SABIC Innovative Plastics LNP THERMOCOMP RF008ESY PA 66
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP THERMOCOMP |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP THERMOCOMP RF008ESY PA 66.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP THERMOCOMP* RF008ESY is a compound based on Nylon 66 resin containing 40% Glass Fiber. Added features of this material include: Easy Molding, Heat Stabilized.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.46 g/cc | 0.0527 lb/in³ | ISO 1183 |
| 1.471 g/cc | 0.05314 lb/in³ | ASTM D792 | |
| Moisture Absorption | 0.770 % | 0.770 % | 50% RH, 24 hrs; ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.0017 cm/cm @Time 86400 sec |
0.0017 in/in @Time 24.0 hour |
ISO 294 |
| 0.0020 cm/cm @Time 86400 sec |
0.0020 in/in @Time 24.0 hour |
ASTM D955 | |
| Linear Mold Shrinkage, Transverse | 0.0105 cm/cm @Time 86400 sec |
0.0105 in/in @Time 24.0 hour |
ISO 294 |
| 0.011 cm/cm @Time 86400 sec |
0.011 in/in @Time 24.0 hour |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 168 MPa | 24400 psi | ASTM D638 |
| 168 MPa | 24400 psi | ISO 527 | |
| Elongation at Break | 2.4 % | 2.4 % | ASTM D638 |
| 2.8 % | 2.8 % | ISO 527 | |
| Tensile Modulus | 11.9 GPa | 1730 ksi | 1 mm/min; ISO 527 |
| 13.03 GPa | 1890 ksi | 50 mm/min; ASTM D638 | |
| Flexural Strength | 246 MPa | 35700 psi | ASTM D790 |
| 263 MPa | 38100 psi | ISO 178 | |
| Flexural Modulus | 9.10 GPa | 1320 ksi | ASTM D790 |
| 11.3 GPa | 1640 ksi | ISO 178 | |
| Izod Impact, Notched | 1.12 J/cm | 2.10 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 10.89 J/cm | 20.40 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 12.0 kJ/m² | 5.71 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 74.0 kJ/m² | 35.2 ft-lb/in² | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 11.0 J | 8.11 ft-lb | Instrumented Impact Energy @ peak; ASTM D3763 |
| Impact Test | 3.00 J | 2.21 ft-lb | Multiaxial Impact; ISO 6603 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 251 °C @Thickness 3.20 mm |
484 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 227 °C | 441 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 229 °C @Thickness 3.20 mm |
444 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Flammability, UL94 | HB @Thickness 1.50 mm |
HB @Thickness 0.0591 in |
UL 94 by SABIC-IP |
Users viewing this material also viewed the following:
- PolyOne Geon™ Vinyl Wire & Cable WR3792CL Polyvinyl Chloride, Flexible (PVC, Flexible)
- DuPont™ Clysar® ABL Polyolefin Shrink Packaging Film, 75 Gauge (discontinued **)
- Lehmann & Voss LUVOCOM® 1-8357 Polyamide 66, with carbon fiber and glass fiber, heat stabilized
- MarkeTech Yttrium aluminum garnet:Ce (YGA:Ce; Y3Al5O12) Scintillator Crystal
- LyondellBasell Petrothene® LR590001 High Density Polyethylene
- CeramTec Sonox® P6 Piezoceramic
- Goodfellow Zinc 90/Nickel 10 Alloy
- Dow Corning HIGH VACUUM GREASE
- Colorite Polymers 9811 Clear Extrusion Vinyl Compound
- Bhansali Engineering Abstron PT-45M ABS Antistatic Extrusion Grade
Copyright © lookpolymers.com All Rights Reserved