Polymer Property : Flexural Modulus = 6.60 GPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.
Mechanical Properties Metric English Comments
Flexural Modulus 6.60 - 26.0 GPa
957 - 3770 ksi
Average value: 13.7 GPa Grade Count:52
Overview of materials for Liquid Crystal Polymer (LCP), 30% Glass Fiber Filled
This property data is a summary of similar materials in the MatWeb database for the category "Liquid Crystal Polymer (LCP), 30% Glass Fiber Filled". Specific grades with glass content between 25% an..
Flexural Modulus 6.60 - 20.0 GPa
957 - 2900 ksi
Average value: 11.5 GPa Grade Count:24
Overview of materials for Liquid Crystal Polymer (LCP), Mineral Filled
This property data is a summary of similar materials in the MatWeb database for the category "Liquid Crystal Polymer (LCP), Mineral Filled". Each property range of values reported is minimum and max..
Flexural Modulus 6.60 GPa
957 ksi
DIN 53 457
Albis Plastics Tedur® L V 9112-2 PPS, 20% Glass Fiber  (discontinued **)
Excellent Surface Finish (Additional Annealing May Be Necessary). Incandescent wire resistance (2 mm) is 960°C per VDE 0471 T1.2.Applications: Pipes, ProfilesProcessing: Extrusion (Melt Temperatur..
Flexural Modulus 6.60 GPa
957 ksi
ASTM D790
Kolon KOCETAL® CF702 Conductive Grade Acetal Resin
Carbon fiber added, high stiffness and conductive grade. Applications: Conductive products. Information provided by API-Kolon.
Flexural Modulus 6.60 GPa
957 ksi
1.3 mm/min, 50 mm span; ASTM D 790
SABIC Innovative Plastics LNP Lubricomp GFL14 PSU
LNP* Lubricomp* GFL14 is a compound based on Polysulfone containing Glass Fiber and PTFE Lubricant.This data was supplied by SABIC-IP for the Americas region.
Flexural Modulus 6.60 GPa

@Temperature 100 °C
957 ksi

@Temperature 212 °F
ISO 178
Solvay Specialty Polymers Amodel® A-6135 HN Polyphthalamide (PPA), 35% Glass Fiber (Dry)
Amodel® A-6135 HN polyphthalamide (PPA) is a 35% glass reinforced resin that is heat stabilized, lubricated and hot-water moldable. Key properties of the resin are high heat resistance, high stre..
Flexural Modulus 6.60 GPa
957 ksi
2mm/min; ISO 178
Teijin Panlite® G-3430H Low Anisotropy, Glass Fiber Reinforced Polycarbonate Resin
Reinforced with 30 % of special GF and improved appearance grade, meeting UL 94 V-2.Applications:Mechanical, electric and electronic components that need good appearance and mechanical propertyPreci..
Flexural Modulus 6.60 GPa
957 ksi
ISO 178
SABIC Innovative Plastics LNP THERMOCOMP ZF0049 PPE+PS (Asia Pacific)
LNP* Thermocomp* ZF0049 is a compound based on PPE+PS Blend resin containing Flame Retardant. Added features of this material include: Flame Retardant.
Flexural Modulus 6.60 GPa
957 ksi
ASTM D790
Sumitomo Bakelite North America EM 7400-2 Long Glass Fiber Reinforced Epoxy
EM 7400-2 is a polyaramide fiber reinforced epoxy molding compound, which features abrasion resistance and light weight.Information provided by Sumitomo Bakelite North America, Inc.
Flexural Modulus 6.60 GPa
957 ksi
2 mm/min; ISO 178
SABIC Innovative Plastics NORYL GTX GTX8720 PPE+PA (Asia Pacific)
Noryl GTX* GTX8720 resin is a glass filled, high performance blend of PPE/PA that exhibits an excellent balance of high-heat resistance, strength, flow, and conductivity. This grade can be electro-..
Flexural Modulus 6.60 GPa
957 ksi
2 mm/min; ISO 178
SABIC Innovative Plastics NORYL GTX GTX8720 PPE+PA (Europe-Africa-Middle East)
Noryl GTX* GTX8720 resin is a glass filled, high performance blend of PPE/PA that exhibits an excellent balance of high-heat resistance, strength, flow, and conductivity. This grade can be electro-..
Flexural Modulus 6.60 GPa
957 ksi
1.3 mm/min, 50 mm span; ASTM D790
SABIC Innovative Plastics NORYL PPX ZX09022 PPE+PP (Europe-Africa-Middle East)
Thermocomp ZX09022 Polyphenylene Oxide (PPO*) + Polypropylene (PP) resin is a 30 % Glass Reinforced, injection moldable grade with a HDT /1.8MPa temperature resistance of 153 deg C and a Tensile mod..
Flexural Modulus 6.60 GPa
957 ksi
ASTM D790
Plenco 2369 Phenolic, Granular, Injection Molded
PLENCO 02369 is a general purpose, organic filled phenolic molding compound, formulated to minimize the generation of free ammonia for applications that are sensitive to such formation. PLENCO 02369..
Flexural Modulus 6.60 GPa
957 ksi
ISO 178
Polyram PlusTek PA351M8 Nylon 6.6 for Injection Molding, 40% Mineral Reinforced
40% Minerals Reinforced Nylon 6.6 for injection molding applications.Information provided by Polyram.
Flexural Modulus 6.60 GPa
957 ksi
ASTM D790
Tipco Tipcofil® AGM 602 - 10% Mineral & 20% Glass Fiber Reinforced Nylon-6 Compound, with High Heat Stability
10% Mineral + 20% Glass Reinforced Nylon-6 CompoundApplications: General PurposeProcessing: Injection MoldingInformation provided by the Manufacturer, Tipco Industries Ltd., India.
Flexural Modulus 6.60 GPa

@Thickness 3.17 mm
957 ksi

@Thickness 0.125 in
ASTM D790
Polyram PlusTek RA353M8 Nylon 66, 40% Mineral Filled
Information provided by Polymer Technology and Services, LLC (PTS).
Flexural Modulus 6.60 GPa
957 ksi
2 mm/min; ISO 178
Eurostar Staramide RF005Z PA66, 25% Glass Fiber, Injection Molded
Starflam RF005Z is a 25% Glass Reinforced Polyamide 66 Injection Molding Resin (also known as Staramide RF1005E-BK82205)Information provided by Eurostar.
Flexural Modulus 6.60 GPa
957 ksi
2 mm/min; ISO 178
Eurostar Starflam AF430B1 PA66, Glass Fiber Reinforced, Flame Retardant, Injection Molding
Starflam AFR430B1 is a Flame Retardant, Glass Fiber Reinforced Polyamide 66, Injection Molding ResinInformation provided by Eurostar.
Flexural Modulus 6.60 GPa
957 ksi
ASTM D790
Adell BT-37 Nylon 6, 35% Glass Reinforced; Impact Modified
Data provided by Adell Plastics, Inc.
Flexural Modulus 6.60 GPa
957 ksi
ISO 178
Celanese Celstran® +PP-GF30-04CN02/10 PP, 30% Glass Reinforced
Material code according to ISO 1043-1: PPInformation provided by Celanese
Flexural Modulus 6.60 GPa
957 ksi
ASTM D790
Ashley Polymers Ashlene® 525-33G Nylon 66, 33% Glass Reinforced
High impact Nylon 66 reinforced with 33% glass fibers, lubricated.Data provided by the manufacturer
Flexural Modulus 6.60 GPa
957 ksi
ASTM D790
Ashley Polymers Ashlene® 990L-30G Nylon 610, 30% Glass Reinforced
30% glass reinforced for excellent dimensional stability and low water absorption.Data provided by the manufacturer
Flexural Modulus 6.60 GPa
957 ksi
ASTM D790
Adell BT-17 Nylon 6, 35% Glass Reinforced; Impact Modified
Data provided by Adell Plastics, Inc.
Flexural Modulus 6.60 GPa

@Temperature 80.0 °C
957 ksi

@Temperature 176 °F
ISO 178
Celanese Celstran® PP-GF30-0405 P10/10 PP, 30% Glass Reinforced
Material code according to ISO 1043-1: PPInformation provided by Celanese
Flexural Modulus 6.60 GPa

@Temperature 80.0 °C
957 ksi

@Temperature 176 °F
ISO 178
Celanese Celstran® PP-GF30-0455 P10/16 PP, 30% Glass Reinforced
Material code according to ISO 1043-1: PPInformation provided by Celanese
Flexural Modulus 6.60 GPa
957 ksi
ASTM D790
Ashley Polymers Ashlene® 61M Nylon 66, 40% Mineral reinforced
A 40% mineral reinforced general purpose Nylon 66 resin with superior stiffness and dimensional stability.Data provided by the manufacturer
Flexural Modulus 6.60 GPa

@Temperature 100 °C
957 ksi

@Temperature 212 °F
ISO 178
Solvay Specialty Polymers Amodel® A-6135 HN Polyphthalamide (PPA)  (Unverified Data**)
Amodel A-6135 HN polyphthalamide (PPA) is a 35% glass reinforced resin that is heat stabilized, lubricated and hot-water moldable. Key properties of the resin are high heat resistance, high strength..
Flexural Modulus 6.60 GPa
957 ksi
2 mm/min, 64mm span; ISO 178
SABIC Innovative Plastics SABIC PPCOMPOUND G3230A PP
SABIC® PPcompound G3230A is a general purpose, 30% glass filled, chemically coupled, heat stabilized homopolymer polypropylene compound. The IMDS ID is 109612410
Flexural Modulus 6.60 - 35.0 GPa
957 - 5080 ksi
Average value: 18.0 GPa Grade Count:54
Overview of materials for Epoxy, Molded, Glass Fiber Filler
This property data is a summary of similar materials in the MatWeb database for the category "Epoxy, Molded, Glass Fiber Filler". Each property range of values reported is minimum and maximum values..
Flexural Modulus 6.60 GPa
957 ksi
ASTM D790
PolyOne Lubri-Tech™ MP-15MCF/15T-2S Modified PPO - 15% Milled Carbon Fiber - 15% PTFE - 2% Silicone  (disconti
Data provided by PolyOne.