Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength, Ultimate | 18.6 MPa | 2700 psi | ASTM D638-95 |
Multibase Multi-Pro® 4518 CU W 45% Mineral Filled Polypropylene Mineral filled PP concentrate formulated to meet resin furniture properties at 1:1 dilution with polypropylene. The product contains UV and TiO2 adequate to stabilize the total product.Data provide.. |
|||
Tensile Strength, Ultimate | 18.6 MPa | 2700 psi | ASTM D638 |
DuPont 20 Series 2020 Specialty Polyethylene Resin
(discontinued **) DuPont 2020T and 2020 specialty low density polyethylene resins are products characterized by low melt index and intermediate crystallinity. These products, produced via a unique polymerization proc.. |
|||
Tensile Strength, Ultimate | 18.6 - 42.0 MPa | 2700 - 6090 psi | Average value: 29.1 MPa Grade Count:23 |
Overview of materials for Polytetrafluoroethylene (PTFE) Powder This property data is a summary of similar materials in the MatWeb database for the category "PTFE Powder". Each property range of values reported is minimum and maximum values of appropriate MatWeb.. |
|||
Tensile Strength, Ultimate | 18.6 MPa | 2700 psi | 2 in/min.; ASTM D638 |
Ineos R01A-01 Polypropylene Copolymer, Antistatic An antistated polypropylene random copolymer produced by Ineos utilizing unique catalyst technology. It is designed for blowmolding and extrusion applications and exhibits good stiffness and improv.. |
|||
Tensile Strength, Ultimate | 18.6 MPa | 2700 psi | |
Sylvin Technologies 6400-85 PVC Wire/Cable Compound Information provided by Sylvin Technologies Inc. |
|||
Tensile Strength, Ultimate | 18.6 MPa | 2700 psi | |
Sylvin Technologies 8915-85 Natural PVC Extrusion Compound Information provided by Sylvin Technologies Inc. |
|||
Tensile Strength, Ultimate | 18.6 MPa | 2700 psi | |
Sylvin Technologies 8925-90 Natural PVC Extrusion Compound Information provided by Sylvin Technologies Inc. |
|||
Tensile Strength, Ultimate | 18.6 MPa | 2700 psi | |
Sylvin Technologies 9600-95 Clear PVC Molding Compound Information provided by Sylvin Technologies Inc. |
|||
Tensile Strength, Ultimate | 18.6 MPa | 2700 psi | |
Sylvin Technologies 9915-85 Natural PVC Molding Compound Information provided by Sylvin Technologies Inc. |
|||
Tensile Strength, Ultimate | 18.6 MPa | 2700 psi | |
Sylvin Technologies 5042N PVC Wire/Cable Compound Information provided by Sylvin Technologies Inc. |
|||
Tensile Strength, Ultimate | 18.6 MPa | 2700 psi | |
Sylvin Technologies 6112-85 FU PVC Wire/Cable Compound Information provided by Sylvin Technologies Inc. |
|||
Tensile Strength, Ultimate | 18.6 MPa | 2700 psi | ASTM D412 |
Lubrizol Estane® T460AH Thermoplastic Polyurethane Type: Estane® T460AH is a Shore 60A, polyester grade, plasticizer-free, with low hardness and Hydrolytic Stabilizer thermoplastic polyurethane (TPU).Uses: Injection Molding.Availability: Americas, .. |
|||
Tensile Strength, Ultimate | 18.6 MPa | 2700 psi | ASTM D638 |
DuPont 20 Series 2020T Specialty Polyethylene Resin DuPont 2020T and 2020 specialty low density polyethylene resins are products characterized by low melt index and intermediate crystallinity. These products, produced via a unique polymerization proc.. |
|||
Tensile Strength, Ultimate | 18.6 MPa | 2700 psi | ASTM D638 |
Ecomass® 4703ZC76 Stainless Steel Filled Polyurethane Nontoxic alternative to Lead (Pb), weighting and balancing applicationsModerate Specific GravityStainless Steel Filled Polyurethane (TPU)FlexibleInformation provided by Technical Polymers |
|||
Tensile Strength, Ultimate | 18.6 MPa | 2700 psi | ASTM D638 |
DuPont™ Surlyn® 8320 Ionomer Resin, Sodium Surlyn® 8320 thermoplastic resin is an advanced ethylene/methacrylic acid (E/MAA) copolymer, in which the MAA acid groups have been partially neutralized with sodium ions. This very low modulus sod.. |
|||
Tensile Strength, Ultimate | 18.6 MPa | 2700 psi | |
Dow HDPE 12450N High Density Polyethylene DOW HDPE 12450N resin is a narrow molecular weight distribution copolymer designed to offer excellent impact strength and toughness with moderate stiffness. This resin has good processability over a.. |
|||
Tensile Strength, Ultimate | 18.6 MPa | 2700 psi | ASTM D412 |
Colorite Polymers CS6023GP Non Lead Wire and Cable Vinyl Compound Description: Colorite specialty wire and cable compounds feature low smoke properties, excellent flame retardance, low temperature flexibility, and resistance to abrasion and chemicals. All are avai.. |
|||
Tensile Strength, Ultimate | 18.6 MPa | 2700 psi | ASTM D638 |
Colorite Polymers 8300 General Purpose Vinyl Compound Description: Colorite produces many vinyl compounds. They have the compounds that perfectly suit whatever the application. Requirements such as ultraviolet ray resistance, fungus resistance, flame r.. |
|||
Tensile Strength, Ultimate | 18.6 MPa | 2700 psi | ASTM D638 |
Colorite Polymers 8302 General Purpose Vinyl Compound Description: Colorite produces many vinyl compounds. They have the compounds that perfectly suit whatever the application. Requirements such as ultraviolet ray resistance, fungus resistance, flame r.. |
|||
Tensile Strength, Ultimate | 18.6 MPa | 2700 psi | |
Colorite Polymers 8311 Clear Extrusion Vinyl Compound Description: Clear non-toxic vinyl compounds are utilized by the health and medical industries for the extrusion of various components for the production of devices. The vinyl components used in pre.. |
|||
Tensile Strength, Ultimate | 18.6 MPa | 2700 psi | ASTM D638 |
Colorite Polymers 8534 General Purpose Vinyl Compound Description: Colorite produces many vinyl compounds. They have the compounds that perfectly suit whatever the application. Requirements such as ultraviolet ray resistance, fungus resistance, flame r.. |
|||
Tensile Strength, Ultimate | 18.6 MPa | 2700 psi | ASTM D638 |
Colorite Polymers 9226 General Purpose Vinyl Compound Description: Colorite produces many vinyl compounds. They have the compounds that perfectly suit whatever the application. Requirements such as ultraviolet ray resistance, fungus resistance, flame r.. |
|||
Tensile Strength, Ultimate | 18.6 MPa | 2700 psi | ASTM D638 |
Colorite Polymers 93-732A General Purpose Vinyl Compound Description: Colorite produces many vinyl compounds. They have the compounds that perfectly suit whatever the application. Requirements such as ultraviolet ray resistance, fungus resistance, flame r.. |
|||
Tensile Strength, Ultimate | 18.6 MPa | 2700 psi | ASTM D412 |
Colorite Polymers CS6038UL Wire and Cable Insulation Vinyl Compound Description: Colorite specialty wire and cable compounds feature low smoke properties, excellent flame retardance, low temperature flexibility, and resistance to abrasion and chemicals. All are avai.. |
|||
Tensile Strength, Ultimate | 18.6 MPa | 2700 psi | 2 in/min (50 mm/min); ASTM D638 |
Bapolene® 4071 Polypropylene, Fiber/Injection Grade Bapolene PP4071 is a high flow PP homopolymer for staple and continuous filament applications as well as general purpose injection molding. This resin exhibits good melt and thermal stability.Appli.. |
|||
Tensile Strength, Ultimate | 18.6 MPa | 2700 psi | |
BCC Products BC 8690E Polyurethane Elastomer BC 8690E is a two-component urethane elastomer compound specifically designed for casting applications. This product is a safe, easy-to-handle, room temperature mixing and curing system that contain.. |
|||
Tensile Strength, Ultimate | 18.6 MPa | 2700 psi | ASTM D638 |
Colorite Polymers 8000 General Purpose Vinyl Compound Description: Colorite produces many vinyl compounds. They have the compounds that perfectly suit whatever the application. Requirements such as ultraviolet ray resistance, fungus resistance, flame r.. |
|||
Tensile Strength, Ultimate | 18.6 MPa | 2700 psi | ASTM D638 |
Colorite Polymers 8002 General Purpose Vinyl Compound Description: Colorite produces many vinyl compounds. They have the compounds that perfectly suit whatever the application. Requirements such as ultraviolet ray resistance, fungus resistance, flame r.. |
|||
Tensile Strength, Ultimate | 18.6 MPa | 2700 psi | ASTM D412-80 |
DuPont Performance Polymers Hypalon® 40S Chlorosulfonated Polyethylene Rubber, Mineral Filled Compound
(disco Mineral filled compound with 100 parts Hypalon; 80 parts hard clay; 4 parts magnesia; 30 parts aromatic process oil; 3 parts pentaerythritol; and 2 parts Tetrone® A rubber accelerator (from DuPont .. |
|||
Tensile Strength, Ultimate | 18.6 MPa | 2700 psi | ASTM D412 |
DuPont Performance Polymers Kalrez® 1050LF FFKM Perfluoroelastomer A general-purpose compound for O-rings, seals, and other parts used in chemical process industries. It has good hot water/steam, excellent amine resistance, and enhanced compression set properties... |