- Ovation Polymers UTTAP™ SF 50030 GF Polyether Sulfone, 30% Glass Fiber
Ovation Polymers UTTAP™ SF 50030 GF Polyether Sulfone, 30% Glass Fiber
| Category | Polymer , Thermoplastic , Polyethersulfone (PES) , Polyethersulfone (PES), 30%Glass Fiber Filled |
| Manufacturer | Ovation Polymers |
| Trade Name | UTTAP™ |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Ovation Polymers UTTAP™ SF 50030 GF Polyether Sulfone, 30% Glass Fiber.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Excellent chemical and electrical resistance, high stiffness, modulus and HDTAll properties after 48hrs conditioning at 23°C/50% RH
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.62 g/cc | 1.62 g/cc | ASTM D792 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 169 MPa | 24500 psi | 50 mm/min; ASTM D638 |
| Elongation at Break | 3.5 % | 3.5 % | 50 mm/min; ASTM D638 |
| Tensile Modulus | 6.60 GPa | 957 ksi | 50 mm/min; ASTM D638 |
| Flexural Strength | 221 MPa | 32100 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| Flexural Modulus | 11.3 GPa | 1640 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
| Izod Impact, Notched | 0.801 J/cm @Temperature 23.0 °C |
1.50 ft-lb/in @Temperature 73.4 °F |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | >= 210 °C @Thickness 3.20 mm |
>= 410 °F @Thickness 0.126 in |
Unannealed; ASTM D648 |
| Glass Transition Temp, Tg | 225 °C | 437 °F | ASTM D3482 |