SABIC Innovative Plastics Ultem ATX102R PEI+PCE

Category Polymer , Thermoplastic , Polyetherimide (PEI) , Polyetherimide (PEI) + PCE
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name ULTEM
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics Ultem ATX102R PEI+PCE.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
20% Glass fiber filled, high flow Polyetherimide blend with internal mold release. ECO Conforming, UL94 V0 and 5VA listing.This data was supplied by SABIC-IP for the Americas region.
Physical Properties Metric English Comments
Specific Gravity 1.43 g/cc
1.43 g/cc
ASTM D 792
Density 1.43 g/cc
0.0517 lb/in³
ISO 1183
Moisture Absorption at Equilibrium 0.15 %
0.15 %
23°C / 50% RH; ISO 62
Water Absorption at Saturation 0.40 %

@Temperature 23.0 °C
0.40 %

@Temperature 73.4 °F
ISO 62
Linear Mold Shrinkage, Flow 0.0030 - 0.0050 cm/cm
0.0030 - 0.0050 in/in
on tensile bar; SABIC Method
0.0030 - 0.0050 cm/cm

@Thickness 3.20 mm
0.0030 - 0.0050 in/in

@Thickness 0.126 in
SABIC Method
Linear Mold Shrinkage, Transverse 0.0040 - 0.0060 cm/cm

@Thickness 3.20 mm
0.0040 - 0.0060 in/in

@Thickness 0.126 in
SABIC Method
Melt Flow 40 g/10 min

@Load 6.60 kg,
Temperature 337 °C
40 g/10 min

@Load 14.6 lb,
Temperature 639 °F
ASTM D 1238
55 g/10 min

@Load 5.00 kg,
Temperature 360 °C
55 g/10 min

@Load 11.0 lb,
Temperature 680 °F
[cm^3/10 min] Melt Volume Rate; ISO 1133
Mechanical Properties Metric English Comments
Tensile Strength at Break 98.0 MPa
14200 psi
5 mm/min; ISO 527
117 MPa
17000 psi
Type I, 5 mm/min; ASTM D 638
Tensile Strength, Yield 100 MPa
14500 psi
5 mm/min; ISO 527
117 MPa
17000 psi
Type I, 5 mm/min; ASTM D 638
Elongation at Break 3.9 %
3.9 %
5 mm/min; ISO 527
4.3 %
4.3 %
Type I, 5 mm/min; ASTM D 638
Elongation at Yield 3.3 %
3.3 %
5 mm/min; ISO 527
4.3 %
4.3 %
Type I, 5 mm/min; ASTM D 638
Tensile Modulus 6.15 GPa
892 ksi
1 mm/min; ISO 527
6.40 GPa
928 ksi
5 mm/min; ASTM D 638
Flexural Yield Strength 170 MPa
24700 psi
2 mm/min; ISO 178
182 MPa
26400 psi
1.3 mm/min, 50 mm span; ASTM D 790
Flexural Modulus 5.24 GPa
760 ksi
2 mm/min; ISO 178
5.88 GPa
853 ksi
1.3 mm/min, 50 mm span; ASTM D 790
Izod Impact, Notched 0.950 J/cm

@Temperature 23.0 °C
1.78 ft-lb/in

@Temperature 73.4 °F
ASTM D 256
Izod Impact, Unnotched 8.54 J/cm

@Temperature 23.0 °C
16.0 ft-lb/in

@Temperature 73.4 °F
ASTM D 4812
Izod Impact, Notched (ISO) 6.00 kJ/m²

@Temperature 23.0 °C
2.86 ft-lb/in²

@Temperature 73.4 °F
80*10*4; ISO 180/1A
6.00 kJ/m²

@Temperature -30.0 °C
2.86 ft-lb/in²

@Temperature -22.0 °F
80*10*4; ISO 180/1A
Izod Impact, Unnotched (ISO) 49.0 kJ/m²

@Temperature 23.0 °C
23.3 ft-lb/in²

@Temperature 73.4 °F
80*10*4; ISO 180/1U
49.0 kJ/m²

@Temperature -30.0 °C
23.3 ft-lb/in²

@Temperature -22.0 °F
80*10*4; ISO 180/1U
Charpy Impact Unnotched 5.80 J/cm²

@Temperature 23.0 °C
27.6 ft-lb/in²

@Temperature 73.4 °F
Edgew 80*10*4 sp=62mm; ISO 179/1eU
6.00 J/cm²

@Temperature -30.0 °C
28.6 ft-lb/in²

@Temperature -22.0 °F
Edgew 80*10*4 sp=62mm; ISO 179/1eU
Charpy Impact, Notched 0.500 J/cm²

@Temperature -30.0 °C
2.38 ft-lb/in²

@Temperature -22.0 °F
V-notch Edgew 80*10*4 sp=62mm; ISO 179/1eA
0.700 J/cm²

@Temperature 23.0 °C
3.33 ft-lb/in²

@Temperature 73.4 °F
V-notch Edgew 80*10*4 sp=62mm; ISO 179/1eA
Impact Test 25.0 J

@Temperature 23.0 °C
18.4 ft-lb

@Temperature 73.4 °F
Instrumented Impact Total Energy; ASTM D 3763
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 29.0 µm/m-°C

@Temperature -40.0 - 150 °C
16.1 µin/in-°F

@Temperature -40.0 - 302 °F
ASTM E 831
29.0 µm/m-°C

@Temperature 23.0 - 150 °C
16.1 µin/in-°F

@Temperature 73.4 - 302 °F
ISO 11359-2
CTE, linear, Transverse to Flow 77.0 µm/m-°C

@Temperature -40.0 - 150 °C
42.8 µin/in-°F

@Temperature -40.0 - 302 °F
ASTM E 831
77.0 µm/m-°C

@Temperature 23.0 - 150 °C
42.8 µin/in-°F

@Temperature 73.4 - 302 °F
ISO 11359-2
Deflection Temperature at 0.46 MPa (66 psi) 162 °C
324 °F
Flatw 80*10*4 sp=64mm; ISO 75/Bf
169 °C

@Thickness 3.20 mm
336 °F

@Thickness 0.126 in
unannealed; ASTM D 648
174 °C

@Thickness 6.40 mm
345 °F

@Thickness 0.252 in
unannealed; ASTM D 648
Deflection Temperature at 1.8 MPa (264 psi) 158 °C
316 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
160 °C

@Thickness 3.20 mm
320 °F

@Thickness 0.126 in
unannealed; ASTM D 648
164 °C

@Thickness 6.40 mm
327 °F

@Thickness 0.252 in
unannealed; ASTM D 648
Vicat Softening Point 179 °C
354 °F
Rate B/50; ISO 306
182 °C
360 °F
Rate B/120; ISO 306
184 °C
363 °F
Rate B/50; ASTM D 1525
Flammability, UL94 V-0

@Thickness 3.00 mm
V-0

@Thickness 0.118 in
UL 94
5VA

@Thickness 3.00 mm
5VA

@Thickness 0.118 in
UL 94
Electrical Properties Metric English Comments
Volume Resistivity 4.50e+16 ohm-cm
4.50e+16 ohm-cm
IEC 60093
Surface Resistance 4.00e+13 ohm
4.00e+13 ohm
ROA; IEC 60093
Dielectric Strength 25.0 kV/mm

@Thickness 1.60 mm
635 kV/in

@Thickness 0.0630 in
in oil; IEC 60243-1
Dissipation Factor 0.0021

@Frequency 50.0 - 60.0 Hz
0.0021

@Frequency 50.0 - 60.0 Hz
IEC 60250
0.0034

@Frequency 1000 Hz
0.0034

@Frequency 1000 Hz
IEC 60250
0.0122

@Frequency 1.00e+6 Hz
0.0122

@Frequency 1.00e+6 Hz
IEC 60250
Comparative Tracking Index 125 V
125 V
IEC 60112
>= 125 V
>= 125 V
IEC 60112
Descriptive Properties Value Comments
Ball Pressure Test, 125°C +/- 2°C Passes
IEC 60695-10-2