Category Polymer , Thermoplastic , Nylon , Polyphenylene Ether/PPO
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name NORYL GTX
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics NORYL GTX GTX8720 PPE+PA.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Noryl GTX* GTX8720 resin is a glass filled, high performance blend of PPE/PA that exhibits an excellent balance of high-heat resistance, strength, flow, and conductivity. This grade can be electro-statically painted or powder coated without the need for a conductive primer.
Physical Properties Metric English Comments
Specific Gravity 1.26 g/cc
1.26 g/cc
ASTM D792
Density 1.26 g/cc
0.0455 lb/in³
ISO 1183
Moisture Absorption 0.500 %
0.500 %
23°C / 50% RH; ISO 62
Water Absorption at Saturation 4.0 %
4.0 %
ISO 62
Linear Mold Shrinkage, Flow 0.0026 - 0.0030 cm/cm

@Thickness 3.20 mm
0.0026 - 0.0030 in/in

@Thickness 0.126 in
SABIC Method
Linear Mold Shrinkage, Transverse 0.0072 - 0.0085 cm/cm

@Thickness 3.20 mm
0.0072 - 0.0085 in/in

@Thickness 0.126 in
SABIC Method
Melt Flow 8.6 g/10 min

@Load 5.00 kg,
Temperature 280 °C
8.6 g/10 min

@Load 11.0 lb,
Temperature 536 °F
ASTM D1238
Melt Index of Compound 7.0 g/10 min

@Load 5.00 kg,
Temperature 280 °C
7.0 g/10 min

@Load 11.0 lb,
Temperature 536 °F
MVR [cm^3/10 min]; ISO 1133
Mechanical Properties Metric English Comments
Tensile Strength at Break 140 MPa
20300 psi
Type I, 5 mm/min; ASTM D638
140 MPa
20300 psi
5 mm/min; ISO 527
Tensile Strength, Yield 140 MPa
20300 psi
Type I, 5 mm/min; ASTM D638
140 MPa
20300 psi
5 mm/min; ISO 527
Elongation at Break 4.0 %
4.0 %
Type I, 5 mm/min; ASTM D638
4.0 %
4.0 %
5 mm/min; ISO 527
Elongation at Yield 3.1 %
3.1 %
Type I, 5 mm/min; ASTM D638
3.1 %
3.1 %
5 mm/min; ISO 527
Tensile Modulus 7.00 GPa
1020 ksi
5 mm/min; ASTM D638
7.00 GPa
1020 ksi
1 mm/min; ISO 527
Flexural Yield Strength 200 MPa
29000 psi
1.3 mm/min, 50 mm span; ASTM D790
200 MPa
29000 psi
2 mm/min; ISO 178
Flexural Modulus 6.60 GPa
957 ksi
1.3 mm/min, 50 mm span; ASTM D790
6.60 GPa
957 ksi
2 mm/min; ISO 178
Izod Impact, Notched 0.850 J/cm
1.59 ft-lb/in
ASTM D256
0.600 J/cm

@Temperature -30.0 °C
1.12 ft-lb/in

@Temperature -22.0 °F
ASTM D256
Izod Impact, Notched (ISO) 10.0 kJ/m²
4.76 ft-lb/in²
80*10*4; ISO 180/1A
8.00 kJ/m²

@Temperature -30.0 °C
3.81 ft-lb/in²

@Temperature -22.0 °F
80*10*4; ISO 180/1A
Charpy Impact, Notched 1.10 J/cm²
5.23 ft-lb/in²
Edgew 80*10*4 sp=62mm; ISO 179/1eA
Dart Drop, Total Energy 17.0 J

@Temperature 23.0 °C
12.5 ft-lb

@Temperature 73.4 °F
ASTM D3763
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 23.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
12.8 µin/in-°F

@Temperature -40.0 - 104 °F
ASTM E 831
23.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
12.8 µin/in-°F

@Temperature -40.0 - 104 °F
ISO 11359-2
CTE, linear, Transverse to Flow 80.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
44.4 µin/in-°F

@Temperature -40.0 - 104 °F
ASTM E 831
80.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
44.4 µin/in-°F

@Temperature -40.0 - 104 °F
ISO 11359-2
Deflection Temperature at 0.46 MPa (66 psi) 215 °C
419 °F
Flatw 80*10*4 sp=64mm; ISO 75/Bf
215 °C

@Thickness 3.20 mm
419 °F

@Thickness 0.126 in
unannealed; ASTM D648
Vicat Softening Point 215 °C
419 °F
Rate B/50; ASTM D1525
215 °C
419 °F
Rate B/50; ISO 306
225 °C
437 °F
Rate B/120; ISO 306
Electrical Properties Metric English Comments
Volume Resistivity 1000 - 10000 ohm-cm
1000 - 10000 ohm-cm
SABIC Method