Solvay TECHNYL® C 52G4 MZ25 PA6, 25% mineral filler, DRY

Category Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, 30% Mineral Filled
Manufacturer Solvay
Trade Name Technyl®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Solvay TECHNYL® C 52G4 MZ25 PA6, 25% mineral filler, DRY.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Description: TECHNYL® C 52G4 MZ25 is a 25% mineral reinforced melamine cyanurate flame retarded polyamide 6.This product is heat stabilized and is suitable for injection molding. This product is available in both dark and light electrical Grey, other colors can be made upon request.Benefits: The product offers a robust glow wire resistance, combined with enhanced processing behavior suitable for thin wall parts.Available in: Asia Pacific, Europe, Latin America and North AmericaRegulations compliance: Grades produced or imported in Europe comply with directive 453/2010/EC, which amends REACH directive 1907/2006/EC. This grade complies with RoHS directive 2002/95/EC. Unless specified, this grade is not suitable for food contact, medical devices or toy applications.Applications: This product is ideally suited for power distribution applications such as MCB housing.Information provided by Rhodia, Rhodia has been acquired by Solvay.
Physical Properties Metric English Comments
Density 1.37 g/cc
0.0495 lb/in³
ISO 1183/A
Water Absorption 1.0 %

@Temperature 23.0 °C,
Time 86400 sec
 1.0 %

@Temperature 73.4 °F,
Time 24.0 hour
 ISO 62
Linear Mold Shrinkage 0.010 cm/cm
0.010 in/in
Isotropy
Linear Mold Shrinkage, Flow 0.0080 cm/cm
0.0080 in/in
Linear Mold Shrinkage, Transverse 0.0080 cm/cm
0.0080 in/in
Melt Flow 20 g/10 min

@Load 2.16 kg,
Temperature 275 °C
 20 g/10 min

@Load 4.76 lb,
Temperature 527 °F
 ISO/FDIS 1133
Mechanical Properties Metric English Comments
Tensile Strength at Break 75.0 MPa
10900 psi
ISO 527 Type 1A
75.0 MPa
10900 psi
ASTM D638
Elongation at Break 3.0 %
3.0 %
ISO 527 Type 1A
3.0 %
3.0 %
ASTM D638
Tensile Modulus 6.40 GPa
928 ksi
ISO 527 Type 1A
Flexural Strength 130 MPa
18900 psi
ASTM D790
136 MPa
19700 psi
ISO 178
Flexural Modulus 0.600 GPa
87.0 ksi
ISO 178
5.70 GPa
827 ksi
ASTM D790
Izod Impact, Notched 0.550 J/cm
1.03 ft-lb/in
ASTM D256
Charpy Impact Unnotched 4.70 J/cm²
22.4 ft-lb/in²
ISO 179/1eU
Charpy Impact, Notched 0.300 J/cm²
1.43 ft-lb/in²
ISO 179/1eA
Thermal Properties Metric English Comments
Melting Point 222 °C
432 °F
ISO 11357
Deflection Temperature at 0.46 MPa (66 psi) 205 °C
401 °F
ISO 75/Bf
Deflection Temperature at 1.8 MPa (264 psi) 130 °C
266 °F
ISO 75/Af
145 °C
293 °F
ASTM D648
Flammability, UL94 V-2

@Thickness 0.800 mm
 V-2

@Thickness 0.0315 in
 1210
V-2

@Thickness 1.60 mm
 V-2

@Thickness 0.0630 in
 1210
V-2

@Thickness 3.20 mm
 V-2

@Thickness 0.126 in
 1210
Oxygen Index 31 %
31 %
ISO 4589
Glow Wire Test 960 °C

@Thickness 0.800 mm
 1760 °F

@Thickness 0.0315 in
 ISO 60695-2-12
960 °C

@Thickness 1.60 mm
 1760 °F

@Thickness 0.0630 in
 ISO 60695-2-12
Electrical Properties Metric English Comments
Comparative Tracking Index 252 V
252 V
Solution A; IEC 60112
Processing Properties Metric English Comments
Feed Temperature 230 - 235 °C
446 - 455 °F
Mold Temperature 70.0 - 100 °C
158 - 212 °F
Drying Temperature 80.0 °C
176 °F
Moisture Content <= 0.20 %
<= 0.20 %
Descriptive Properties Value Comments
Compression Zone 230-240°C
Mixing Zone 245-250°C