EPICHEM Epilon PC GF 10 V0 Polycarbonate, 10% Glass Fiber
| Category | Polymer , Thermoplastic , Polycarbonate (PC) , Polycarbonate, 10% Glass Filled |
| Manufacturer | EPICHEM srl |
| Trade Name | Epilon |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | EPICHEM Epilon PC GF 10 V0 Polycarbonate, 10% Glass Fiber.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Characteristics: self-extinguishing V0 at 1,6 mm, 10% glass fibre filled
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.25 g/cc | 0.0452 lb/in³ | ASTM D792, ISO 1183 |
| Filler Content | 10 % | 10 % | Internal |
| Water Absorption | 0.12 % @Temperature 23.0 °C |
0.12 % @Temperature 73.4 °F |
24h; ASTM D570, ISO 62 |
| Linear Mold Shrinkage | 0.0030 - 0.0040 cm/cm | 0.0030 - 0.0040 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 65.0 MPa | 9430 psi | ASTM D638, ISO R527 |
| Elongation at Break | 5.0 % | 5.0 % | ASTM D638, ISO R527 |
| Flexural Strength | 120 MPa | 17400 psi | ASTM D790, ISO 178 |
| Flexural Modulus | 3.60 GPa | 522 ksi | ASTM D790, ISO 178 |
| Izod Impact, Notched | 0.700 J/cm @Thickness 3.20 mm, Temperature -40.0 °C |
1.31 ft-lb/in @Thickness 0.126 in, Temperature -40.0 °F |
ASTM D256, ISO 180/4a |
| 0.800 - 1.00 J/cm @Thickness 3.20 mm, Temperature 0.000 °C |
1.50 - 1.87 ft-lb/in @Thickness 0.126 in, Temperature 32.0 °F |
ASTM D256, ISO 180/4a | |
| 0.900 - 1.10 J/cm @Thickness 3.20 mm, Temperature 23.0 °C |
1.69 - 2.06 ft-lb/in @Thickness 0.126 in, Temperature 73.4 °F |
ASTM D256, ISO 180/4a |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Maximum Service Temperature, Air | 140 °C | 284 °F | 20000 h; VDE 0304/P2-1, IEC 216 |
| 145 °C | 293 °F | 5000 h; VDE 0304/P2-1, IEC 216 | |
| 150 °C | 302 °F | few hours; VDE 0304/P2-1, IEC 216 | |
| Hot Ball Pressure Test | >= 140 °C | >= 284 °F | BS 3456, IEC 335 |
| Deflection Temperature at 1.8 MPa (264 psi) | 145 °C | 293 °F | ASTM D648, ISO 75 |
| Vicat Softening Point | 150 °C @Load 5.00 kg |
302 °F @Load 11.0 lb |
120°C/min; ASTM D1525/B, ISO 306/B |
| 160 °C @Load 0.999 kg |
320 °F @Load 2.20 lb |
120°C/min; ASTM D1525/A, ISO 306/A | |
| Flammability, UL94 | V-0 @Thickness 1.60 mm |
V-0 @Thickness 0.0630 in |
|
| V-0 @Thickness 3.20 mm |
V-0 @Thickness 0.126 in |
||
| Glow Wire Test | 960 °C @Thickness 3.20 mm |
1760 °F @Thickness 0.126 in |
VDE 0471/P2-4, IEC 695 |
| 960 °C @Thickness 2.00 mm |
1760 °F @Thickness 0.0787 in |
VDE 0471/P2-4, IEC 695 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Surface Resistance | 1.00e+14 ohm | 1.00e+14 ohm | ASTM D257, IEC 93 |
| Dielectric Constant | 3.0 @Frequency 1000 Hz |
3.0 @Frequency 1000 Hz |
ASTM D150, IEC 250 |
| Dielectric Strength | 35.0 kV/mm | 889 kV/in | ASTM D149, IEC 243 |
| Dissipation Factor | 0.0080 @Frequency 1000 Hz |
0.0080 @Frequency 1000 Hz |
ASTM D150, IEC 250 |
| Comparative Tracking Index | 175 V | 175 V | VDE 0303-P1, IEC 112 |
Users viewing this material also viewed the following:
- Polymer Resources PPX-FR3 Modified-PPO, V-1 Flame Retardant
- SABIC PVC 741E Emulsion Polyvinyl Chloride for Paste Preparation
- PolyOne Edgetek® AS-1000 Acrylonitrile Butadiene Styrene (ABS) (discontinued **)
- Greene Tweed CHEMRAZ® E38 Perfluoroelastomer
- Momentive Performance Materials PolarTherm® PT110 Boron Nitride (BN) Powder
- Lubrizol Advanced Materials Pearlstick® 46-10/01 Linear Thermoplastic Polyurethane Elastomer
- Hexcel® HexPly® 8552 Epoxy Matrix, A280-5H Fiber
- Ensinger Tecatron® XP-74 Compression Molded PPS Compound, with 30% Carbon Fiber and 8% PTFE
- DuPont Teijin Films Mylar® WC Polyester Film, 300 Gauge
Copyright © lookpolymers.com All Rights Reserved