Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength, Ultimate | 97.0 MPa | 14100 psi | ASTM D638 |
Chevron Phillips Ryton® R10 5004A PPS Polyphenylene Sulfide
(discontinued **) Ryton® PPS is used in many electronic and automotive applications because of its high strength, favorable electrical properties, and high temperature stability.Data provided by the manufacturer.Sol.. |
|||
Tensile Strength, Ultimate | 97.0 MPa | 14100 psi | ASTM D638 |
Shell Carilon® DB6G6P30 Polyketone, Lubricated, Glass-Reinforced, Injection Molding Grade
(discontinued **)&l Shell announced in Feb. 2000 that the Carilon product line is being discontinued. CARILON Polymer DA6P2L10 is a high-performance lubricated injection molding grade with mechanical properties which .. |
|||
Tensile Strength, Ultimate | 97.0 - 125 MPa | 14100 - 18100 psi | Average value: 113 MPa Grade Count:15 |
Overview of materials for Polycyclohexylenedimethylene Terephthalate (PCT), 30% Glass Reinforced This property data is a summary of similar materials in the MatWeb database for the category "PCT or PCTA, 30% Glass Reinforced".Specific grades with glass content between 25% and 34% are included. .. |
|||
Tensile Strength, Ultimate | 97.0 MPa | 14100 psi | |
Cookson Group Plaskon® 435 Mineral Filled Epoxy Molding Compound
(discontinued **) Test specimens were transfer molded and post cured 4 hours at 175°C.Combines exceptional reliability with wide molding process latitude. This material is designed to encapsulate a variety of semic.. |
|||
Tensile Strength, Ultimate | 97.0 MPa | 14100 psi | |
Cookson Group Plaskon® 440 Mineral Filled Novolac Epoxy Molding Compound
(discontinued **) Test specimens were transfer molded and post cured 4 hours at 175°C.Combines exceptional reliability with wide molding process latitude. This material is designed to encapsulate semiconductor devi.. |
|||
Tensile Strength, Ultimate | 97.0 MPa | 14100 psi | |
Cookson Group Plaskon® 440S Mineral Filled Novolac Epoxy Molding Compound
(discontinued **) Test specimens were transfer molded and post cured 4 hours at 175°C.Combines exceptional reliability with wide process latitude. This material is designed to encapsulate a wide range of semiconduc.. |
|||
Tensile Strength, Ultimate | 97.0 MPa | 14100 psi | ASTM D638 |
IDI Composites C-206 Thermoset Polyester, Sheet CORROSION - (Patent pending). Versatile family of compounds designed for pressurized and thermo-mechanically stressed applications. Excellent corrosion resistance and high strength.Data provided by .. |
|||
Tensile Strength, Ultimate | 97.0 MPa | 14100 psi | ASTM D638 |
IDI Composites E-205 Thermoset Polyester, Sheet ELECTRICAL - U.L. recognized (E53587). Versatile family of compounds designed to meet the most demanding electrical and electronic applications. Excellent dielectric properties and arc/track resista.. |
|||
Tensile Strength, Ultimate | 97.0 MPa | 14100 psi | ASTM D638 |
IDI Composites M-106 Thermoset Polyester, Molding Mechanical grade materials in a range of strengths with excellent moldability and molded part appearance.Data provided by the manufacturer. |
|||
Tensile Strength, Ultimate | 97.0 MPa @Temperature 1095 °C |
14100 psi @Temperature 2003 °F |
|
Haynes Hastelloy® X alloy, sheet Solid-solution-strengthened with very good high-temperature strength and very good resistance to oxidizing environments up to about 1095°C, and good carburization resistance. Applications includ.. |
|||
Tensile Strength, Ultimate | 97.0 MPa | 14100 psi | |
Cosmic Plastics E484 Glass Filled Epoxy Molding Compound, Electrical Grade Data provided by the manufacturer. |
|||
Tensile Strength, Ultimate | 97.0 MPa | 14100 psi | ATSM D638 |
Ashley Polymers Ashlene® 528L-13G Nylon 66, 13% Glass Reinforced General purpose glass fiber reinforced Nylon 66, designed for parts requiring excellent thermal and dimensional stability and higher strength than conventional resins.Data provided by the manufactur.. |
|||
Tensile Strength, Ultimate | 97.0 MPa | 14100 psi | ATSM D638 |
Ashley Polymers Ashlene® D925LH-30G Nylon 12, 30% Glass Reinforced A 30% glass reinforced heat and light stabilized Nylon 12.Data provided by the manufacturer |
|||
Tensile Strength, Ultimate | 97.0 MPa | 14100 psi | ASTM D638 |
A. Schulman ComAlloy E-16903B Nylon 6/6, Electrically Conductive - Stainless Steel Fiber Filled Data provided by the manufacturer, ComAlloy International Company.The ComAlloy product line has been integrated into the A Schulman product line. |
|||
Tensile Strength, Ultimate | 97.0 MPa | 14100 psi | ASTM D638 |
A. Schulman ComAlloy Voloy® 631 Nylon 6/6, Glass Reinforced, Flow Enhanced, Flame Retardant, UL Data provided by the manufacturer, ComAlloy International Company.13% Glass Reinforced.The ComAlloy product line has been integrated into the A Schulman product line. |
|||
Tensile Strength, Ultimate | 97.0 MPa | 14100 psi | ASTM D638 |
A. Schulman ComAlloy Voloy® 683 Nylon 6/6, Glass Fiber/Bead Reinforced, Nylon 6/6 Alloy, Flame Retardant, UL Data provided by the manufacturer, ComAlloy International Company.45% Glass Fiber/Bead Reinforced. Halogen- and phosphorous-freeThe ComAlloy product line has been integrated into the A Schulman prod.. |
|||
Tensile Strength, Ultimate | 97.0 MPa | 14100 psi | ATSM D638 |
Ashley Polymers Ashlene® 520-20GU Nylon 66, 20% Glass Reinforced 20% Glass reinforced Nylon 66, utility grade.Data provided by the manufacturer |
|||
Tensile Strength, Ultimate | 97.0 MPa | 14100 psi | ATSM D638 |
Ashley Polymers Ashlene® 925LMS-22G Nylon 12, 22% Glass Reinforced A 22% glass reinforced, Molybdenum disulfide filled, Nylon 12 resin for injection molding.Data provided by the manufacturer |