Overview of materials for Polycyclohexylenedimethylene Terephthalate (PCT), 30% Glass Reinforced

Category Polymer , Thermoplastic , Polyester, TP , Polycyclohexylenedimethylene Terephthalate (PCT) , Polycyclohexylenedimethylene Terephthalate (PCT), 30% Glass Reinforced
Manufacturer
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Overview of materials for Polycyclohexylenedimethylene Terephthalate (PCT), 30% Glass Reinforced.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
This property data is a summary of similar materials in the MatWeb database for the category "PCT or PCTA, 30% Glass Reinforced".Specific grades with glass content between 25% and 34% are included. Each property range of values reported is minimum and maximum values of appropriate MatWeb entries. The comments report the average value, and number of data points used to calculate the average. The values are not necessarily typical of any specific grade, especially less common values and those that can be most affected by additives or processing methods.
Physical Properties Metric English Comments
Density 1.39 - 1.65 g/cc
0.0502 - 0.0596 lb/in³
Average value: 1.52 g/cc Grade Count:15
Filler Content 30.0 %
30.0 %
Average value: 30.0 % Grade Count:10
Linear Mold Shrinkage 0.00200 - 0.00300 cm/cm
0.00200 - 0.00300 in/in
Average value: 0.00269 cm/cm Grade Count:8
Linear Mold Shrinkage, Transverse 0.00750 - 0.00900 cm/cm
0.00750 - 0.00900 in/in
Average value: 0.00806 cm/cm Grade Count:8
Mechanical Properties Metric English Comments
Hardness, Rockwell M 65.0 - 119
65.0 - 119
Average value: 84.7 Grade Count:3
Tensile Strength, Ultimate 97.0 - 125 MPa
14100 - 18100 psi
Average value: 113 MPa Grade Count:15
Elongation at Break 1.20 - 3.10 %
1.20 - 3.10 %
Average value: 2.05 % Grade Count:15
Modulus of Elasticity 7.40 - 11.0 GPa
1070 - 1600 ksi
Average value: 9.35 GPa Grade Count:15
Flexural Yield Strength 150 - 188 MPa
21800 - 27300 psi
Average value: 171 MPa Grade Count:15
Flexural Modulus 6.50 - 10.5 GPa
943 - 1520 ksi
Average value: 8.61 GPa Grade Count:15
Izod Impact, Notched 0.750 - 1.50 J/cm
1.41 - 2.81 ft-lb/in
Average value: 1.05 J/cm Grade Count:3
1.10 - 1.10 J/cm

@Temperature -40.0 - -40.0 °C
2.06 - 2.06 ft-lb/in

@Temperature -40.0 - -40.0 °F
Average value: 1.10 J/cm Grade Count:1
Izod Impact, Unnotched 6.90 - 9.10 J/cm
12.9 - 17.0 ft-lb/in
Average value: 7.77 J/cm Grade Count:3
Izod Impact, Notched (ISO) 6.00 - 10.0 kJ/m²
2.86 - 4.76 ft-lb/in²
Average value: 7.91 kJ/m² Grade Count:11
Charpy Impact Unnotched 2.00 - 5.50 J/cm²
9.52 - 26.2 ft-lb/in²
Average value: 3.82 J/cm² Grade Count:14
Charpy Impact, Notched 0.600 - 1.00 J/cm²
2.86 - 4.76 ft-lb/in²
Average value: 0.770 J/cm² Grade Count:15
Thermal Properties Metric English Comments
CTE, linear 6.00 - 48.0 µm/m-°C
3.33 - 26.7 µin/in-°F
Average value: 28.7 µm/m-°C Grade Count:3
CTE, linear, Transverse to Flow 85.0 - 100 µm/m-°C
47.2 - 55.6 µin/in-°F
Average value: 91.7 µm/m-°C Grade Count:3
Melting Point 283 - 285 °C
541 - 545 °F
Average value: 284 °C Grade Count:13
Deflection Temperature at 0.46 MPa (66 psi) 268 - 276 °C
514 - 529 °F
Average value: 271 °C Grade Count:4
Deflection Temperature at 1.8 MPa (264 psi) 221 - 262 °C
430 - 504 °F
Average value: 247 °C Grade Count:15
UL RTI, Electrical 150 °C
302 °F
Average value: 150 °C Grade Count:4
UL RTI, Mechanical without Impact 140 - 150 °C
284 - 302 °F
Average value: 149 °C Grade Count:4
Flammability, UL94 HB - V-0
HB - V-0
Grade Count:13
Electrical Properties Metric English Comments
Electrical Resistivity 1.00e+15 - 1.00e+16 ohm-cm
1.00e+15 - 1.00e+16 ohm-cm
Average value: 3.25e+15 ohm-cm Grade Count:4
Surface Resistance 1.00e+15 - 1.00e+16 ohm
1.00e+15 - 1.00e+16 ohm
Average value: 5.50e+15 ohm Grade Count:4
Dielectric Constant 3.00 - 3.30
3.00 - 3.30
Average value: 3.11 Grade Count:3
Dielectric Strength 16.1 - 35.0 kV/mm
409 - 889 kV/in
Average value: 25.6 kV/mm Grade Count:6
Dissipation Factor 0.00200 - 0.0180
0.00200 - 0.0180
Average value: 0.0101 Grade Count:3
Comparative Tracking Index 440 - 600 V
440 - 600 V
Average value: 520 V Grade Count:5
Processing Properties Metric English Comments
Processing Temperature 80.0 - 120 °C
176 - 248 °F
Average value: 102 °C Grade Count:5
Melt Temperature 295 - 310 °C
563 - 590 °F
Average value: 302 °C Grade Count:15
Mold Temperature 80.0 - 175 °C
176 - 347 °F
Average value: 112 °C Grade Count:10
Drying Temperature 70.0 - 150 °C
158 - 302 °F
Average value: 98.7 °C Grade Count:15
Moisture Content 0.0300 %
0.0300 %
Average value: 0.0300 % Grade Count:14