Material Notes:
LNP* Verton* RX93407D is a compound based on Nylon 66 resin.This data was supplied by SABIC-IP for the Americas region.
Physical Properties Metric English Comments
Specific Gravity 1.50 g/cc
1.50 g/cc
ASTM D 792
Density 1.51 g/cc
0.0546 lb/in³
ASTM D 792
1.54 g/cc
0.0556 lb/in³
ASTM D 792
Moisture Absorption at Equilibrium 0.93 %
0.93 %
23°C / 50% RH; ISO 62
0.64 %

@Time 86400 sec
0.64 %

@Time 24.0 hour
50% RH; ASTM D 570
Linear Mold Shrinkage, Flow 0.0010 - 0.0030 cm/cm

@Time 86400 sec
0.0010 - 0.0030 in/in

@Time 24.0 hour
ASTM D 955
0.0040 cm/cm

@Time 86400 sec
0.0040 in/in

@Time 24.0 hour
ASTM D 955
Linear Mold Shrinkage, Transverse 0.0060 - 0.0080 cm/cm

@Time 86400 sec
0.0060 - 0.0080 in/in

@Time 24.0 hour
ASTM D 955
Mechanical Properties Metric English Comments
Tensile Strength at Break 211 MPa
30600 psi
Type I, 5 mm/min; ASTM D 638
214 MPa
31000 psi
ASTM D 638
220 MPa
31900 psi
5 mm/min; ISO 527
Elongation at Break 2.1 %
2.1 %
5 mm/min; ISO 527
2.1 %
2.1 %
Type I, 5 mm/min; ASTM D 638
2.1 %
2.1 %
ASTM D 638
Tensile Modulus 14.24 GPa
2065 ksi
5 mm/min; ASTM D 638
14.75 GPa
2139 ksi
1 mm/min; ISO 527
15.9 GPa
2310 ksi
50 mm/min; ASTM D 638
Flexural Strength 304 MPa
44100 psi
1.3 mm/min, 50 mm span; ASTM D 790
310 MPa
45000 psi
ISO 178
330 MPa
47900 psi
ASTM D 790
Flexural Yield Strength 306 MPa
44400 psi
1.3 mm/min, 50 mm span; ASTM D 790
Flexural Modulus 11.3 GPa
1640 ksi
1.3 mm/min, 50 mm span; ASTM D 790
11.83 GPa
1716 ksi
2 mm/min; ISO 178
13.67 GPa
1983 ksi
ASTM D 790
Izod Impact, Notched 2.22 J/cm

@Temperature 23.0 °C
4.16 ft-lb/in

@Temperature 73.4 °F
ASTM D 256
2.67 J/cm

@Temperature 23.0 °C
5.00 ft-lb/in

@Temperature 73.4 °F
ASTM D 256
Izod Impact, Unnotched 11.8 J/cm

@Temperature 23.0 °C
22.1 ft-lb/in

@Temperature 73.4 °F
ASTM D 4812
14.75 J/cm

@Temperature 23.0 °C
27.63 ft-lb/in

@Temperature 73.4 °F
ASTM D 4812
Izod Impact, Notched (ISO) 27.0 kJ/m²

@Temperature 23.0 °C
12.8 ft-lb/in²

@Temperature 73.4 °F
80*10*4; ISO 180/1A
Izod Impact, Unnotched (ISO) 75.0 kJ/m²

@Temperature 23.0 °C
35.7 ft-lb/in²

@Temperature 73.4 °F
80*10*4; ISO 180/1U
Charpy Impact Unnotched 8.80 J/cm²

@Temperature 23.0 °C
41.9 ft-lb/in²

@Temperature 73.4 °F
ISO 179/2C
Charpy Impact, Notched 2.40 J/cm²

@Temperature 23.0 °C
11.4 ft-lb/in²

@Temperature 73.4 °F
ISO 179/2C
Impact Test 6.00 J
4.43 ft-lb
Multiaxial Impact; ISO 6603
17.0 J

@Temperature 23.0 °C
12.5 ft-lb

@Temperature 73.4 °F
Instrumented Impact Total Energy; ASTM D 3763
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 33.0 µm/m-°C

@Temperature -30.0 - 30.0 °C
18.3 µin/in-°F

@Temperature -22.0 - 86.0 °F
ASTM D 696
CTE, linear, Transverse to Flow 61.0 µm/m-°C

@Temperature -30.0 - 30.0 °C
33.9 µin/in-°F

@Temperature -22.0 - 86.0 °F
ASTM D 696
Deflection Temperature at 0.46 MPa (66 psi) 255 °C
491 °F
Flatw 80*10*4 sp=64mm; ISO 75/Bf
256 °C

@Thickness 3.20 mm
493 °F

@Thickness 0.126 in
unannealed; ASTM D 648
Deflection Temperature at 1.8 MPa (264 psi) 249 °C
480 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
249 °C

@Thickness 3.20 mm
480 °F

@Thickness 0.126 in
unannealed; ASTM D 648
251 °C

@Thickness 3.20 mm
484 °F

@Thickness 0.126 in
unannealed; ASTM D 648