Borealis Borstar® FB1350 Medium Density Polyethylene

Category Polymer , Thermoplastic , Polyethylene (PE) , MDPE
Manufacturer Borealis
Trade Name Borstar®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Borealis Borstar® FB1350 Medium Density Polyethylene.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Borstar® FB1350 is a linear medium density polyethylene grade combining excellent extrusion properties with high film stiffness. Borstar® FB1350 is well suited for mono- and coextrusion of films produced with high neck or low neck extrusion. Applications Borstar® FB1350 has been developed especially for applications like heavy-duty sack, general packaging, pouches, refuse sacks and liners, geomembranes, and blending.Information provided by Borealis AG
Physical Properties Metric English Comments
Density 0.935 g/cc
0.0338 lb/in³
ISO 1183
Melt Flow 0.70 g/10 min

@Load 5.00 kg,
Temperature 190 °C
0.70 g/10 min

@Load 11.0 lb,
Temperature 374 °F
ISO 1133
15 g/10 min

@Load 21.6 kg,
Temperature 190 °C
15 g/10 min

@Load 47.6 lb,
Temperature 374 °F
ISO 1133
Mechanical Properties Metric English Comments
Film Elongation at Break, MD 400 %
400 %
ISO 527-3
Film Elongation at Break, TD 650 %
650 %
ISO 527-3
Tensile Modulus 0.500 GPa
72.5 ksi
MD; ASTM D882-A
0.650 GPa
94.3 ksi
TD; ASTM D882-A
Coefficient of Friction 0.40
0.40
ISO 8295
Elmendorf Tear Strength MD 200 g
200 g
ISO 6383/2
Elmendorf Tear Strength TD 150 g
150 g
ISO 6383/2
Elmendorf Tear Strength, MD 2.04 g/micron
51.8 g/mil
ISO 6383/2
Elmendorf Tear Strength, TD 26.5 g/micron
673 g/mil
ISO 6383/2
Dart Drop Test 220 g

@Thickness 0.0250 mm
0.485 lb

@Thickness 0.000984 in
ISO 7765-1
Film Tensile Strength at Break, MD 57.0 MPa
8270 psi
ISO 527-3
Film Tensile Strength at Break, TD 48.0 MPa
6960 psi
ISO 527-3
Processing Properties Metric English Comments
Melt Temperature 190 - 210 °C