SABIC Innovative Plastics SABIC STAMAX 30YK270 PP
| Category | Polymer , Thermoplastic , Polypropylene (PP) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | SABIC STAMAX |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics SABIC STAMAX 30YK270 PP.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
SABIC® STAMAX 30YK270 is a 30% long glass fiber reinforced polypropylene with improved impact and flow properties. The glass fibers are chemically coupled to the PP matrix, resulting in high stiffness and strength. The IMDS is 80929807.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.13 g/cc | 1.13 g/cc | ASTM D792 |
| Density | 1.12 g/cc | 0.0405 lb/in³ | ISO 1183 |
| Filler Content | 30 % | 30 % | glass; ISO 3451 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 98.0 MPa | 14200 psi | 50 mm/min, 1A; ISO 527 |
| 43.0 MPa @Temperature 120 °C |
6240 psi @Temperature 248 °F |
50 mm/min, 1A; ISO 527 | |
| 60.0 MPa @Temperature 80.0 °C |
8700 psi @Temperature 176 °F |
50 mm/min, 1A; ISO 527 | |
| Elongation at Break | 2.3 % | 2.3 % | 50 mm/min; ISO 527 |
| Tensile Modulus | 6.20 GPa | 899 ksi | 1 mm/min; ISO 527 |
| 3.60 GPa @Temperature 120 °C |
522 ksi @Temperature 248 °F |
1 mm/min; ISO 527 | |
| 4.40 GPa @Temperature 80.0 °C |
638 ksi @Temperature 176 °F |
1 mm/min; ISO 527 | |
| Flexural Modulus | 5.50 GPa | 798 ksi | 2 mm/min, 64mm span; ISO 178 |
| 3.60 GPa @Temperature 80.0 °C |
522 ksi @Temperature 176 °F |
2 mm/min, 64mm span; ISO 178 | |
| Charpy Impact, Notched | 2.10 J/cm² | 9.99 ft-lb/in² | 80*10*4mm, Cut; ISO 179/1eA |
| 2.40 J/cm² @Temperature -30.0 °C |
11.4 ft-lb/in² @Temperature -22.0 °F |
80*10*4mm, Cut; ISO 179/1eA | |
| Dart Drop, Total Energy | 5.00 J @Temperature 23.0 °C |
3.69 ft-lb @Temperature 73.4 °F |
Instrumented Impact Energy @ peak, 6.6 m/s; ASTM D3763 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 157 °C | 315 °F | 80*10*4mm, Cut; ISO 75-1&2 |
Users viewing this material also viewed the following:
- Lehmann & Voss LUVOCOM® 50-7644 Polycarbonate, with carbon fiber and PTFE
- SABIC Innovative Plastics Xenoy® 1731J PBT+PC (Europe-Africa-Middle East)
- Lubrizol STAT-RITE® S-1100 Static Dissipative TPU
- The Chemical Company Nature-Flexx 509 Acetyl Tributyl Citrate, C20H34O8
- Williams Advanced Alloys Wambraze™ WB1238 Solder
- Dow Corning HS II BASE & 10:1 CLEAR CATALYST
- Eurostar Staramide ACF3 PA66, 15% Carbon Fiber Reinforced, Heat stabilized, Injection Molding
- Braskem PB681/59 LDPE Blown Film Extrusion Polyethylene
Copyright © lookpolymers.com All Rights Reserved