Diamond Polymers ABS/PC 9801
| Category | Polymer , Thermoplastic , ABS Polymer , Polycarbonate/ABS Alloy, Unreinforced , Polycarbonate (PC) |
| Manufacturer | Diamond and Network Polymers |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Diamond Polymers ABS/PC 9801.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description: Injection Molding Grade, High Impact, High HeatInformation provided by Diamond Polymers, Inc.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.12 g/cc | 1.12 g/cc | ASTM D792 |
| Linear Mold Shrinkage | 0.0050 - 0.0080 cm/cm | 0.0050 - 0.0080 in/in | ASTM D955 |
| Melt Flow | 0.40 g/10 min @Load 5.00 kg, Temperature 200 °C |
0.40 g/10 min @Load 11.0 lb, Temperature 392 °F |
Procedure A Condition G; ASTM D1238 |
| 3.3 g/10 min @Load 3.80 kg, Temperature 230 °C |
3.3 g/10 min @Load 8.38 lb, Temperature 446 °F |
Procedure A Condition I; ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 112 | 112 | ASTM D785 |
| Tensile Strength, Yield | 49.0 MPa | 7100 psi | chs 2 in/min; ASTM D638 |
| Flexural Modulus | 1.78 GPa | 258 ksi | Tangent, chs 0.05 in/min; ASTM D790 |
| Izod Impact, Notched | 5.66 J/cm @Thickness 3.17 mm, Temperature 23.0 °C |
10.6 ft-lb/in @Thickness 0.125 in, Temperature 73.4 °F |
bar; ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 106 °C | 223 °F | 0.125 in bar Annealed 4 hours at 80°C; ASTM D648 |
| 107 °C | 225 °F | 0.125 in bar Unannealed/Conditioned 48 hours at 23°C; ASTM D648 | |
| Vicat Softening Point | 140 °C | 284 °F | 0.125 inch, 1 Kg; ASTM D1525 |
| Flammability, UL94 | HB @Thickness 1.50 mm |
HB @Thickness 0.0591 in |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 229 - 260 °C | 445 - 500 °F | |
| Middle Barrel Temperature | 235 - 266 °C | 455 - 510 °F | |
| Front Barrel Temperature | 238 - 271 °C | 460 - 520 °F | |
| Nozzle Temperature | 238 - 271 °C | 460 - 520 °F | |
| Melt Temperature | 238 - 271 °C | 460 - 520 °F | Melt temperatures above 530°F are not recommended, and may result in color shifts and or thermal instability. |
| Mold Temperature | 37.8 - 82.2 °C | 100 - 180 °F | Higher mold temperature can aid flow in processing, provides a better surface finish, and creates less residual stress in the finished products. |
| Drying Temperature | 90.6 - 98.9 °C | 195 - 210 °F | |
| Dry Time | 2 - 4 hour | 2 - 4 hour | |
| Moisture Content | <= 0.020 % | <= 0.020 % | |
| Back Pressure | 0.345 - 1.03 MPa | 50.0 - 150 psi |
Users viewing this material also viewed the following:
- Polymax® Maxelast® P1780 TPE, PP Overmold or Standalone use
- Premix Thermoplastics PRE-ELEC® ESD 6600 Static Dissipative Thermoplastic Compound
- Niche Polymer PCABSN10BK PC/ABS
- PTS SAN-82TR SAN Resin
- Kennametal Stellite Stellite® 33
- Minelco Quickbond
- Teknor Apex Monprene® MP-1736R1 Thermoplastic Elastomer
- A. Schulman POLYFORT™ FPP 3443U UV Resistant Homopolymer Polypropylene
- 3M 8454 Cable Accessory Sealing Kits
- TSE Industries Millathane® 5004 Millable Polyurethane Elastomer, Hardness 84A
Copyright © lookpolymers.com All Rights Reserved