BASF Ultramid® 8260 HS BK-102 40% Mineral Filled PA6 (Dry)

Category Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, 40% Mineral Filled
Manufacturer BASF
Trade Name Ultramid®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF BASF Ultramid® 8260 HS BK-102 40% Mineral Filled PA6 (Dry).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Ultramid 8260 HS BK-102 is a heat stabilized, pigmented black, 40% mineral reinforced PA6 injection molding resin. It possesses high stiffness, dimensional stability and heat resistance combined with excellent processability including low warp and resistance to sink-mark formation. It maintains its inherent chemical resistance to greases, oils and hydrocarbons.
Physical Properties Metric English Comments
Density 1.49 g/cc
0.0538 lb/in³
ISO 1183
Water Absorption 1.1 %
1.1 %
24 hour; ISO Test
5.7 %
5.7 %
ISO 62
Moisture Absorption at Equilibrium 1.6 %
1.6 %
23°C/50% R.H.; ISO 62
Linear Mold Shrinkage 0.0090 cm/cm
0.0090 in/in
ASTM Data; MD
Mechanical Properties Metric English Comments
Hardness, Rockwell R 119
119
ASTM Test
Tensile Strength at Break 85.0 MPa
12300 psi
0.2 in/min; ASTM Test
30.0 MPa

@Temperature 120 °C
4350 psi

@Temperature 248 °F
ISO Data
30.0 MPa

@Temperature 120 °C
4350 psi

@Temperature 248 °F
ASTM Test
40.0 MPa

@Temperature 80.0 °C
5800 psi

@Temperature 176 °F
ASTM Test
40.0 MPa

@Temperature 80.0 °C
5800 psi

@Temperature 176 °F
ISO Data
135 MPa

@Temperature -40.0 °C
19600 psi

@Temperature -40.0 °F
ASTM Test
135 MPa

@Temperature -40.0 °C
19600 psi

@Temperature -40.0 °F
ISO Data
Tensile Strength, Ultimate 85.0 MPa
12300 psi
5mm/min; ISO 527
Elongation at Break 10 %
10 %
0.2 in/min; ASTM Test
10 %
10 %
5mm/min; ISO 527
6.0 %

@Temperature -40.0 °C
6.0 %

@Temperature -40.0 °F
ISO Data
6.0 %

@Temperature -40.0 °C
6.0 %

@Temperature -40.0 °F
ASTM Test
35 %

@Temperature 80.0 °C
35 %

@Temperature 176 °F
ASTM Test
35 %

@Temperature 80.0 °C
35 %

@Temperature 176 °F
ISO Data
40 %

@Temperature 120 °C
40 %

@Temperature 248 °F
ASTM Test
40 %

@Temperature 120 °C
40 %

@Temperature 248 °F
ISO Data
Tensile Modulus 6.40 GPa
928 ksi
1mm/min; ISO 527
0.970 GPa

@Temperature 120 °C
141 ksi

@Temperature 248 °F
ISO Data
1.36 GPa

@Temperature 80.0 °C
197 ksi

@Temperature 176 °F
ISO Data
8.31 GPa

@Temperature -40.0 °C
1210 ksi

@Temperature -40.0 °F
ISO Data
Flexural Strength 140 MPa
20300 psi
ISO Data
Flexural Modulus 5.20 GPa
754 ksi
ISO Data
Izod Impact, Notched (ISO) 6.00 kJ/m²
2.86 ft-lb/in²
ISO Test
Charpy Impact Unnotched 13.0 J/cm²
61.9 ft-lb/in²
ISO 179
Charpy Impact, Notched 0.300 J/cm²
1.43 ft-lb/in²
ISO 179
Thermal Properties Metric English Comments
CTE, linear 50.0 µm/m-°C

@Temperature -30.0 - 30.0 °C
27.8 µin/in-°F

@Temperature -22.0 - 86.0 °F
ASTM Test
Melting Point 220 °C
428 °F
10 K/min
220 °C
428 °F
ASTM Test
Deflection Temperature at 0.46 MPa (66 psi) 190 °C
374 °F
ISO 75
Flammability, UL94 HB
HB
HB

@Thickness 3.00 mm
HB

@Thickness 0.118 in
Electrical Properties Metric English Comments
Volume Resistivity >= 1.00e+13 ohm-cm
>= 1.00e+13 ohm-cm
IEC 60093
Processing Properties Metric English Comments
Melt Temperature 275 °C
527 °F
Injection molding
Mold Temperature 95.0 °C
203 °F
Injection molding
Descriptive Properties Value Comments
Color BK-102
Commercial Status Active America
Form Pellets
Impact Modified No
Primary Processing Technique Injection Molding
Processing Injection Molding
Special characteristic Heat stabilized or stable to heat
X
UL.UL-C Yes