Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength, Yield | 28.0 MPa | 4060 psi | ISO 527 |
Polimeri Europa Eraclene® MM 84 High Density Polyethylene - Injection Molding Eraclene MM 84 is a high density polyethylene resin (HDPE) with antioxidants, suitable for injection molding application.Eraclene MM 84 is characterized by high rigidity and good impact resistance. .. |
|||
Tensile Strength, Yield | 28.0 MPa | 4060 psi | ISO 527 |
Premix Thermoplastics PRE-ELEC® ESD 5300 Static Dissipative Thermoplastic Compound PRE-ELEC® ESD 5300 is a static dissipative thermoplastic compound based on polypropylene homopolymer. The dissipative property is permanent and built into the polymer chain. Surface resistance valu.. |
|||
Tensile Strength, Yield | 28.0 MPa | 4060 psi | ISO 527 |
SABIC Innovative Plastics LNP COLORCOMP M1000S PP LNP COLORCOMP* M1000S is an unfilled Polypropylene resin. Added features of this material include: Heat Stabilized. |
|||
Tensile Strength, Yield | 28.0 MPa | 4060 psi | ASTM D638 |
SABIC B5429/B5429A High Density Polyethylene for Blow Molding Product Description: B5429 Series grades are medium molecular weight High Density Polyethylene copolymer. They are primarily intended for blow molding articles of small sizes. B5429 series grades.. |
|||
Tensile Strength, Yield | 28.0 MPa | 4060 psi | 2in (50mm) per min.; ASTM D638 Type 4 |
Polymer Industries Densetec HDPE Arena Board Densetec Arena Board is ideal for hockey rink applications including dasher boards, kick plates and official lines. Densetec Arena Board exhibits the properties of high impact strength, abrasion-res.. |
|||
Tensile Strength, Yield | 28.0 - 88.3 MPa | 4060 - 12800 psi | Average value: 59.4 MPa Grade Count:38 |
Overview of materials for Acrylonitrile Butadiene Styrene (ABS), 10% Glass Fiber Filled This property data is a summary of similar materials in the MatWeb database for the category "Acrylonitrile Butadiene Styrene (ABS), 10% Glass Fiber Filled". Specific grades with glass content betwe.. |
|||
Tensile Strength, Yield | 28.0 MPa | 4060 psi | |
LyondellBasell Lupolen® 5261 Z HI HDPE Data was collected by ISO methods and originally provided by BASF. The Lupolen® product line is now produced by Basell. |
|||
Tensile Strength, Yield | 28.0 MPa | 4060 psi | ASTM D638 |
LyondellBasell Pro-fax SA861 Polypropylene Random Copolymer, Cast Film Extrusion Key Features: polypropylene random copolymer resin formulated for cast film extrusion, good optical properties, excellent slip properties, FDA acceptable, improved cold temperature impact resistance.. |
|||
Tensile Strength, Yield | >= 28.0 MPa | >= 4060 psi | |
Kazanorgsintez PE2NT22-12 High Density Polyethylene Composite Production Method: Copolymerization of eythylene at low pressure in presence of complex catalysts using gaseous-phase method. Application: Composition is intended for injection molding processin.. |
|||
Tensile Strength, Yield | 28.0 MPa | 4060 psi | ASTM D638 |
Flint Hills AP5135-HS Impact Copolymer Polypropylene Medium impact copolymer, FDA compliantFeatures: Nucleated and heat stabilized.Applications: Injection molding: large, thin wall automotive interior parts and housewares.Former Huntsman polypropylene.. |
|||
Tensile Strength, Yield | 28.0 MPa | 4060 psi | ASTM D638 |
Flint Hills PP 13R9A Random Copolymer Polypropylene Random copolymer, Drug Master File (DMF) listed, USP Class VI certified, and FDA compliantFeatures: Radiation resistant and good contact clarity.Applications: Injection molding: radiation sterilizab.. |
|||
Tensile Strength, Yield | 28.0 MPa | 4060 psi | 50 mm/min; ISO 527-1,-2 |
Inno-Comp INNOPOL® CS 2-3130 NU UV-Stabilized 30% Talc-Filled Polypropylene Block-Copolymer INNOPOL® CS 2-3130 NU is an UV-stabilized 30% talc-filled polypropylene block-copolymer compound /PP-B TD30 (ISO 1043)/.INNOPOL® CS 2-3130 NU is recommended for producing injection molded prod.. |
|||
Tensile Strength, Yield | 28.0 MPa | 4060 psi | Type I, 5 mm/min; ASTM D638 |
SABIC Innovative Plastics LNP THERMOCOMP AFB42 ABS LNP* THERMOCOMP* AFB42 is a compound based on ABS containing 10% Glass Fiber, 20% Glass Bead. |
|||
Tensile Strength, Yield | 28.0 MPa | 4060 psi | 50mm/min; ISO 527 |
Styrolution Styrolux 684D SBC Styrolux 684D is a thermoplastic styrene-butadiene block copolymer which is suitable for injection molding, extrusion, and thermoforming. It offers an outstanding combination of crystal clarity and.. |
|||
Tensile Strength, Yield | 28.0 MPa | 4060 psi | ISO 527 |
SABIC Innovative Plastics LNP THERMOCOMP TH0300A PUR (Asia Pacific) LNP THERMOCOMP* TH0300A is a compound based on Polyurethane resin. Added features of this material include: High Specific Gravity. |
|||
Tensile Strength, Yield | 28.0 MPa | 4060 psi | ASTM D638 |
A. Schulman POLYFORT™ FPP 1908E Talc Filled Copolymer Polypropylene DescriptionPolyfort® FPP 1908E is a 20% talc filled impact copolymer polypropylene product. Information provided by A. Schulman. |
|||
Tensile Strength, Yield | 28.0 MPa | 4060 psi | ASTM D638 |
A. Schulman POLYFLAM™ E-17338 22% CACO3 Filled Copolymer Polypropylene DescriptionPolyfort® E 17338 is a 22% filled copolymer polypropylene product. Information provided by A. Schulman. |
|||
Tensile Strength, Yield | 28.0 MPa | 4060 psi | ISO 527-2 |
Tisan TISOPLEN® 30% Calcite Filled Heat Stabilized Homopolymer Polypropylene TISOPLEN has a wide area of application in furniture, durable goods, household appliances, electrics/electronics, and telecommunication industries. General specifications include Low densityLow mois.. |
|||
Tensile Strength, Yield | 28.0 MPa | 4060 psi | ASTM D 638 |
Cossa Polimeri ESTADIENE 0425 GFS Acrylonitrile Butadiene Styrene, 13% Glass Filled ABS with 13% short glass fiberExcellent mechanical and thermal propertiesInformation provided by Cossa Polimeri S.r.l. |
|||
Tensile Strength, Yield | 28.0 MPa | 4060 psi | 5 mm/min; ISO 527 |
Eurostar Starglas FF001 HDPE, Glass Fiber Filled Starglas FF001 is a Glass Fiber Reinforced High Density Polyethylene ResinInformation provided by Eurostar. |
|||
Tensile Strength, Yield | 28.0 MPa | 4060 psi | ASTM D638 |
Entec Hypro™ PPH-CC20 Natural Homopolymer Polypropylene, 20% Calcium Carbonate Filled Information provided by Entec |
|||
Tensile Strength, Yield | 28.0 MPa | 4060 psi | ASTM-D638 |
Braskem AC59 HDPE Monofilament Polyethylene Homopolymer AC59 resin is a high-density polyethylene homopolymer produced by the solution process and designed for monofilament applications. It contains antioxidant additives. Its applications include: film .. |
|||
Tensile Strength, Yield | 28.0 MPa | 4060 psi | 50 mm/min |
Arkema Group Rilsan® BESN P40 W5 TL Nylon 11, Flexible Tubing Grade (Dry) Designation ISO 1874-PA11-P,EFHL,22-003Flexible grade for tubes extrusion. Available color: milky white. Light and heat stabilized. Flame retardant agent.Fire-resistant. Flexibility. High impact str.. |
|||
Tensile Strength, Yield | 28.0 MPa | 4060 psi | |
BASF Novolen® 2340 P Polypropylene Grade with nucleating agent for injection molded parts.Data was collected by ISO methods and provided by BASF. |
|||
Tensile Strength, Yield | 28.0 MPa | 4060 psi | ASTM D638 |
Aclo Accutech Polypropylene Copolymer CP0436G10CL Glass Reinforced |
|||
Tensile Strength, Yield | 28.0 MPa | 4060 psi | |
BASF Procom® D 1187 Polypropylene Data was collected by ISO methods and provided by BASF. |
|||
Tensile Strength, Yield | 28.0 MPa | 4060 psi | ASTM D638 |
Chevron Phillips Marlex® HMN 5580 Polyethylene, Injection Molding Grade, HDPE
(discontinued **) Meets FDA Regulation 177.1520. High stiffness, excellent surface appearance, good impact strength and warpage resistance.Data provided by the manufacturer |
|||
Tensile Strength, Yield | 28.0 - 80.0 MPa | 4060 - 11600 psi | Average value: 60.1 MPa Grade Count:26 |
Overview of materials for Nylon 6, Film Grade This property data is a summary of similar materials in the MatWeb database for the category "Nylon 6, Film Grade". Each property range of values reported is minimum and maximum values of appropriat.. |
|||
Tensile Strength, Yield | 28.0 MPa | 4060 psi | ASTM D638 |
BP Amoco Acctuf® 3432 Impact Copolymer Polypropylene
(discontinued **) Suggested fabrication methods: Injection moldingFeatures: Nucleated, AntistaticComplies with FDA specification, Title 21, CFR 177.1520.Typical property data below from injection molded samples. |
|||
Tensile Strength, Yield | 28.0 MPa | 4060 psi | 2 in per min; ASTM D638 Type IV |
Chevron Phillips Marlex® HHM 5502-01 ST High Density Ethylene Hexene Copolymer High Density Ethylene Hexene CopolymerSag Upper Limit: 18 cm, Lower Limit: 13 cm; 2 ft. X 4ft. X 125 mil thick blank heated to forming temperature.Data provided by Chevron Phillips Chemical Company.. |