Braskem HM 150 HDPE Monofilament Polyethylene (discontinued **)
| Category | Polymer , Thermoplastic , Polyethylene (PE) , HDPE |
| Manufacturer | |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Braskem HM 150 HDPE Monofilament Polyethylene
(discontinued **).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Applications: Raschel; flat yarn; general and industrial rape netting. Information provided by Braskem
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.950 g/cc | 0.0343 lb/in³ | ASTM D1505 |
| ESCR 100% Igepal® | 24 hour @Thickness 3.00 mm, Temperature 23.0 °C |
24 hour @Thickness 0.118 in, Temperature 73.4 °F |
compression molded plaques; ASTM D1693B |
| Melt Flow | 1.0 g/10 min @Load 2.16 kg, Temperature 190 °C |
1.0 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore D | 64 | 64 | ASTM D2240 |
| Tensile Strength at Break | 33.0 MPa | 4790 psi | ASTM D638 |
| Film Tensile Strength at Yield, MD | 26.0 MPa | 3770 psi | ASTM D882 |
| Film Tensile Strength at Yield, TD | 30.0 MPa | 4350 psi | ASTM D882 |
| Tensile Strength, Yield | 28.0 MPa | 4060 psi | ASTM D638 |
| Film Elongation at Break, MD | 1300 % | 1300 % | ASTM D882 |
| Film Elongation at Break, TD | >= 1700 % | >= 1700 % | ASTM D882 |
| Flexural Modulus | 1.145 GPa | 166.1 ksi | ASTM D790 |
| Elmendorf Tear Strength, MD | 0.700 g/micron | 17.8 g/mil | ASTM D1922 |
| Elmendorf Tear Strength, TD | 1.90 g/micron | 48.3 g/mil | ASTM D1922 |
| Film Tensile Strength at Break, MD | 49.0 MPa | 7110 psi | ASTM D882 |
| Film Tensile Strength at Break, TD | 48.0 MPa | 6960 psi | ASTM D882 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Vicat Softening Point | 126 °C | 259 °F | ASTM D1525 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Minimum Recommended Thickness | 15 µm | |
| Puncture Strength | 26 J/mm | Braskem® Method |
Users viewing this material also viewed the following:
- Samyang Triloy® 410 PC/PET alloy (discontinued **)
- Pyrotek M-8 Fiber Seal Pre-cut Gasket
- SABIC Innovative Plastics LNP LUBRICOMP JX00061 PES (Europe-Africa-Middle East)
- Saint-Gobain CHR® SG05-06(R) Premium Glass-PTFE Backing Silicone Adhesive Pressure Sensitive Tape
- Techmer ES Plastiblend® TPX-HTN-000CA
- DuPont Performance Polymers Crastin® HR5315HF NC010 Polybutylene Terephthalate (PBT) (Unverified Data**)&
- Axiall 8820 Moldings & Extrusions Flexible PVC
- Braskem LL218/21 Cast Film Extrusion Linear Low Density Polyethylene
- Fainplast Compounds PM 85/M Flexible PVC, Extrusion
- Covestro Makrolon® LQ 2643 Polycarbonate, UV-Stabilized
Copyright © lookpolymers.com All Rights Reserved