- Acrylonitrile/Styrene/Acrylate (ASA), Unreinforced, Molded
- Techmer ES HiFill® ASA 778 UV WT168
Techmer ES HiFill® ASA 778 UV WT168
| Category | Polymer , Thermoplastic , ASA Polymer , Acrylonitrile/Styrene/Acrylate (ASA), Unreinforced, Molded |
| Manufacturer | Techmer ES |
| Trade Name | HiFill® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Techmer ES HiFill® ASA 778 UV WT168.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Availability: North AmericaForms: PelletsAdditive: UV StabilizerFeatures: Good UV ResistanceAppearance: WhiteInformation provided by TP Composites, Inc.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.07 g/cc | 0.0387 lb/in³ | ASTM D792 |
| Water Absorption | 0.35 % @Time 86400 sec |
0.35 % @Time 24.0 hour |
ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.0070 cm/cm @Thickness 3.17 mm |
0.0070 in/in @Thickness 0.125 in |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 108 | 108 | ASTM D785 |
| Tensile Strength, Yield | 49.0 MPa | 7100 psi | ASTM D638 |
| Elongation at Break | 8.0 % | 8.0 % | ASTM D638 |
| Flexural Strength | 40.7 MPa | 5900 psi | ASTM D790 |
| Flexural Modulus | 2.14 GPa | 310 ksi | ASTM D790 |
| Izod Impact, Notched | 2.40 J/cm @Thickness 3.17 mm |
4.50 ft-lb/in @Thickness 0.125 in |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 70.2 µm/m-°C | 39.0 µin/in-°F | ASTM D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 106 °C | 223 °F | Unannealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 103 °C | 217 °F | Unannealed; ASTM D648 |
| Flammability, UL94 | HB | HB |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 5.00e+13 ohm-cm | 5.00e+13 ohm-cm | ASTM D257 |
| Dielectric Strength | 15.7 kV/mm | 400 kV/in | Method A (Short-Time); ASTM D149 |
Users viewing this material also viewed the following:
- Piezo Kinetics 406 Lead Zirconate Titanate Piezoelectric
- LATI Latigray 66-01 CX/50 PA 66
- Solvay Specialty Polymers Ryton® PR11 Polyphenylene Sulfide (PPS)
- Teknor Apex Telcar® TL-1686D1 Thermoplastic Elastomer
- PlastxWorld CEVIAN® CGF10 10% GF PC/Acrylic Alloy
- A. Schulman POLYBATCH™ Grey 8218 Concentrate Based In Polyethylene
- Trelleborg E569 EPDM Rubber
- Breplast Bretene LD FILM Low Density Polyethylene
- Asahi Kasei Leona® 1502 Nylon 66
Copyright © lookpolymers.com All Rights Reserved