NOVA Chemicals Sclair® FP019-C Octene Copolymer LLDPE Film Resin

Category Polymer , Film , Thermoplastic , Polyethylene (PE) , LLDPE , Linear Low Density Polyethylene (LLDPE)/Octene, Film
Manufacturer NOVA Chemicals
Trade Name Sclair®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF NOVA Chemicals Sclair® FP019-C Octene Copolymer LLDPE Film Resin.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
FP019-C is biologically and chemically inert.Features: Superior toughness, Outstanding melt strength, Excellent sealability, Low gelAdditives: Polymer Process AidApplications: High toughness film, freezer film, lamination and sealant filmProperties measured from blown film produced on a laboratory extruder with 4" die and a 35-mil die gap at a blowup ratio of 2.5:1, and melt temperature 420°F. Films were made from 100% FP019-C.
Physical Properties Metric English Comments
Density 0.918 g/cc
0.0332 lb/in³
ASTM D 792
Thickness 25.0 microns
0.984 mil
Melt Flow 0.80 g/10 min

@Load 2.16 kg,
Temperature 190 °C
0.80 g/10 min

@Load 4.76 lb,
Temperature 374 °F
ASTM D 1238
Mechanical Properties Metric English Comments
Film Tensile Strength at Yield, MD 9.20 MPa
1330 psi
ASTM D 882
Film Tensile Strength at Yield, TD 9.50 MPa
1380 psi
ASTM D 882
Film Elongation at Break, MD 560 %
560 %
ASTM D 882
Film Elongation at Break, TD 760 %
760 %
ASTM D 882
Elmendorf Tear Strength MD 303 g
303 g
ASTM D 1922
Elmendorf Tear Strength TD 588 g
588 g
ASTM D 1922
Elmendorf Tear Strength, MD 12.1 g/micron
307 g/mil
ASTM D 1922
Elmendorf Tear Strength, TD 23.5 g/micron
597 g/mil
Dart Drop Test 560 g
1.23 lb
22; ASTM D 1709/A
Film Tensile Strength at Break, MD 61.0 MPa
8850 psi
ASTM D 882
Film Tensile Strength at Break, TD 48.0 MPa
6960 psi
ASTM D 882
1% Secant Modulus, MD 140 MPa
20300 psi
ASTM D 882
1% Secant Modulus, TD 170 MPa
24700 psi
ASTM D 882
Optical Properties Metric English Comments
Haze 7.0 %
7.0 %
ASTM D 1003
Gloss 65 %
65 %
at 45°; ASTM D 2457
Descriptive Properties Value Comments
Low Friction Puncture (J/mm) 89
NOVA Chemicals Test Method