Material Notes:
Solid-solution-strengthened with very good high-temperature strength and very good resistance to oxidizing environments up to about 1095°C, and good carburization resistance. Applications include materials for fabricated or forged parts in gas turbine engines, and chemical and petrochemical plants, power plant and industrial heating applications.Data provided by the manufacturer, Haynes International, Inc.
Physical Properties Metric English Comments
Density 8.22 g/cc
0.297 lb/in³
at RT.
Mechanical Properties Metric English Comments
Tensile Strength, Ultimate 765 MPa
111000 psi
97.0 MPa

@Temperature 1095 °C
 14100 psi

@Temperature 2003 °F
175 MPa

@Temperature 980 °C
 25400 psi

@Temperature 1800 °F
310 MPa

@Temperature 870 °C
 45000 psi

@Temperature 1600 °F
465 MPa

@Temperature 760 °C
 67400 psi

@Temperature 1400 °F
570 MPa

@Temperature 650 °C
 82700 psi

@Temperature 1200 °F
615 MPa

@Temperature 540 °C
 89200 psi

@Temperature 1000 °F
Tensile Strength, Yield 380 MPa

@Strain 0.200 %
 55100 psi

@Strain 0.200 %
44.0 MPa

@Strain 0.200 %,
Temperature 1095 °C
 6380 psi

@Strain 0.200 %,
Temperature 2003 °F
91.0 MPa

@Strain 0.200 %,
Temperature 980 °C
 13200 psi

@Strain 0.200 %,
Temperature 1800 °F
195 MPa

@Strain 0.200 %,
Temperature 870 °C
 28300 psi

@Strain 0.200 %,
Temperature 1600 °F
235 MPa

@Strain 0.200 %,
Temperature 760 °C
 34100 psi

@Strain 0.200 %,
Temperature 1400 °F
245 MPa

@Strain 0.200 %,
Temperature 540 °C
 35500 psi

@Strain 0.200 %,
Temperature 1000 °F
245 MPa

@Strain 0.200 %,
Temperature 650 °C
 35500 psi

@Strain 0.200 %,
Temperature 1200 °F
Elongation at Break 44.2 %
44.2 %
in 51 mm
49.5 %

@Temperature 540 °C
 49.5 %

@Temperature 1000 °F
 in 51 mm
53.4 %

@Temperature 760 °C
 53.4 %

@Temperature 1400 °F
 in 51 mm
54 %

@Temperature 650 °C
 54 %

@Temperature 1200 °F
 in 51 mm
58.3 %

@Temperature 870 °C
 58.3 %

@Temperature 1600 °F
 in 51 mm
59.8 %

@Temperature 1095 °C
 59.8 %

@Temperature 2003 °F
 in 51 mm
65.1 %

@Temperature 980 °C
 65.1 %

@Temperature 1800 °F
 in 51 mm
Modulus of Elasticity 139 GPa

@Temperature 1000 °C
 20200 ksi

@Temperature 1830 °F
151 GPa

@Temperature 900 °C
 21900 ksi

@Temperature 1650 °F
158 GPa

@Temperature 800 °C
 22900 ksi

@Temperature 1470 °F
166 GPa

@Temperature 700 °C
 24100 ksi

@Temperature 1290 °F
174 GPa

@Temperature 600 °C
 25200 ksi

@Temperature 1110 °F
186 GPa

@Temperature 400 °C
 27000 ksi

@Temperature 752 °F
197 GPa

@Temperature 200 °C
 28600 ksi

@Temperature 392 °F
205 GPa

@Temperature 20.0 °C
 29700 ksi

@Temperature 68.0 °F
Thermal Properties Metric English Comments
CTE, linear 15.0 µm/m-°C

@Temperature 20.0 - 500 °C
 8.33 µin/in-°F

@Temperature 68.0 - 932 °F
15.3 µm/m-°C

@Temperature 20.0 - 600 °C
 8.50 µin/in-°F

@Temperature 68.0 - 1110 °F
15.6 µm/m-°C

@Temperature 20.0 - 700 °C
 8.67 µin/in-°F

@Temperature 68.0 - 1290 °F
16.0 µm/m-°C

@Temperature 20.0 - 800 °C
 8.89 µin/in-°F

@Temperature 68.0 - 1470 °F
16.3 µm/m-°C

@Temperature 20.0 - 900 °C
 9.06 µin/in-°F

@Temperature 68.0 - 1650 °F
16.6 µm/m-°C

@Temperature 20.0 - 1000 °C
 9.22 µin/in-°F

@Temperature 68.0 - 1830 °F
Thermal Conductivity 16.9 W/m-K

@Temperature 400 °C
 117 BTU-in/hr-ft²-°F

@Temperature 752 °F
20.9 W/m-K

@Temperature 600 °C
 145 BTU-in/hr-ft²-°F

@Temperature 1110 °F
22.8 W/m-K

@Temperature 700 °C
 158 BTU-in/hr-ft²-°F

@Temperature 1290 °F
24.8 W/m-K

@Temperature 800 °C
 172 BTU-in/hr-ft²-°F

@Temperature 1470 °F
26.7 W/m-K

@Temperature 900 °C
 185 BTU-in/hr-ft²-°F

@Temperature 1650 °F
28.7 W/m-K

@Temperature 1000 °C
 199 BTU-in/hr-ft²-°F

@Temperature 1830 °F
Melting Point 1260 - 1355 °C
2300 - 2471 °F
Solidus 1260 °C
2300 °F
Liquidus 1355 °C
2471 °F
Maximum Service Temperature, Air 1095 °C
2003 °F
Component Elements Properties Metric English Comments
Boron, B <= 0.0080 %
<= 0.0080 %
Carbon, C 0.10 %
0.10 %
Chromium, Cr 22 %
22 %
Cobalt, Co 1.5 %
1.5 %
Iron, Fe 18 %
18 %
Manganese, Mn <= 1.0 %
<= 1.0 %
Molybdenum, Mo 9.0 %
9.0 %
Nickel, Ni 47 %
47 %
Silicon, Si <= 1.0 %
<= 1.0 %
Tungsten, W 0.60 %
0.60 %