Polyram PlusTek RA300G4 Nylon 6.6, 20% Glass Fiber
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, 20% Glass Fiber Filled |
| Manufacturer | Polyram |
| Trade Name | PlusTek |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Polyram PlusTek RA300G4 Nylon 6.6, 20% Glass Fiber.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
20% glass fiber reinforced polyamide 6.6 for injection molding applicationsInformation provided by Polyram Ram On Ind.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.27 g/cc | 0.0459 lb/in³ | DIN 53479 |
| Water Absorption | 0.85 % | 0.85 % | DIN 53495 |
| Linear Mold Shrinkage | 0.0040 - 0.0050 cm/cm | 0.0040 - 0.0050 in/in |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | >= 110 MPa | >= 16000 psi | ASTM-D638 |
| Elongation at Break | 3.0 % | 3.0 % | ASTM-D638 |
| Flexural Strength | >= 160 MPa | >= 23200 psi | ASTM D790 |
| Flexural Modulus | >= 5.00 GPa | >= 725 ksi | ASTM-D790 |
| Izod Impact, Notched | >= 0.400 J/cm @Temperature 23.0 °C |
>= 0.749 ft-lb/in @Temperature 73.4 °F |
ASTM-D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 256 °C | 493 °F | |
| Deflection Temperature at 0.46 MPa (66 psi) | >= 240 °C | >= 464 °F | DIN 53461 |
| Deflection Temperature at 1.8 MPa (264 psi) | >= 210 °C | >= 410 °F | DIN 53461 |
| Flammability, UL94 | HB @Thickness 3.00 mm |
HB @Thickness 0.118 in |