SABIC Innovative Plastics LNP Lubricomp GL004 PSU

Category Polymer , Thermoplastic , Polysulfone (PSU)
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name LNP LUBRICOMP
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics LNP Lubricomp GL004 PSU.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
LNP* Lubricomp* GL004 is a compound based on Polysulfone resin containing PTFE. Added features of this material include: Internally Lubricated.This data was supplied by SABIC-IP for the Americas region.
Physical Properties Metric English Comments
Density 1.36 g/cc
0.0491 lb/in³
ASTM D 792
1.36 g/cc
0.0491 lb/in³
ISO 1183
Moisture Absorption at Equilibrium 0.20 %

@Time 86400 sec
0.20 %

@Time 24.0 hour
50% RH; ASTM D 570
Linear Mold Shrinkage, Flow 0.0077 cm/cm

@Time 86400 sec
0.0077 in/in

@Time 24.0 hour
ISO 294
0.0070 - 0.0090 cm/cm

@Time 86400 sec
0.0070 - 0.0090 in/in

@Time 24.0 hour
ASTM D 955
Linear Mold Shrinkage, Transverse 0.0070 - 0.0090 cm/cm

@Time 86400 sec
0.0070 - 0.0090 in/in

@Time 24.0 hour
ASTM D 955
0.0082 cm/cm

@Time 86400 sec
0.0082 in/in

@Time 24.0 hour
ISO 294
Mechanical Properties Metric English Comments
Tensile Strength at Break 47.0 MPa
6820 psi
ISO 527
49.0 MPa
7110 psi
ASTM D 638
Tensile Strength, Yield 48.0 MPa
6960 psi
ISO 527
50.0 MPa
7250 psi
ASTM D 638
Elongation at Break 5.8 %
5.8 %
ASTM D 638
6.3 %
6.3 %
ISO 527
Elongation at Yield 4.7 %
4.7 %
ASTM D 638
4.8 %
4.8 %
ISO 527
Tensile Modulus 1.86 GPa
270 ksi
1 mm/min; ISO 527
2.06 GPa
299 ksi
50 mm/min; ASTM D 638
Flexural Strength 71.0 MPa
10300 psi
ISO 178
Flexural Modulus 2.00 GPa
290 ksi
ISO 178
2.06 GPa
299 ksi
ASTM D 790
Izod Impact, Notched 0.850 J/cm

@Temperature 23.0 °C
1.59 ft-lb/in

@Temperature 73.4 °F
ASTM D 256
Izod Impact, Unnotched 5.76 J/cm

@Temperature 23.0 °C
10.8 ft-lb/in

@Temperature 73.4 °F
ASTM D 4812
Izod Impact, Notched (ISO) 6.00 kJ/m²

@Temperature 23.0 °C
2.86 ft-lb/in²

@Temperature 73.4 °F
80*10*4; ISO 180/1A
Izod Impact, Unnotched (ISO) 38.0 kJ/m²

@Temperature 23.0 °C
18.1 ft-lb/in²

@Temperature 73.4 °F
80*10*4; ISO 180/1U
Impact Test 5.00 J
3.69 ft-lb
Multiaxial Impact; ISO 6603
13.0 J

@Temperature 23.0 °C
9.59 ft-lb

@Temperature 73.4 °F
Instrumented Impact Energy @ peak; ASTM D 3763
Coefficient of Friction, Dynamic 0.23
0.23
ASTM D 3702 Modified
Coefficient of Friction, Static 0.10
0.10
ASTM D 3702 Modified
K (wear) Factor 44.3 x 10-8 mm³/N-M
22.0 x 10-10 in³-min/ft-lb-hr
Washer; ASTM D 3702 Modified
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 61.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
33.9 µin/in-°F

@Temperature -40.0 - 104 °F
ISO 11359-2
61.2 µm/m-°C

@Temperature -40.0 - 40.0 °C
34.0 µin/in-°F

@Temperature -40.0 - 104 °F
ASTM E 831
CTE, linear, Transverse to Flow 59.4 µm/m-°C

@Temperature -40.0 - 40.0 °C
33.0 µin/in-°F

@Temperature -40.0 - 104 °F
ASTM E 831
60.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
33.3 µin/in-°F

@Temperature -40.0 - 104 °F
ISO 11359-2
Deflection Temperature at 0.46 MPa (66 psi) 177 °C
351 °F
Flatw 80*10*4 sp=64mm; ISO 75/Bf
177 °C

@Thickness 3.20 mm
351 °F

@Thickness 0.126 in
unannealed; ASTM D 648
Deflection Temperature at 1.8 MPa (264 psi) 167 °C
333 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
162 °C

@Thickness 3.20 mm
324 °F

@Thickness 0.126 in
unannealed; ASTM D 648