Polimeri Europa Eraclene® FA 706 Hexene Copolymer High Density Polyethylene - Blown Film Extrusion

Category Polymer , Film , Thermoplastic , Polyethylene (PE) , HDPE , High Density Polyethylene (HDPE), Film Grade
Manufacturer Polimeri Europa (Former EniChem)
Trade Name Eraclene®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Polimeri Europa Eraclene® FA 706 Hexene Copolymer High Density Polyethylene - Blown Film Extrusion.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Eraclene FA 706 is a high density polyethylene resin (HDPE), hexene copolymer, with antioxidants, suitable for blown film extrusion.Films manufactured with Eraclene FA 706 show good processability together with high temperature resistance and good tensile properties at low strain (Young modulus, yield strength).Main Applications: Eraclene FA 706 is especially recommended for the production of "paper-like" films having high stiffness together with high thermal resistance. Due to its excellent compromise between drawability and bubble stability, Eraclene FA 706 is the ideal choice for manufacturing of high strength thin films (shopping bags, bags on the reel, lamination films).Information provided by Polimeri Europa.
Physical Properties Metric English Comments
Specific Gravity 0.952 g/cc
0.952 g/cc
ISO 1183
Thickness 10.0 - 50.0 microns
0.394 - 1.97 mil
Recommended
Melt Flow 0.30 g/10 min

@Load 5.00 kg,
Temperature 190 °C
0.30 g/10 min

@Load 11.0 lb,
Temperature 374 °F
ISO 1133
8.0 g/10 min

@Load 21.6 kg,
Temperature 190 °C
8.0 g/10 min

@Load 47.6 lb,
Temperature 374 °F
ISO 1133
Mechanical Properties Metric English Comments
Film Elongation at Break, MD 500 %
500 %
ISO 527-3
Film Elongation at Break, TD 450 %
450 %
ISO 527-3
Elmendorf Tear Strength, MD 1.019 g/micron
25.88 g/mil
ISO 6383-2
Elmendorf Tear Strength, TD 2.5475 g/micron
64.706 g/mil
ISO 6383-2
Dart Drop Test 100 g
0.221 lb
F50; ISO 7765-1
Film Tensile Strength at Break, MD 46.0 MPa
6670 psi
ISO 527-3
Film Tensile Strength at Break, TD 48.0 MPa
6960 psi
ISO 527-3
1% Secant Modulus, MD 760 MPa
110000 psi
ISO 527-3
1% Secant Modulus, TD 830 MPa
120000 psi
ISO 527-3
Thermal Properties Metric English Comments
Melting Point 134 °C
273 °F
Internal method
Vicat Softening Point 127 °C

@Load 1.00 kg
261 °F

@Load 2.20 lb
ISO 306/A
Brittleness Temperature <= -60.0 °C
<= -76.0 °F
ASTM D746