
Comparative Tracking Index 150 V
150 V
Result based on 450G; IEC 60112
Processing Properties Metric English Comments
Processing Temperature <= 100 °C
<= 212 °F
Hopper Temperature
Nozzle Temperature 390 °C
734 °F
Zone 1 370 °C
698 °F
Zone 2 375 °C
707 °F
Zone 3 380 °C
716 °F
Zone 4 385 °C
725 °F
Mold Temperature 190 - 220 °C
374 - 428 °F
<= 250 °C
<= 482 °F
Dry Time 3 hour

@Temperature 150 °C
3 hour

@Temperature 302 °F
5 hour

@Temperature 120 °C
5 hour

@Temperature 248 °F
Descriptive Properties Value Comments
Color Natural/Beige
Gate > 1mm or 0.5 x part thickness
Runner Die/nozzle > 3mm, manifold > 3.5mm