PolyOne Lubri-Tech™ MP-15MCF/15T-2S Modified PPO - 15% Milled Carbon Fiber - 15% PTFE - 2% Silicone (disconti
| Category | Polymer , Thermoplastic , Polyphenylene Ether/PPO |
| Manufacturer | |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | PolyOne Lubri-Tech™ MP-15MCF/15T-2S Modified PPO - 15% Milled Carbon Fiber - 15% PTFE - 2% Silicone
(disconti.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Data provided by PolyOne.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.23 g/cc | 0.0444 lb/in³ | ASTM D792 |
| Water Absorption | 0.20 % | 0.20 % | 24 hrs. ASTM D570 |
| Linear Mold Shrinkage | 0.0020 - 0.0025 cm/cm @Thickness 3.17 mm |
0.0020 - 0.0025 in/in @Thickness 0.125 in |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Ultimate | 59.0 MPa | 8560 psi | ASTM D638 |
| Elongation at Break | 1.0 - 3.0 % | 1.0 - 3.0 % | ASTM D638 |
| Tensile Modulus | 6.60 GPa | 957 ksi | ASTM D638 |
| Flexural Yield Strength | 83.0 MPa | 12000 psi | ASTM D790 |
| Flexural Modulus | 6.60 GPa | 957 ksi | ASTM D790 |
| Izod Impact, Notched | 0.480 - 0.750 J/cm @Thickness 6.35 mm |
0.899 - 1.41 ft-lb/in @Thickness 0.250 in |
ASTM D256 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Electrical Resistivity | 1000 - 1.00e+7 ohm-cm | 1000 - 1.00e+7 ohm-cm | ASTM D257 |
| Surface Resistance | 1000 - 1.00e+7 ohm | 1000 - 1.00e+7 ohm | ASTM D257 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 271 - 304 °C | 520 - 579 °F | Stock |
| Mold Temperature | 121 °C | 250 °F | |
| Drying Temperature | 121 °C | 250 °F |
Users viewing this material also viewed the following:
- Pinnacle Polymers 2135 Impact Polypropylene Copolymer, Injection Molding Grade
- TSE Industries Millathane® E34 Millable Polyether Polyurethane Rubber with 40 PHR Talc-Mistron Vapor
- Eastman Tenite 371A-10 Cellulose Acetate Propionate (discontinued **)
- Lord Adhesives Thermosetâ„¢ MD-150 Conductive Adhesive
- Solvay Specialty Polymers Amodel® A-8950 HS Polyphthalamide (PPA), 50% Glass Fiber
- A. Schulman POLYFLAM™ RPP 1360 Non-Halogenated Homopolymer Polypropylene
- Hexcel® HexWeb® HRH-10 - 3/8 - 1.5 Aramid Fiber/Phenolic Resin Honeycomb
- ChevronTexaco ISO 320 Ultra Gear Lubricant
- Asahi Kasei Leona® 1402G 33% Glass Filled Nylon 66
- AorTech Biomaterials Elast-Eon™ E2-862 Biomedical Polyurethane Pellets
Copyright © lookpolymers.com All Rights Reserved