- Polymer Property : Flexural Modulus = 957 ksi
Polymer Property : Flexural Modulus = 957 ksi Product List
Mechanical PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Flexural Modulus | 6.60 GPa | 957 ksi | ASTM D790 |
| Nylene® PA6/6 Mineral Filled 6140 HS Nylon 6/6 40% Mineral Filler; Property data for dry as molded samples.ALM, Nylene Canada, and Custom Resins are all operting companies of Polymeric Resources Corporation. |
|||
| Flexural Modulus | 6.60 GPa | 957 ksi | ISO 178 |
| PolyOne Bergadur™ PB400 G15 H UF UV Polybutylene Terephthalate (PBT) Information provided by PolyOne |
|||
| Flexural Modulus | 6.60 - 26.0 GPa | 957 - 3770 ksi | Average value: 13.7 GPa Grade Count:52 |
| Overview of materials for Liquid Crystal Polymer (LCP), 30% Glass Fiber Filled This property data is a summary of similar materials in the MatWeb database for the category "Liquid Crystal Polymer (LCP), 30% Glass Fiber Filled". Specific grades with glass content between 25% an.. |
|||
| Flexural Modulus | 6.60 - 8.60 GPa | 957 - 1250 ksi | Average value: 7.50 GPa Grade Count:10 |
| Overview of materials for Phenolic, Resole, Wood Filled This property data is a summary of similar materials in the MatWeb database for the category "Phenolic, Resole, Wood Filled". Each property range of values reported is minimum and maximum values of .. |
|||
| Flexural Modulus | 6.60 GPa | 957 ksi | ASTM D790 |
| Kolon KOCETAL® CF702 Conductive Grade Acetal Resin Carbon fiber added, high stiffness and conductive grade. Applications: Conductive products. Information provided by API-Kolon. |
|||
| Flexural Modulus | 6.60 GPa | 957 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
| SABIC Innovative Plastics NORYL ZX09022 PPE+PP (Europe-Africa-Middle East) Thermocomp ZX09022 Polyphenylene Oxide (PPO*) + Polypropylene (PP) resin is a 30 % Glass Reinforced, injection moldable grade with a HDT /1.8MPa temperature resistance of 153 deg C and a Tensile mod.. |
|||
| Flexural Modulus | 6.60 GPa @Temperature 100 °C |
957 ksi @Temperature 212 °F |
ISO 178 |
| Solvay Specialty Polymers Amodel® A-6135 HN Polyphthalamide (PPA), 35% Glass Fiber (Dry) Amodel® A-6135 HN polyphthalamide (PPA) is a 35% glass reinforced resin that is heat stabilized, lubricated and hot-water moldable. Key properties of the resin are high heat resistance, high stre.. |
|||
| Flexural Modulus | 6.60 GPa | 957 ksi | ASTM D790 |
| Sumitomo Bakelite North America EM 7400-2 Long Glass Fiber Reinforced Epoxy EM 7400-2 is a polyaramide fiber reinforced epoxy molding compound, which features abrasion resistance and light weight.Information provided by Sumitomo Bakelite North America, Inc. |
|||
| Flexural Modulus | 6.60 GPa | 957 ksi | 2 mm/min; ISO 178 |
| SABIC Innovative Plastics NORYL GTX GTX8720 PPE+PA Noryl GTX* GTX8720 resin is a glass filled, high performance blend of PPE/PA that exhibits an excellent balance of high-heat resistance, strength, flow, and conductivity. This grade can be electro-.. |
|||
| Flexural Modulus | 6.60 GPa | 957 ksi | 2 mm/min; ISO 178 |
| SABIC Innovative Plastics NORYL GTX GTX8720 PPE+PA (Asia Pacific) Noryl GTX* GTX8720 resin is a glass filled, high performance blend of PPE/PA that exhibits an excellent balance of high-heat resistance, strength, flow, and conductivity. This grade can be electro-.. |
|||
| Flexural Modulus | 6.60 GPa | 957 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
| SABIC Innovative Plastics NORYL PPX PPX830 PPE+PP Noryl* PPX830 Polyphenylene Oxide (PPO*) + Polypropylene (PP) resin is a 30 % Glass Reinforced, injection moldable grade with a HDT /1.8MPa temperature resistance of 153 deg C and a Tensile modulus .. |
|||
| Flexural Modulus | 6.60 GPa | 957 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
| SABIC Innovative Plastics NORYL PPX PPX830 PPE+PP (Asia Pacific) Noryl* PPX830 Polyphenylene Oxide (PPO*) + Polypropylene (PP) resin is a 30 % Glass Reinforced, injection moldable grade with a HDT /1.8MPa temperature resistance of 153 deg C and a Tensile modulus .. |
|||
| Flexural Modulus | 6.60 GPa | 957 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
| SABIC Innovative Plastics NORYL PPX PPX830 PPE+PP (Europe-Africa-Middle East) Noryl* PPX830 Polyphenylene Oxide (PPO*) + Polypropylene (PP) resin is a 30 % Glass Reinforced, injection moldable grade with a HDT /1.8MPa temperature resistance of 153 deg C and a Tensile modulus .. |
|||
| Flexural Modulus | 6.60 GPa | 957 ksi | 2mm/min; ISO 178 |
| Borealis GD310U Polypropylene Compound, Glass Fiber Reinforced GD310U is a 30% chemically coupled glass fiber reinforced polypropylene compound intended for injection molding. This material shows excellent mechanical properties also at elevated temperatures. .. |
|||
| Flexural Modulus | 6.60 GPa | 957 ksi | ASTM D790 |
| Plenco 2369 Phenolic, Granular, Injection Molded PLENCO 02369 is a general purpose, organic filled phenolic molding compound, formulated to minimize the generation of free ammonia for applications that are sensitive to such formation. PLENCO 02369.. |
|||
| Flexural Modulus | 6.60 GPa | 957 ksi | ASTM D790 |
| Tipco Tipcofil® AGM 602 - 10% Mineral & 20% Glass Fiber Reinforced Nylon-6 Compound, with High Heat Stability 10% Mineral + 20% Glass Reinforced Nylon-6 CompoundApplications: General PurposeProcessing: Injection MoldingInformation provided by the Manufacturer, Tipco Industries Ltd.,
India. |
|||
| Flexural Modulus | 6.60 GPa @Thickness 3.17 mm |
957 ksi @Thickness 0.125 in |
ASTM D790 |
| Polyram PlusTek RA353M8 Nylon 66, 40% Mineral Filled Information provided by Polymer Technology and Services, LLC (PTS). |
|||
| Flexural Modulus | 6.60 GPa | 957 ksi | cond; ISO 178 |
| DSM Novamid® 1015G35 NAT PA6-GF35 35% Glass Reinforced, Injection Molding |
|||
| Flexural Modulus | 6.60 GPa | 957 ksi | cond; ISO 178 |
| DSM Novamid® 1015GH35 BK37 PA6-GF35 35% Glass Reinforced, Heat Stabilized, Injection Molding |
|||
| Flexural Modulus | 6.60 GPa | 957 ksi | 2 mm/min; ISO 178 |
| Eurostar Staramide RF005Z PA66, 25% Glass Fiber, Injection Molded Starflam RF005Z is a 25% Glass Reinforced Polyamide 66 Injection Molding Resin (also known as Staramide RF1005E-BK82205)Information provided by Eurostar. |
|||
| Flexural Modulus | 6.60 GPa | 957 ksi | 2 mm/min; ISO 178 |
| Eurostar Starflam AF430B1 PA66, Glass Fiber Reinforced, Flame Retardant, Injection Molding Starflam AFR430B1 is a Flame Retardant, Glass Fiber Reinforced Polyamide 66, Injection Molding ResinInformation provided by Eurostar. |
|||
| Flexural Modulus | 6.60 GPa | 957 ksi | ASTM D790 |
| Ashley Polymers Ashlene® 990L-30G Nylon 610, 30% Glass Reinforced 30% glass reinforced for excellent dimensional stability and low water absorption.Data provided by the manufacturer |
|||
| Flexural Modulus | 6.60 GPa | 957 ksi | ASTM D790 |
| Chem Polymer Chemlon 140 M Nylon 66, 40% Mineral Reinforced A 40% mineral reinforced nylon 66 exhibiting excellent stiffness in parts where control of warpage is essential.Data provided by the manufacturer, Chem Polymer. |
|||
| Flexural Modulus | 6.60 GPa | 957 ksi | ASTM D790 |
| Adell AJ-17 Nylon 66, 35% Glass Reinforced; High Impact Data provided by Adell Plastics, Inc. |
|||
| Flexural Modulus | 6.60 GPa @Temperature 80.0 °C |
957 ksi @Temperature 176 °F |
ISO 178 |
| Celanese Celstran® PP-GF30-0405 P10/10 PP, 30% Glass Reinforced Material code according to ISO 1043-1: PPInformation provided by Celanese |
|||
| Flexural Modulus | 6.60 GPa @Temperature 80.0 °C |
957 ksi @Temperature 176 °F |
ISO 178 |
| Celanese Celstran® PP-GF30-0455 P10/16 PP, 30% Glass Reinforced Material code according to ISO 1043-1: PPInformation provided by Celanese |
|||
| Flexural Modulus | 6.60 GPa | 957 ksi | ASTM D790 |
| Ashley Polymers Ashlene® 520-25G Nylon 66, 25% Glass Reinforced Nylon 66, 25% glass reinforced.Data provided by the manufacturer |
|||
| Flexural Modulus | 6.60 GPa | 957 ksi | 2 mm/min, 64mm span; ISO 178 |
| SABIC Innovative Plastics SABIC PPCOMPOUND G3230A PP SABIC® PPcompound G3230A is a general purpose, 30% glass filled, chemically coupled, heat stabilized homopolymer polypropylene compound. The IMDS ID is 109612410 |
|||
| Flexural Modulus | 6.60 - 35.0 GPa | 957 - 5080 ksi | Average value: 18.0 GPa Grade Count:54 |
| Overview of materials for Epoxy, Molded, Glass Fiber Filler This property data is a summary of similar materials in the MatWeb database for the category "Epoxy, Molded, Glass Fiber Filler". Each property range of values reported is minimum and maximum values.. |
|||
| Flexural Modulus | 6.60 GPa | 957 ksi | ASTM D790 |
| PolyOne Lubri-Tech™ MP-15MCF/15T-2S Modified PPO - 15% Milled Carbon Fiber - 15% PTFE - 2% Silicone
(disconti Data provided by PolyOne. |
|||